Search

Pd/C catalysts are widely used for hydrogenation reactions in the chemical industry. One of the reasons for their high activity is the ability of Pd nanoparticles (PdNP) to dissociate H2 and promote H‐spillover. Nevertheless, for selective hydrogenation unpromoted Pd/C catalysts show disappointing results. The use of supported Pd single atom (PdSA) catalysts permits to achieve high selectivity. However, PdSA show low activity because they have difficulty in activating H2. A cooperative catalysis between PdNP and PdSA operates for the hydrogenation of alkenes thanks to the H‐spillover, which makes it possible to obtain active isolated PdSA−H species. Here, we present experimental and computational results obtained for phenylacetylene hydrogenation on Pd/CNT catalysts showing different PdSA/PdNP ratios. Tuning this ratio allows doubling the activity while reaching high selectivity to styrene at high conversion. DFT calculations suggest that the first coordination sphere of PdSA has a pronounced effect on their reactivity. [ABSTRACT FROM AUTHOR]

Copper-based nanoparticles, supported on either a silica aerogel or cubic mesostructured silicas obtained by using two different synthetic protocols, were used as catalysts for the water gas shift reaction. The obtained nanocomposites were thoroughly characterised before and after catalysis through nitrogen adsorption-desorption measurements at −196 °C, TEM, and wide- and low-angle XRD. The samples before catalysis contained nanoparticles of copper oxides (either CuO or Cu2O), whereas the formation of metallic copper nanoparticles, constituting the active catalytic phase, was observed either by using pre-treatment in a reducing atmosphere or directly during the catalytic reaction owing to the presence of carbon monoxide. A key role in determining the catalytic performances of the samples is played by the ability of different matrices to promote a high dispersion of copper metal nanoparticles. The best catalytic performances are obtained with the aerogel sample, which also exhibits constant carbon monoxide conversion values at constant temperature and reproducible behaviour after subsequent catalytic runs. On the other hand, in the catalysts based on cubic mesostructured silica, the detrimental effects related to sintering of copper nanoparticles are avoided only on the silica support, which is able to produce a reasonable dispersion of the copper nanophase. [ABSTRACT FROM AUTHOR]

A mesoporous ordered cubic Im3m silica (SBA-16) characterized by a three dimensional cage-like structure of pores was used as a host matrix for the preparation of a series of FeCo-SiO2 nanocomposites with different alloy loading and composition by the wet impregnation method. The mesoporous structure of the SBA-16-type support, prepared according to a versatile sol-gel templated synthetic method, which makes use of n-butanol as a co-surfactant, is stable during the treatments necessary to obtain the final nanocomposites, as pointed out by low-angle X-Ray diffraction, transmission electron microscopy, and N2 physisorption at 77 K. Wide-angle X-ray diffraction shows that upon reduction at 800 °C, FeCo nanocrystals (6-7 nm) with the typical bcc structure are formed and energy-dispersive X-ray spectroscopy analysis, performed by scanning transmission electron microscopy on one of the samples, shows that the Fe/Co atomic ratio in the alloy nanoparticles is very close to the expected value of two. Electron tomography was used for the first time to gain evidence on the highly interconnected mesoporous structure of SBA-16 and the arrangement of the nanoparticles within the matrix. It was found that spherical alloy nanocrystals with narrow size distribution are homogeneously distributed throughout the mesoporous matrix and that the resulting FeCo-SiO2 nanocomposite material displays superparamagnetic behavior with high strength dipolar interactions, as expected for particles with a large magnetic moment. [ABSTRACT FROM AUTHOR]