The plastic stability of bimetals composed of a Ti-based metallic glass composite (MGC) and a pure titanium (PT) under tension has been investigated. The results reveal that the plastic stability of the MGC/PT bimetal is strongly dependent on the thickness fraction of the MGC: when the thickness fraction of the MGC decreases to a critical value, a homogeneous plastic deformation occurs in the MGC/PT bimetals, i.e. the strain localization and necking of the MGC is effectively suppressed. This unique phenomenon is explained using the normalized strain-hardening rate, and the quantitative relationship between the normalized strain-hardening rate of the MGC/PT bimetals and the thickness fraction of the MGC is thereby established. [ABSTRACT FROM AUTHOR]

Large NdP 5 O 14 crystal with dimension of 15 × 25 × 60 mm 3 has been grown by flux method. The spontaneous strains and ferroelastic domain structures have been investigated by high resolution X-ray diffractometry for the first time. The reflection peak separations resulting from the misorientation between matrix domain and ferroelastic domain were observed in the rocking curves for several different reflections. Based on the features of the reflection peak separations, the ferroelastic domain structures were determined. It is found that most of the ferroelastic domains in NdP 5 O 14 are of type-a, while type-b ferroelastic domains only appear in the serious strain regions. Based on the domain structures of NdP 5 O 14 , the reflection peak separations for 802, 402 and 204 reflections were calculated respectively. And the experimental observations are in agreement with the calculations very well. In addition, the spontaneous strain in NdP 5 O 14 was determined to be 0.0082 by measuring the peak separation between two 800 diffraction from the matrix domain and the ferroelastic domain respectively. A detailed discussion on domain structures in the crystal is given in terms of structural and symmetric analyses. [ABSTRACT FROM AUTHOR]