Staphylococcus aureus is the most common contagious mastitis pathogen of dairy cattle. Antimicrobial treatment of infected cattle results in variable cure rates. Epidermal growth factor (EGF) plays an important role in the modulation of host innate immune responses and the regulation of mammary epithelial regeneration, indicating that EGF may be useful as a treatment for mastitis. A pilot study was conducted to evaluate the efficacy of recombinant bovine EGF (rbEGF) for the treatment of S aureus intramammary infection (IMI) using an ovine model. Each ewe was experimentally infected with S aureus in both udder halves. One udder half of each ewe received one of two treatments: EGF (n=13) or pirlimycin (n=13). The contralateral udder half of each ewe received sterile saline as a control. The bacteriological cure rate following rbEGF was significantly lower (15 per cent) than that attained with pirlimycin hydrochloride (61 per cent) and did not differ from that following treatment with sterile saline. Cure rates following treatment with rbEGF were not significantly different to those following sterile saline. Given that EGF is associated with modulation of host immunity and wound healing, future studies into EGF should not focus on whether EGF increases cure rates of S aureus IMI., Competing Interests: Competing interests: None declared.

The solution treatment of an as-cast ASTM F-75 alloy was investigated. Microstructural evolution was followed during thermal processing, in particular with regard to the content and type of carbides formed. To evidence any probable carbide transformations occurring during the heating stage, as well as to clarify their effect on the carbide dissolution kinetics, three heating rates were studied. Image analysis and scanning electron microscopy techniques were used for microstructural characterization. For the identification of precipitates, these were electrolytically extracted from the matrix and then analyzed by X-ray diffraction. It was found that the precipitates in the as-cast alloy were constituted by both a M(23)C(6) carbide and a sigma intermetallic phase. The M(23)C(6) carbide was the only phase identified in solution-treated specimens, regardless of the heating rate employed, which indicated that this carbide dissolved directly into the matrix without being transformed first into an M(6)C carbide, as reported in the literature. It was found that the kinetics of dissolution for the M(23)C(6) carbide decreased progressively during the solution treatment, and that it was sensitive to the heating rate, decreasing whenever the latter was decreased. Because the M(23)C(6) carbide was not observed to suffer a phase transformation prior to its dissolution into the matrix, the effect of the heating rate was associated to the morphological change occurred as the specimens were heated. The occurrence of the observed phases was analyzed with the aid of phase diagrams computed for the system Co-Cr-Mo-C., (Copyright 2001 John Wiley & Sons, Inc. J Biomed Mater Res 59: 378-385, 2002)