Engineering mechanically robust ZrO2 foams with three‐dimensional (3D) reticular architecture and high porosity is extremely challenging. In current work, we presented an approach for constructing such cellular ceramics via a combined polyurethane foaming and chemical grafting method. Ester functional groups were chemically grafted on the ZrO2 powder surface to enhance its dispersibility. This approach caused the micron‐sized windows to assemble onto the cell wall of porous framework, contributing to 3D interconnected reticular architecture. The resulting products with such cellular architecture possessed a high porosity level of 89.2% and maintained an ultrahigh compressive strength of 8.5 MPa. Our results open up new opportunities for fabricating high‐performance ZrO2 foams toward practical applications. [ABSTRACT FROM AUTHOR]

Hierarchical cellular architectures hold great potential in a vast range of applications due to their superior mechanical properties and multifunctionality. In the present work, hierarchical structures composed of porous struts patterned in the form of quadrangular and triangular honeycombs were fabricated via direct foam writing (DFW) using colloidal particle‐stabilized Al2O3‐MgO‐SiO2 foams as the ink. Hydration process of MgO and subsequent formation of colloidal Mg(OH)2 network endowed the foam ink with viscoelasticity and high storage modulus. The resulting honeycombs with ultrahigh overall porosity (95.3%) and robust compressive strength (2.5 MPa) can be readily fabricated by DFW. The current work exhibits a significant step toward the scalable production of cellular ceramics with hierarchical architecture for various applications, including tissue scaffolds, catalyst supports, thermal insulation, and lightweight structures. [ABSTRACT FROM AUTHOR]

Ceramic foams with significant porosity and robust mechanical properties have received extensive attentions. However, it is still difficult to achieve excellent compressive strength at high porosity levels. In this work, a gelation of foamed boehmite sol method is proposed to settle this issue. The technological parameters during preparation process are systematically investigated. As‐prepared alumina ceramic foams possess unprecedentedly high compressive strength of 34.1‐89.1 MPa at high porosity levels of 66.0%‐87.2%, which is attributed to the present of hierarchical pore structure, small grain size and pore size. This work demonstrates a facile and novel method for the fabrication of high‐performance alumina ceramic foams toward practical applications. [ABSTRACT FROM AUTHOR]