Search

Two silane-based hybrid coatings were developed to modify the surface energy of phenolic resin impregnated paper. The coated paper samples were further pressed onto surfaces of plywood. The surface properties and water repellence of coated paper were investigated by AFM, XPS and water contact angle measurements. The water absorption of plywood with pressed paper was studied by water uptake tests. It was found that the sol-gel coatings had slightly improved the water repellence of the impregnated paper. The water absorption of plywood was also slightly decreased.

The sintering behaviour of several ceramics prepared using a previously selected mixture of incinerated paper mill sludge and glass cullet which was blended with 10, 20, 30 and 40 wt% of some natural clayey materials has been studied. Three natural commercial product were used: a red clay, a yellow clay and a kaolin. Mixtures were blended by wet attrition milling, dried, sieved, pressed into specimens and then fired for 1 h at temperatures ranging from 1040 to 1140 °C. The resulting materials were characterized by water absorption, shrinkage and crystallographic composition. It was observed that materials containing kaolin display the best overall behaviour independently of the quantity of kaolin introduced. Conversely the optimal sintering temperature, and consequently the best properties of materials prepared using red or yellow clay was found above 1080 °C and depends of their specific composition being affected by the amount of clay added.

Graphene is a flat monolayer of carbon atoms tightly packed into a two-dimensional 2D honeycomb lattice. The graphene sheets in graphite interact with each other through van der Waals forces to form layered structure. The first graphene sheets were obtained by extracting monolayer sheets from the three-dimensional graphite using a technique called micromechanical cleavage in 2004 [. There are numerous attempts in the literature to produce monolayer graphene sheets by the treatment of graphite. The first work was conducted by Brodie in 1859 and GO was prepared by repeated treatment of Ceylon graphite with an oxidation mixture consisting of potassium chlorate and fuming nitric acid [. Then, in 1898, Staudenmaier produced graphite oxide (GO) by the oxidation of graphite in concentrated sulfuric acid and nitric acid with potassium chlorate [. However, this method was time consuming and hazardous. Hummers and Offeman found a rapid and safer method for the preparation of GO and in this method graphite was oxidized in water free mixture of sulfuric acid, sodium nitrate and potassium permanganate [.

Zinc is a base metal present in several products of general use, and therefore found in numerous residues and end-of-life products. The two main sources of zinc containing wastes are spent Zn-MnO2 portable batteries and electric arc furnace (EAF) dusts from steelmaking plants. The recovery of metals from these residues by appropriate recycling processes is mandatory due to environmental, economic and resource conservation issues. Concerning the similar composition of both residues, their simultaneous processing can be envisaged. The research herein described consists on the hydrometallurgical treatment of zinc bearing waste, where several leaching routes for solubilising metals, mainly zinc, are studied. The leaching of shredded batteries and EAF dusts was carried out using three different leaching solutions containing sulfuric acid, hydrochloric acid or ammonium chloride. The acid leaching of zinc in the oxide form (zincite) using both acids, was very efficient and quick, allowing the recovery of practically all Zn contained in batteries and about of 80% of Zn in dusts. Regarding to the leaching media the behaviour of lead oxides present in dusts was different, being insoluble with H2SO4 and partially soluble with HCl (40-90% yield, depending on conditions). For battery waste stream, manganese is also other important metal, which oxides were only partially soluble in acid media, attaining a maximum leaching yield of 90% Mn. Iron, considered a contaminant in both residues, was partially leached and required further purification steps. The use of an ammoniacal medium (NH4Cl) was very selective for zinc, being iron practically insoluble. However, the maximum zinc leaching yield attained for both residues was only near 60%. Under these conditions, manganese contained in batteries was very insoluble while lead from dusts was leached up to 70% due to the relative solubility of lead chloride. This research showed that hydrometallurgical treatment can provide versatile solutions for recycling metals from Zn waste. Ammoniacal leaching allows high selectivity for zinc but less recovery efficiency is attained, while acid leaching allows higher metal recovery yields but unwanted elements like iron are co-dissolved.