Search

In order to study adhesion/decalcification mechanisms of acid interactions with human hard tissues such as bones and teeth, the chemical interaction of five carboxylic acids (acetic, citric, lactic, maleic, and oxalic) and two inorganic acids (hydrochloric and nitric) with enamel and two synthetic hydroxyapatite (HAp) powders with, respectively, a high and a low crystallinity were analyzed using X-ray photoelectron spectroscopy (XPS), atomic absorption spectrophotometry (AAS), and spectrophotometry (S). X-ray diffraction revealed that the crystallinity of the highly crystallized HAp was considerably higher than that of enamel while the crystallinity of the poorly crystallized HAp was similar to that of dentin and bone. XPS of acid-treated enamel demonstrated for all carboxylic acids ionic bonding to calcium of HAp. AAS and S showed for both HAps that all carboxylic and inorganic acids except oxalic acid extracted Ca significantly more than P, leading to a Ca/P ratio close to that of synthetic HAp (2.16 w/w). Oxalic acid extracted hardly any Ca, but substantially more P, leading to a significantly smaller Ca/P ratio than that of HAp. AAS showed that the calcium salt of oxalic acid hardly could be dissolved, whereas the calcium salts of all the other acids were very soluble in their respective acid solution. These results confirm the adhesion/decalcification concept (AD-concept) previously advanced. Depending on the dissolution rate of the respective calcium salts, acids either adhere to or decalcify apatitic substrates. It is concluded that the AD-concept that originally dictated the interaction of carboxylic acids with human hard tissues can be extended to inorganic acids, such as hydrochloric and nitric acid. Furthermore, HAp crystallinity was found not to affect the adhesion/decalcification behavior of acids when interacting with apatitic substrates, so that the AD-concept can be applied to all human hard tissues with varying HAp crystallinity., (Copyright 2001 John Wiley & Sons, Inc.)

Recently, polymerization-initiator-induced radicals have been identified as a biohazard as well as residual monomers. The present investigation was conducted to clarify the leaching behavior of the polymerization initiator and to measure the relationship between the leached amount of polymerization initiator and the degree of conversion of visible light (VL)-cured resin. Moreover, determining a suitable ratio of polymerization initiator to the base monomer according to the above relationship was carried out. The base monomer (UDMA/TEGDMA) was activated with varying concentrations of polymerization initiator (CQ/DMPT, CQ/DMAEMA) from 0.3-0.9 wt%, respectively, which were exposed to light for 40 s. Gas chromatograph mass spectrometry (GCMS) was carried out to evaluate the leached amount of polymerization initiator. The degree of conversion (DC) of the cured sample was estimated using attenuated total reflectance-Fourier transform infrared (ATR-FTIR) spectroscopy. As the result, it was recognized that the leachability of the polymerization initiator (CQ, DMPT, and DMAEMA) depended on the degree of conversion of the VL-cured resin. Therefore, the optimal concentration of polymerization initiator can be determined from the relation between the degree of conversion and the leached amount of polymerization initiator, which is about 0.6 wt% for CQ/DMPT (1:1 in weight) and 0.5 wt% for CQ/DMAEMA (1:1 in weight) relative to the UDMA/TEGDMA (1:1 in weight) monomer., (Copyright 2000 John Wiley & Sons, Inc.)

In this experiment, we found that a potential carcinogen, 4,4'-methylenedianiline (MDA), was produced from gamma-ray irradiated potting materials, medical thermosetting polyurethane (PU). gamma-Ray irradiated PUs were immersed in either methanol or in equine serum. The time course of MDA leached from the potting materials and other variables were compared. A significant relationship was noted between the amount extracted and the rigidity of the potting material. The accumulated amount of extracted MDA (a few ppm in the original sample) increased with increasing irradiation dose by a second-order equation. One sample indicated reduced MDA elution after irradiation in the early stage. MDA extraction with serum was 82-87% that with methanol. In one case, MDA leaching into serum in the early stage was higher than that into methanol. Autoclave sterilization did not promote MDA formation, thus indicating that autoclaving would be preferable.