Material systems capable of handling both the ballistic impact and blast waves are necessary for security forces. In this study, the high strain rate performance of monolithic and bonded ultra‐high molecular weight polyethylene (UHMWPE) with high‐temperature resistant basalt/polyetherimide (B/PEI) composite is presented. Individual composite laminates were fabricated using vacuum‐assisted compression molding. Subsequently, cylindrical test coupons were cut using a high‐pressure waterjet. A suitable adhesive grade was used for the bonding of two different composite types. The dynamic compression studies were conducted on a split‐Hopkinson pressure bar (SHPB). For identical incident energies, the range of strain rates attained by monolithic UHMWPE, B/PEI and bonded composites differed significantly. Monolithic UHMWPE achieved the highest rates of loading, whereas higher stresses were recorded for the B/PEI composite. Yet, monolithic UHMWPE, owing to higher constant stress plastic flow, results in higher toughness. Bonded composites revealed hybrid properties with delamination of UHMWPE as the primary failure mode. High‐speed imaging exposed severe deformation of UHMWPE during dynamic compression. SEM micrographs revealed fiber pull‐out and deforming behavior of UHMWPE and brittle failure of B/PEI composite. B/PEI in a bonded composite system never failed under dynamic compression within the experimental range, thus providing a window of opportunity to tailor‐make better ballistic and blast protection materials. [ABSTRACT FROM AUTHOR]

An investigation of the effect of strain rate on the dynamic compressive behavior of glass/polytetrafluoroethylene (PTFE) composite is presented. Experimental studies were carried out on two dimensional (2D), satin weave (SW) and three dimensional (3D) woven glass/PTFE composites using split Hopkinson pressure bar (SHPB) apparatus. Commercial grades of glass/PTFE fabrics were autoclaved to prepare the composite laminates and circular specimens were cut out using a high‐pressure water jet. High strain rate studies confirmed the rate‐dependent behavior of all the woven composite systems under consideration. The highest rates of loading were attained by 3D woven specimens for identical incident energies. The highest peak stress attained by 3D woven specimens was 501 MPa, which was trailed by 2D woven specimens with 482 MPa stress. The advantage of satin weave was not reflected in the small specimens as the peak stress attained for identical loading was limited to 405 MPa. Similarly, the highest strain and toughness were recorded for 3D woven composites. However, the SW pattern unlocked a new possibility of controlling the primary damage axis. Furthermore, an analytical method is presented based on variable rate power law to predict the dynamic compressive stress of glass/PTFE. [ABSTRACT FROM AUTHOR]