Search

In this work, low density polyethylene (LDPE) was modified in the melt state with a maleinized hyperbranched polyester polyol (HBPAM), using several proportions of dicumyl peroxide (0.5, 1.0, 1.5 and 2.0 %). Infrared analysis showed the signals of OH, C=O, -COOR and -C=C- groups of the HBPAM in the spectra of the functionalized samples (LDPE-g-HBPAM). Grafting degree (GD) was between 9.14 and 9.82 %. Melt flow index of the samples LDPE-g-HBPAM was lower than that of the LDPE, and it did not exhibit dependency on the dicumyl peroxide content and GD. Exceptfor the sample obtained with a 2.0 % of dicumyl peroxide, all melting temperatures of the samples of LDPE-g-HBPAM were similar to that of the LDPE. The melting enthalpy of the samples LDPE-g-HBPAM decreased with the concentration of dicumyl peroxide and GD. The tensile modulus of these samples was higher than that of LDPE, but the elongation at break was lower., En este trabajo, polietileno de baja densidad (PEBD) fue modificado en estado fundido con un poliester poliol altamente ramificado maleinizado (HBPAM), usando varias proporciones de peróxido de dicumilo (0.5, 1.0, 1.5 y 2.0%). El análisis infrarrojo mostró las señales de grupos OH, C=O, -COOR y -C=C- del HBPAM en el espectro de las muestras funcionalizadas (PEBD-g-HBPAM). El grado de injerto (GI) fue entre 9.14 y 9.82%. El índice de fluidez de las muestras PEBD-g-HBPAM fue más bajo que el del PEBD, y no exhibió una dependencia con el contenido de peróxido de dicumilo y GI. Excepto para la muestra obtenida con un 2.0% de peróxido de dicumilo, todas las temperaturas de fusión de las muestras de PEBD-g-HBPAM fueron similares a la del PEBD. La entalpia de fusión de las muestras de PEBD-g-HBPAM disminuyó con la concentración de peróxido de dicumilo y GI. El módulo ténsil de estas muestras fue más alto que el del PEBD, pero la elongación a la ruptura fue más baja.

This study evaluates the influence of recycled rubber (RR) with a specific particle size in the properties of blends, blended recycled polypropylene/polyethylene (RPP) and RR (RPP/RR) -- The proportions of RPP/RR employed to obtain the blends were as follows: 90/10 (PP90), 75/25 (PP75), 60/40 (PP60) and 45/55 (PP45) -- The particle size of the RR employed was 850 µm -- The properties of the blends were evaluated by rheometric, thermogravimetric (TGA), differential scanning calorimetric (DSC), scanning electronic microscopy (SEM), density, melt flow index and tensile analysis -- The maximum torque increased with the RPP content -- By DSC analysis, it was observed that the RPP exhibited two melting temperatures, the first corresponded to low density polyethylene (LDPE) and the second to polypropylene (PP) -- Furthermore, the RR affected the crystallinity of the RPP -- By using SEM and TGA analyses, it was determined that the RPP as well as RR contained fillers -- The blend densities were higher than those of RPP -- The melt flow index exhibited a trend with the amount of RR.PACS: 61.25.hk, 83.80.Va, 81.05.Lg, Este estudio evalúa la influencia de caucho reciclado (RR) con un tamaño de partícula específico en las propiedades de mezclas, mezclas de polipropileno reciclado/polietileno (RPP) y RR (RPP/RR) -- Las proporciones de RPP/RR para obtener los compósitos fueron como sigue: 90/10 (PP90), 75/25 (PP75), 60/40 (PP60) and 45/55 (PP45) -- El tamaño de partícula empleado del RR fue 850 µm -- Las propiedades de las mezclas, fueron evaluadas por análisis reométrico, termogravimétrico (TGA), calorimetría diferencial de barrido (DSC), microscopia de barrido electrónica (SEM), densidad, índice de fluidez y ténsil -- El torque máximo incrementó con el contenido de RPP -- Por análisis DSC se observó que el RPP exhibió dos temperaturas de fusión, la primera correspondió al polietileno de baja densidad (LDPE) y la segunda al polipropileno (PP) -- Además, el RR afectó la cristalinidad del RPP -- Por análisis de SEM y TGA, se determinó que el RR y el RPP contenían rellenos -- Las densidades de las mezclas fueron más altas que la del RPP -- El índice de fluidez exhibió una tendencia con la cantidad de RR.PACS: 61.25.hk, 83.80.Va, 81.05.Lg