Search

To reduce the production of wear particles and subsequent aseptic loosening, we created a human articular cartilage-mimicked surface for a highly cross-linked polyethylene liner, whose surface grafted layer consisted of a biocompatible phospholipid polymer, poly(2-methacryloyloxyethyl phosphorylcholine). Although our previous in vitro findings showed that poly(2-methacryloyloxyethyl phosphorylcholine)-grafted particles were biologically inert and caused no subsequent bone resorptive responses, and poly(2-methacryloyloxyethyl phosphorylcholine) grafting markedly decreased wear in hip joint simulator tests, the clinical safety, and in vivo wear resistance of poly(2-methacryloyloxyethyl phosphorylcholine)-grafted highly cross-linked polyethylene liners remained open to question. Therefore, in the present study, we evaluated clinical and radiographic outcomes of poly(2-methacryloyloxyethyl phosphorylcholine)-grafted highly cross-linked polyethylene liners 5 years subsequent to total hip replacement in 68 consecutive patients. No reoperation was required for any reason, and no adverse events were associated with the implanted liners. The average Harris Hip Score increased from 38.6 preoperatively to 96.5 5 years postoperatively, and health-related quality of life, as indicated by the Short Form 36 Health Survey, improved. Radiographic analyses showed no periprosthetic osteolysis or implant migration. Between 1 and 5 years postoperatively, the mean steady-state wear rate was 0.002 mm/year, which represented a marked reduction relative to other highly cross-linked polyethylene liners, and appeared to be unaffected by patient-related or surgical factors. Although longer follow up is required, poly(2-methacryloyloxyethyl phosphorylcholine)-grafted highly cross-linked polyethylene liners improved mid-term clinical outcomes. The clinical safety and wear-resistance results are encouraging with respect to the improvement of long-term clinical outcomes with poly(2-methacryloyloxyethyl phosphorylcholine)-grafted highly cross-linked polyethylene liners. © 2016 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res 35:2007-2016, 2017., (© 2016 Orthopaedic Research Society. Published by Wiley Periodicals, Inc.)

The use of larger femoral heads to prevent the dislocation of artificial hip joints has recently become more common. However, concerns about the subsequent use of thinner polyethylene liners and their effects on wear rate have arisen. Previously, we prepared and evaluated the biological and mechanical effects of a novel highly cross-linked polyethylene (CLPE) liner with a nanometer-scaled graft layer of poly(2-methacryloyloxyethyl phosphorylcholine) (PMPC). Our findings showed that the PMPC-grafted particles were biologically inert and caused no subsequent bone resorptive responses and that the PMPC-grafting markedly decreased wear in a hip joint simulator. However, the metal or ceramic femoral heads used in this previous study had a diameter of 26 mm. Here, we investigated the wear-resistance of the PMPC-grafted CLPE liner with a 40-mm femoral head during 10 × 10(6) cycles of loading in the hip joint simulator. The results provide preliminary evidence that the grafting markedly decreased gravimetric wear rate and the volume of wear particles, even when coupled with larger femoral heads. Thus, we believe the PMPC-grafting will prolong artificial hip joint longevity both by preventing aseptic loosening and by improving the stability of articular surface., (© 2015 Orthopaedic Research Society. Published by Wiley Periodicals, Inc.)

To prevent periprosthetic osteolysis and subsequent aseptic loosening of artificial hip joints, we recently developed a novel acetabular highly cross-linked polyethylene (CLPE) liner with graft polymerization of 2-methacryloyloxyethyl phosphorylcholine (MPC) on its surface. We investigated the wear resistance of the poly(MPC) (PMPC)-grafted CLPE liner during 20 million cycles in a hip joint simulator. We extended the simulator test of one liner to 70 million cycles to investigate the long-term durability of the grafting. Gravimetric, surface, and wear particle analyses revealed that PMPC grafting onto the CLPE liner surface markedly decreased the production of wear particles and showed that the effect of PMPC grafting was maintained through 70 million cycles. We believe that PMPC grafting can significantly improve the wear resistance of artificial hip joints., (© 2013 Orthopaedic Research Society. Published by Wiley Periodicals, Inc.)