The Pb(Mg1/3Nb2/3)O3-based ceramic system was obtained by using a modified variant of the conventional ceramic method in order to get pyrochlore-free compositions. Solid solutions obtained from Pb(Mg1/3Nb2/3)O3 and Ln(Mg1/2Ti1/2)O3 with Ln = Y3+, La3+, Pr3+, Nd3+ and Sm3+, were synthesized using a 3-step columbite precursor method and appropriate milling and sintering conditions. The structural phases of all sintered compositions were investigated in detail. The X-ray diffraction results demonstrate that all the samples possess a perovskite structure. The influence of dopant on the incorporation degree in the solid solutions was studied. The dielectric constants at three frequencies were measured and the influence of the dopant on these values was discussed.

The influence of the sintering temperature on the structure and on the hysteresis loops of Fe3+ doped Pb(ZrxTi1-x)O3 system has been investigated. Three compositions have been selected in the following mode: one in rhombohedral region, one in MPB region and one in tetragonal region have been obtained by solid state reaction technique. Sintering has been carried out at 12000C and 12500C respectively. The nature of the phases has been investigated in detail using X-ray diffraction analysis (XRD). All the sintered samples reveal a perovskite type structure. The surfaces have been lapped and metalized in order to obtaine the hysteresis loops at room temperature. The results showed a similar behaviour with “hard” PZT ceramics.

0.88Pb(Zr0.52Ti0.48)O3 – 0.12Pb(Mn1/3Sb2/3)O3 – 0,02 at%E piezoelectric ceramics, with E = Pr3+ were synthesized by using a conventional method, namely a solid state reaction technique. X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM) were employed for the structural and microstructural investigations. Piezoelectric methods were used for the dielectric and piezoelectric properties determination. The results of XRD show a perovskite structure and XRD patterns, indexing on a tetragonal cell structure, was carried out for the most common phases. The SEM micrographs of the sintered compositions reveal a homogenous structure with a sharp or rounded grain boundary. The modified PZT ceramic presents still superior piezoelectric properties. Based on the results obtained, one can conclude that the analysed piezoelectric ceramics are useful for device applications.