A universal sequential synthesis strategy in aqueous solution is presented for highly uniform core-shell structured photocatalysts, which consist of a metal sulfide light absorber core and a metal sulfide co-catalyst shell. We show that the sequential chemistry can drive the formation of unique core-shell structures controlled by the constant of solubility product of metal sulfides. A variety of metal sulfide core-shell structures have been demonstrated, including CdS@CoSx , CdS@MnSx , CdS@NiSx , CdS@ZnSx , CuS@CdS, and more complexed CdS@ZnSx @CoSx . The obtained strawberry-like CdS@CoSx core-shell structures exhibit a high photocatalytic H2 production activity of 3.92 mmol h-1 and an impressive apparent quantum efficiency of 67.3 % at 420 nm, which is much better than that of pure CdS nanoballs (0.28 mmol h-1 ), CdS/CoSx composites (0.57 mmol h-1 ), and 5 %wt Pt-loaded CdS photocatalysts (1.84 mmol h-1 ).

An aqueous emulsion polymerization self‐assembly approach is demonstrated for the first time to synthesize ultrahigh nitrogen containing mesoporous polymer nanospheres, using melamine‐formaldehyde resin oligomers as precursors. In the synthesis, change from alkaline to acidic conditions is critical for the formation of monodisperse mesostructured polymer nanospheres. Owing to unique structure of triazine stabilized in the covalent polymeric networks during the pyrolysis process, the derived mesoporous carbon nanospheres possess an ultrahigh nitrogen content (up to 15.6 wt%) even after pyrolysis at 800 °C, which is the highest nitrogen content among mesoporous carbon nanospheres. Furthermore, these monodisperse mesoporous carbon nanospheres possess a high surface area (≈883 m2 g−1) and large pore size (≈8.1 nm). As an anode for sodium‐ion batteries, the ultrahigh nitrogen‐containing mesoporous carbon nanospheres exhibit superior rate capability (117 mAh g−1 at a high current density of 3 A g−1) and high reversible capacity (373 mAh g−1 at 0.06 A g−1), indicating a promising material for energy storage.