In this study, we considered changes in the surface chemistry after introducing fluorine into the surface layer of nanoporous activated carbon (BAU) produced from the birch wood. Here, we examined the BAU treated with 1,1,1,2-tetrafluoroethane at the selected temperature in the range of 400–800 °C. Diverse methods, including chemical analysis, nitrogen adsorption–desorption, SEM–EDS, XPS, and 19F solid-state NMR, were used for the characterization of the prepared materials. It was found that one can introduce from 0.17 to 0.42 mmol of F per gram of BAU using fluoroalkylation at 400–500 °C. Increasing the temperature to 600 °C increases the fluorination efficiency, and the relatively high fluorine content of 1.86 mmol of F per gram of BAU can be reached. At least three group types, namely, C–F, CF2, and CF3 groups, were found by XPS and 19F solid-state NMR after such treatment. The content of “semi-ionic” fluorine drastically increases in the surface layer after high-temperature fluoroalkylation at 700 °C and 800 °C. This “semi-ionic” fluorine, in the form of C–F and CF2 groups, is directly conjugated with the π-electron system of the carbon matrix.

In this study, we report soft and solvothermal methods for synthesis of zinc oxide nanoparticles (ZnO NPs). Both methods involve a precursor and are carried out at the middle low-temperature regime. The effect of different solvents on the ZnO NPs properties was studied. The nonlinear optical (NLO) response of the NPs was analyzed by the self-action of picosecond laser pulses at 1064 nm and by second harmonic generation (SHG) of a femtosecond laser pulses pump at 800 nm. The luminescence was studied within UV-visible ranges. It was shown that the NLO response efficiency significantly depends on the solvent. The obtained SHG efficiency of small (~2 nm) ZnO NPs is comparable to the one obtained for large (~150 nm) commercial ZnO NPs. The observed results are important for the application of the ZnO NPs in biolabeling. Electronic supplementary material The online version of this article (doi:10.1186/s11671-017-1934-y) contains supplementary material, which is available to authorized users.