Search

Eggshells are daily food waste disposed of in landfills, producing environmental issues and an unpleasant odour. Eggshells powder may be suitably applied as a filler in epoxy resins to improve their mechanical properties. The material properties and fracture energy of toughened epoxy with eggshell powder (TEEP) were measured and investigated. Dog-bone specimens were fabricated to investigate the mechanical properties of TEEP (i.e. elastic modulus, Poisson's ratios and tensile strength) and tested under quasi-static tensile loading. Double Cantilever Beam (DCB) and End-Notched Flexure (ENF) tests were used to determine the mode I and Mode II fracture energies of TEEP specimens, respectively. For this purpose, oven-dried eggshells were crushed into particles size of 100 µm. The volume fraction of eggshell powder as filler in TEEP is designated as 0%, 2.5%, 5%, and 10%. The epoxy resin system was made by mixing EPIKOTE Resin 828 and Hardener 651 with a mixing ratio of 5:2 by weight. The results showed that the tensile strength, elastic modulus, fracture energy in Mode I and Mode II were optimum at TEEP 5% with an enhancement of 36.8%, 24.9%, 60.3% and 166.3%, respectively compared to that of neat epoxy. This is due to better surface roughness and the ability of eggshell powder as a crack arrestor. However, TEEP with 10% eggshell prone to agglomeration of eggshell powder caused poor bonding with epoxy resin and affect the mechanical properties. [ABSTRACT FROM AUTHOR]

The study investigated the effects of ageing on the tensile properties and fracture behaviour of an epoxy filled with inorganic fillers having different reactivity to water, such as fly ash, calcium carbonate (CaCO3), and Portland cement. CaCO3 is insoluble in water, whereas fly ash and cement are reactive to water; however, fly ash is less reactive than cement. The water absorption, tensile properties, and mode-I fracture toughness of the epoxy containing 7 wt% of filler were compared after ageing the composites in distilled water at 50 °C. Gravimetric analyses showed that compared to neat epoxy, CaCO3 slightly decreased the equilibrium water uptake of the filled epoxy, whereas fly ash and cement increased the equilibrium water uptake. Compared to the other fillers, the tensile strength of CaCO3-filled epoxy was inferior in both dry and wet conditions. However, in dry condition, the elastic modulus of CaCO3-filled epoxy was slightly higher. Overall, the fly ash-filled epoxy showed better tensile and fracture properties in both dry and wet conditions although it absorbed more water than the other fillers did. Scanning electron microscopy revealed that crack deflection played a dominant role in the toughening of filled epoxies in both dry and wet conditions. [ABSTRACT FROM AUTHOR]

This paper presents the water uptake and its effect on the tensile properties and the translaminar fracture toughness of glass fiber reinforced unsaturated polyester composites (GFRUPs) aged in distilled and saltwater at a temperature of 50 °C, in steady and fluctuating conditions. In both conditions, the GFRUPs aged in distilled water absorbed more water than in saltwater. The tensile strength of GFRUP tends to decrease with the immersion time in both aging media, but the decrease of tensile strength in saltwater is worse than that in distilled water. In steady condition, the translaminar fracture toughness increases after 7 days immersion and then tends to decrease beyond that immersion time. While in fluctuating condition, the translaminar fracture toughness increases until 15 days immersion and then gradually decreases up to 30 days immersion. Overall, the degradation of mechanical properties in the fluctuating condition is lower than in the steady condition. [ABSTRACT FROM AUTHOR]

The paper presents a comparison of the cohesive zone model (CZM) and the continuum damage mechanics approach in predicting the static failure of a single lap joint (SLJ). The effect of mesh size and viscosity were studied to give more understanding on the failure load and computational time. Both the load–displacement response and the backface strain technique were utilised to compare the validity of predictions. Peel and shear stress and damage distributions along with the damage progression are compared to understand the behaviour of the models in predicting the static failure response. In general, both approaches show good accuracy in predicting the failure load; however, the cohesive zone approach requires shorter computation time than the continuum damage approach. The continuum damage approach shows some mesh-dependency particularly for elements with high aspect ratios, whereas the cohesive zone approach is not. The continuum damage approach is less sensitive than the cohesive zone approach to the artificial damping required to achieve convergence. Another interesting finding is using the same ultimate stress level of damage in the continuum damage approach at the peak load is much lower than that in the cohesive approach; but the failure process in this approach is faster. [ABSTRACT FROM PUBLISHER]

Experimental studies have been undertaken to investigate the static and fatigue responses of metal laminate doublers (MLD) joints under tension loading after ageing in deionised water at a temperature of 50 °C up to 2 years. It was found that absorbed water did not have a significant effect on the static and fatigue degradation of the MLD; however, corrosion pits located on the aluminium surfaces caused a reduction in fatigue life. Inevitably, the laminate contained butts where co-planar aluminium sheets were joined, and it was found that the position of the butt affected the static response of the MLD but, due to a restricted data set, it has not been possible to assess the effect under fatigue loading. The backface strain technique in conjunction with video microscopy has been utilised to monitor the damage of the adhesive bondlines, the butts and the aluminium layers and successfully identified both the localised and the global damage in the MLD. Most of fatigue failures initiated at the stringer bondline edge and at the aluminium layers where the butt was located. A careful design should be made to reduce the stress concentration at the stringer edge and to avoid positioning the butts at the upper layer of aluminium close to the stringer edge. [ABSTRACT FROM PUBLISHER]

The most potent toxins secreted by pathogenic bacteria contain enzymatic moieties that must reach the cytosol of target cells to exert their full toxicity. Toxins such as anthrax, diphtheria, and botulinum toxin all use three well-defined functional domains to intoxicate cells: a receptor-binding moiety that triggers endocytosis into acidified vesicles by binding to a specific host-cell receptor, a translocation domain that forms pores across the endosomal membrane in response to acidic pH, and an enzyme that translocates through these pores to catalytically inactivate an essential host cytosolic substrate. The homologous toxins A (TcdA) and Toxin B (TcdB) secreted byClostridium difficileare large enzyme-containing toxins that for many years have eluded characterization. The cell-surface receptors for these toxins, the non-classical nature of the pores that they form in membranes, and mechanism of translocation have remained undefined, exacerbated, in part, by the lack of any structural information for the central ∼1000 amino acid translocation domain. Recent advances in the identification of receptors for TcdB, high-resolution structural information for the translocation domain, and a model for the pore have begun to shed light on the mode-of-action of these toxins. Here, we will review TcdA/TcdB uptake and entry into mammalian cells, with focus on receptor binding, endocytosis, pore formation, and translocation. We will highlight how these toxins diverge from classical models of translocating toxins, and offer our perspective on key unanswered questions for TcdA/TcdB binding and entry into mammalian cells. [ABSTRACT FROM AUTHOR]

DNA-dependent protein kinase (DNA-PK) orchestrates DNA repair by regulating access to breaks through autophosphorylations within two clusters of sites (ABCDE and PQR). Blocking ABCDE phosphorylation (by alanine mutation) imparts a dominant negative effect, rendering cells hypersensitive to agents that cause DNA double-strand breaks. Here, a mutational approach is used to address the mechanistic basis of this dominant negative effect. Blocking ABCDE phosphorylation hypersensitizes cells to most types of DNA damage (base damage, cross-links, breaks, and damage induced by replication stress), suggesting that DNA-PK binds DNA ends that result from many DNA lesions and that blocking ABCDE phosphorylation sequesters these DNA ends from other repair pathways. This dominant negative effect requires DNA-PK's catalytic activity, as well as phosphorylation of multiple (non-ABCDE) DNA-PK catalytic subunit (DNA-PKcs) sites. PSIPRED analysis indicates that the ABCDE sites are located in the only contiguous extended region of this huge protein that is predicted to be disordered, suggesting a regulatory role(s) and perhaps explaining the large impact ABCDE phosphorylation has on the enzyme's function. Moreover, additional sites in this disordered region contribute to the ABCDE cluster. These data, coupled with recent structural data, suggest a model whereby early phosphorylations promote initiation of nonhomologous end joining (NHEJ), whereas ABCDE phosphorylations, potentially located in a "hinge" region between the two domains, lead to regulated conformational changes that initially promote NHEJ and eventually disengage NHEJ. [ABSTRACT FROM AUTHOR]