Search

Objectives: This study evaluated the durability of bond strength to enamel using total-etch (Single Bond/SB) and self-etch (Clearfil SE Bond/CSEB) adhesives associated with neodymium:yttrium-aluminu-garnet (Nd:YAG) laser irradiation through the uncured adhesives., Methods: Bovine incisors were worn to expose an area of enamel and were divided into four groups: group 1 (control) SB + polymerization; group 2 (control) CSEB + polymerization; group 3 (laser) - SB + Nd:YAG laser (174.16 J/cm(2)) + polymerization; and group 4 (laser) CSEB + Nd:YAG (174.16 J/cm(2)) + polymerization. Blocks of composite were fabricated and stored for 24 hours or 12 months, sectioned into beams, and submitted to microtensile tests. Results were analyzed by three-way analysis of variance (ANOVA) (adhesive, technique, and storage time) and Tukey tests., Results: ANOVA revealed significant differences for adhesive × technique and technique × storage time (p<0.05). The mean values (MPa) for interaction adhesive × technique (standard deviation) were as follows: SB/control = 35.78 (6.04)a; SB/laser = 26.40 (7.25)b, CSEB/control = 26.32 (5.71)b, CSEB/laser = 23.90 (7.49)b. For interaction technique × storage time the mean values were as follows: control/24 hours = 32.58 (6.49)a; control/12 months = 29.52 (8.38)a; laser/24 hours = 29.37 (5.71)a; laser/12 months = 20.92 (6.5)b. Groups with the same letters showed no statistically significant differences., Conclusion: Scanning electron microscope analysis showed evident areas of micromorphological alterations in lased samples after 12 months of water storage. Nd:YAG laser irradiation of enamel through unpolymerized total-etch adhesive significantly reduced bond strength compared with the control. Bond strength decreased when enamel samples irradiated with Nd:YAG laser through unpolymerized adhesives were stored in water for 12 months.

Objective: This study evaluated the influence of different surface treatments on the resin bond strength/light-cured characterizing materials (LCCMs), using the intrinsic characterization technique. The intrinsic technique is characterized by the use of LCCMs between the increments of resin composite (resin/thin film of LCCM/external layer of resin covering the LCCM)., Materials and Methods: Using a silicone matrix, 240 blocks of composite (Z350/3M ESPE) were fabricated. The surfaces received different surface treatments, totaling four groups (n=60): Group C (control group), no surface treatment was used; Group PA, 37% phosphoric acid for one minute and washing the surface for two minutes; Group RD, roughening with diamond tip; and Group AO, aluminum oxide. Each group was divided into four subgroups (n=15), according to the LCCMs used: Subgroup WT, White Tetric Color pigment (Ivoclar/Vivadent) LCCM; Subgroup BT, Black Tetric Color pigment (Ivoclar/Vivadent) LCCM; Subgroup WK, White Kolor Plus pigment (Kerr) LCCM; Subgroup BK, Brown Kolor Plus pigment (Kerr) LCCM. All materials were used according to the manufacturer's instructions. After this, block composites were fabricated over the LCCMs. Specimens were sectioned and submitted to microtensile testing to evaluate the bond strength at the interface. Data were submitted to two-way analysis of variance (ANOVA) (surface treatment and LCCMs) and Tukey tests., Results: ANOVA presented a value of p<0.05. The mean values (±SD) for the factor surface treatment were as follows: Group C, 30.05 MPa (±5.88)a; Group PA, 23.46 MPa (±5.45)b; Group RD, 21.39 MPa (±6.36)b; Group AO, 15.05 MPa (±4.57)c. Groups followed by the same letters do not present significant statistical differences. The control group presented significantly higher bond strength values than the other groups. The group that received surface treatment with aluminum oxide presented significantly lower bond strength values than the other groups., Conclusion: Surface treatments of composite with phosphoric acid, diamond tip, and aluminum oxide significantly diminished the bond strength between composite and the LCCMs.

Purpose: The aim of this study was to investigate the influence of Nd:YAG laser on the shear bond strength to enamel and dentin of total and self-etch adhesives when the laser was applied over the adhesives, before they were photopolymerized, in an attempt to create a new bonding layer by dentin-adhesive melting., Material and Methods: One-hundred twenty bovine incisors were ground to obtain flat surfaces. Specimens were divided into two substrate groups (n=60): substrate E (enamel) and substrate D (dentin). Each substrate group was subdivided into four groups (n=15), according to the surface treatment accomplished: X (Xeno III self-etching adhesive, control), XL (Xeno III + laser Nd:YAG irradiation at 140 mJ/10 Hz for 60 seconds + photopolymerization, experimental), S (acid etching + Single Bond conventional adhesive, Control), and SL (acid etching + Single Bond + laser Nd:YAG at 140 mJ/10 Hz for 60 seconds + photopolymerization, experimental). The bonding area was delimited with 3-mm-diameter adhesive tape for the bonding procedures. Cylinders of composite were fabricated on the bonding area using a Teflon matrix. The teeth were stored in water at 37°C/48 h and submitted to shear testing at a crosshead speed of 0.5 mm/min in a universal testing machine. Results were analyzed with three-way analysis of variance (ANOVA; substrate, adhesive, and treatment) and Tukey tests (α=0.05). ANOVA revealed significant differences for the substrate, adhesive system, and type of treatment: lased or unlased (p<0.05). The mean shear bond strength values (MPa) for the enamel groups were X=20.2 ± 5.61, XL=23.6 ± 4.92, S=20.8 ± 4.55, SL=22.1 ± 5.14 and for the dentin groups were X=14.1 ± 7.51, XL=22.2 ± 6.45, S=11.2 ± 5.77, SL=15.9 ± 3.61. For dentin, Xeno III self-etch adhesive showed significantly higher shear bond strength compared with Single Bond total-etch adhesive; Nd:YAG laser irradiation showed significantly higher shear bond strength compared with control (unlased)., Conclusion: Nd:YAG laser application prior to photopolymerization of adhesive systems significantly increased the bond strength to dentin.

Objective: The aim of this study was to evaluate the two-year clinical performance of Class III, IV, and V composite restorations using a two-step etch-and-rinse adhesive system (2-ERA) and three one-step self-etching adhesive systems (1-SEAs)., Material and Methods: Two hundred Class III, IV, and V composite restorations were placed into 50 patients. Each patient received four composite restorations (Amaris, Voco), and these restorations were bonded with one of three 1-SEAs (Futurabond M, Voco; Clearfil S3 Bond, Kuraray; and Optibond All-in-One, Kerr) or one 2-ERA (Adper Single Bond 2/3M ESPE). The four adhesive systems were evaluated at baseline and after 24 months using the following criteria: restoration retention, marginal integrity, marginal discoloration, caries occurrence, postoperative sensitivity and preservation of tooth vitality. After two years, 162 restorations were evaluated in 41 patients. Data were analyzed using the χ(2) test (p<0.05)., Results: There were no statistically significant differences between the 2-ERA and the 1-SEAs regarding the evaluated parameters (p>0.05)., Conclusion: The 1-SEAs showed good clinical performance at the end of 24 months.

The aim of this study was to assess the influence of manganese gluconate, a chemical activator of bleaching agents, at a concentration of 0.01% on the efficiency of a 10% carbamide peroxide-based bleaching agent. Forty bovine incisors were immersed in a 25% instant coffee solution for seven days and randomly divided into two groups. Group 1 was the control group and consisted of 10% carbamide peroxide-based bleaching gel only. Group 2 consisted of 10% carbamide peroxide-based bleaching gel and 0.01% manganese gluconate. Three readings of color were taken using the Vita Easyshade spectrophotometer: the initial reading, a reading at seven days, and a reading at 14 days. Total color variation was calculated by ΔE*Lab. Data were submitted to the statistical t-test (5%), which showed that after seven days group 2 had a significant increase in the degree of tooth bleaching compared with group 1. The mean values (±SD) were 16.33 (±3.95) for group 1 and 19.29 (±4.97) for group 2. However, the results for group 1 and group 2 were similar after 14 days. Adding 0.01% manganese gluconate to 10% carbamide peroxide bleaching gel increased the degree of tooth bleaching after a seven-day treatment and did not influence the resulting shade after 14 days.

Purpose: This study evaluated the effect of bleaching gel containing 10%, 15% and 20% carbamide peroxide (CP) on the bond strength of dental enamel or dentin and resin composite restorations., Methods: The buccal surfaces of 12 bovine tooth crowns were conditioned with 37% phosphoric acid, and the adhesive resin Single Bond 2 and the resin composite Filtek Z350 were used to perform the restorations. The blocks were sectioned to obtain bar specimens. Each specimen group (enamel-E, dentin-D) was divided into four subgroups (n=15): S-artificial saliva; 10-10% CP bleaching; 15-15% CP bleaching; 20-20% CP bleaching. CP was applied for six hours daily for two weeks. The specimens were submitted to the sigma test in a universal testing machine. The data were analyzed by one-way ANOVA and the Tukey post-hoc test and a correlation analysis (r) was performed., Results: For Group E, the mean value (+/- standard-deviation) was 21.86 (+/- 6.03)a, 18.91 (+/- 8.31)ab, 15.43 (+/- 7.44)b and 10.6 (+/- 4.94)c for ES, E10, E15 and E20, respectively. For Group D, the a values were 34.73 (+/- 4.68)a, 35.12 (+/- 13.43)a, 29.67 (+/- 6.84)ab and 24.56 (+/- 6.54)b for DS, D10, D15 and D20, respectively. A negative correlation between the CP concentration and mean values was observed for both the enamel (r=-0.95) and dentin (r=-0.85) groups., Conclusion: In the current study, the bond strength of the restoration to enamel and the restoration to dentin were influenced by the application of CP and was dependent on the CP concentration in the bleaching gel.

Purpose: This study compared five types of chemical catalyzing agents added to 35% hydrogen peroxide gel, with regard to their capacity of intensifying in-office dental bleaching results., Methods: One-hundred and twenty bovine incisors were used, of which the crowns and roots were cut in the incisor-apical direction, to acquire the dimensions of a human central incisor. The specimens were sectioned in the mesiodistal direction by means of two longitudinal cuts, the lingual halves being discarded. The vestibular halves received prophylaxis with a bicarbonate jet, ultrasound cleaning and acid etching on the dentinal portion. Next, the specimens were stored in receptacles containing a 25% instant coffee solution for two weeks. After the darkening period, initial measurement of the shade obtained was taken with the Easy Shade appliance, which allowed it to be quantified by the CIELab method. The samples were divided into six groups, corresponding to the chemical activator used: a) none (CON); b) ferric chloride (CF); c) ferrous sulphate (SF); d) manganese gluconate (GM); e) manganese chloride (CM); f) mulberry root extract (RA). Each group received three 10-minute applications of the gels containing the respective activating agents. Next, a new shade measurement was made., Results: The Analysis of Variance and Tukey tests (alpha = 5%) showed statistically significant differences for the shade perception values (p = 0.002). Groups GM, CM and RA showed significantly higher means than the control group., Conclusion: The presence of some chemical activators is capable of resulting in a significant increase in tooth shade variation.