In the Belgian supercontainer concept, a carbon steel overpack will surround high-level waste and spent fuel containers and be encased in a cementitious buffer material. A programme of research has...

The materials corrosion test (MaCoTe) is a long‐term, multinational in situ corrosion experiment setup at the Grimsel Test Site, Switzerland. The experiment has been operating since 2014 with a focus on the corrosion behaviour of container materials for the disposal of high‐level waste and spent nuclear fuel under conditions representing a granitic deep geological repository. The experiment consists of eight modules containing metal coupons and bentonite. Two of the modules, each with a different bentonite density, have been retrieved after 394 days of exposure and have been analysed using a range of techniques aimed at studying the corrosion behaviour of the metals and the mineralogical evolution of the bentonite. Weight loss measurements show that carbon steel had a relatively low average corrosion rate (~2 µm year−1). Much lower average corrosion rates were measured for the various types of copper (0.13–0.32 µm year−1). No detectable corrosion was measured on stainless steel coupons. To date, no significant differences were observed in the corrosion behaviour and rate of the test metals in bentonite with different dry densities.

Since 2012, a long‐term in situ corrosion experiment (IC‐A) is being conducted in the Mont Terri Underground Research Laboratory in Switzerland to investigate the corrosion behaviour of candidate canister materials in conditions representative of the Swiss concept for the disposal of high‐level waste and spent nuclear fuel. To date, carbon steel and various types of copper coatings have been retrieved after different exposure periods of up to 3 years, and characterised to establish the composition of the corrosion product, the morphology of the corroded surface, the nature of the interaction between the metal and the surrounding bentonite, and the microbial populations in the bentonite and surrounding porewater. For carbon steel specimens, a complex corrosion product was identified, consisting predominantly of magnetite. Much less alteration on either the metal or the bentonite was observed in the case of copper samples. Low average anaerobic corrosion rates were measured for carbon steel and a very modest amount of alteration was identified on copper. The density and the initial form of the bentonite had a small influence on the rate of corrosion, across all materials. This paper summarises the results of the experimental programme obtained to date and discusses the relationship observed between exposure time and the evolution of the metal–bentonite interface for both carbon steel and copper.