The application of heteroatom doped cobalt (Ni@Co/C) prepared from a porous metal–organic framework as the cathode material for the rechargeable zinc–air batteries has been demonstrated. The Ni@Co/C‐modified electrode showed an excellent catalytic activity toward oxidation–reduction reaction and oxygen evolution reactions. The Co/C catalysts, which were Co particle impregnated on graphitic carbon powders, were synthesized after the calcination of Co3 (SDA)3(DMF)2 precursor, and then Ni deposition (Ni@Co/C) was followed on it by chemical reduction. Linear sweep voltammetry measurement indicates that Ni@Co/C‐H800, which had Ni particles on Co/C derived from MOF at 800 °C under N2, exhibited excellent performance. The stable charging/discharging profiles at 20 mA cm−2 of current were obtained for the 350 h in alkaline medium, suggesting Ni@Co/C‐H800 as a potential candidate for oxidation–reduction and evolution reactions. [ABSTRACT FROM AUTHOR]

Zeolitic imidazolate frameworks (ZIFs) are a subclass of metal–organic frameworks (MOFs). These robust, porous materials have garnered significant interest because of their outstanding properties as catalysts for the oxygen evolution reaction (OER) and oxygen reduction reaction (ORR). Herein, the synthesis of Co‐ and Ni‐containing ZIF‐67 embedded in carbon nanotubes (CNTs) to be used as a cathode material for rechargeable zinc–air batteries is described. Carbon‐nanotube‐encapsulated metallic Co and Ni form via calcination of the MOF at 700 °C for 4 h and are characterized by X‐ray diffraction and transmission electron microscopy (TEM). Co and Ni graphitization within the CNTs is analyzed by Raman spectroscopy, and morphologies are assessed by scanning electron microscopy (SEM) and TEM. Excellent electrochemical performance of the prepared catalysts during charging and discharging reveals that the catalyst is stable for well over 500 h. Moreover, superior OER performance is observed when CNT@Co or CNT@Ni is used as a bifunctional catalyst in the zinc–air battery. [ABSTRACT FROM AUTHOR]

A metal–organic framework (MOF) was synthesized using 4,4′‐stilbenedicarboxylic acid (H2SDA) in dimethylformamide (DMF). Carbon‐coated Co (C@Co) catalysts were prepared by the direct calcination of Co3(SDA)3(DMF)2 MOF crystals at various temperatures. The highest surface area of the C@Co catalyst is obtained at 600 °C which can further be increased by the ball mill operation. The X‐ray photon spectroscopy and X‐ray diffraction analysis proved the formation of metallic Co in the carbon matrix at temperatures over 500 °C, while Co3O4 formation was observed at 500 °C. Furthermore, the graphitic properties of the Co particles were analyzed by Raman spectroscopy. The durability of the carbon‐coated Co catalysts derived from MOFs (C@Co catalysts) was analyzed by the cycle test (charge/discharge at 20 mA/cm2 per 2 h) and was retained over 350 h. These catalysts showed remarkable stability for both ORR (oxygen reduction reaction) and OER (oxygen evolution reaction), comparable to that of Co3O4 and Co metal powder in alkaline solution. [ABSTRACT FROM AUTHOR]