Microstructural evolution and flow behavior of twin-roll cast AZ41 magnesium alloy during hot compression were characterized by employing deformation temperature of 300°C, 350°C and 400°C, and strain rate ranging from 10-3 to 10-2 s-1. When compressed at different temperature (300°C, 350°C and 400°C) and strain rate (10-3 and 10-2 s-1) all stress strain curves showed a flow softening behavior before strained to 0.51 due to dynamic recrystallization, even though concurrent twinning was quite active. Twinning contributed to the flow hardening behavior appeared during the end of hot compression (ε > 0.51) at a strain rate of 10-2s-1 and elevated temperature (300°C, 350°C and 400°C) in spite of the softening effect of concurrently occurred dynamic recrystallization. TEM image showed that discontinuous recrystallization occurred when deformed at elevated temperature as high as 400°C and the strain rate ranging from 10-2 to 10-3 s-1. It is suggested that dislocation slip, twinning and recrystallization develop in a cyclic mode from initial stage to the end of hot compression. [ABSTRACT FROM AUTHOR]

Flow stress behavior during initial stage of hot compression of twin-roll cast ZK60 magnesium alloy was characterized by employing deformation temperature of 300°C and 400°C, and a given strain rate of 10-2 s-1. A stress drop during initial stage of hot compression at 300°C, generally led by dynamic recrystallization, was found to be attributed to twinning, correspondingly to dynamic recrystallization as deformation temperature was raised to 400°C. [ABSTRACT FROM AUTHOR]

The microstructural evolution in an Al-Cu-Mg-Ag alloy with trace Zr addition during homogenization treatment was characterized by Differential Scanning Calorimetry (DSC), Scanning Electron Microscopy (SEM) and Energy-dispersive X-ray Spectroscopy (EDS). It was shown that the low-melting-point phase segregating toward grain boundaries is Al2Cu, with a melting point of 523.52°C. A two-step homogenization process was employed to optimize the microstructure of the as-cast alloy, during which the alloy was first homogenized at a lower temperature, then at a higher temperature. After homogenized at 420°C for 6 h, Al3Zr particles were finely formed in the matrix. After that, when the alloy was homogenized at an elevated temperature for a longer time, i.e., 515°C for 24 h, most of the precipates at the grain boundaries were removed. Furthermore, the dispersive Al3Zr precipitates were retained, without coarsening greatly in the final homogenization step. A kinetics model is employed to predict the optimal homogenization time at a given temperature theoretically, and it confirms the result in present study, which is 420°C/6h+515°C/24h. [ABSTRACT FROM AUTHOR]