The resistive switching behavior of the solution processed SiOx device was investigated by inserting TiO2 nanoparticles (NPs). Compared to the pristine SiOx device, the TiO2 NPs inserted SiOx (SiOx@TiO2 NPs) device achieves outstanding switching characteristics, namely a higher ratio of SET/RESET, lower operating voltages, improved cycle-to-cycle variability, faster switching speed, and multiple-RESET states. Density functional theory calculation (DFT) and circuit breaker simulation (CB) were used to detail the origin of the outstanding switching characteristic of the SiOx@TiO2 NPs. The improvement in resistive switching is mainly based on the difference in formation/rupture of the conductive path in the SiO2 and SiO2@TiO2 NPs devices. In particular, the reduction of resistance and lower switching voltage of TiO2 NPs control the formation and rupture of the conductive path to achieve more abrupt switching between SET/RESET with higher on/off ratio. This method of combined DFT calculation and CB offers a promising approach for high-performance non-volatile memory applications.

We report the growth mechanism and optical characteristics of type-II band-aligned GaSb quantum dots (QDs) grown on GaAs using a droplet epitaxy-driven nanowire formation mechanism with molecular beam epitaxy. Using transmission electron microscopy and scanning electron microscopy images, we confirmed that the QDs, which comprised zinc-blende crystal structures with hexagonal shapes, were successfully grown through the formation of a nanowire from a Ga droplet, with reduced strain between GaAs and GaSb. Photoluminescence (PL) peaks of GaSb capped by a GaAs layer were observed at 1.11 eV, 1.26 eV, and 1.47 eV, assigned to the QDs, a wetting-like layer (WLL), and bulk GaAs, respectively, at the measurement temperature of 14 K and excitation laser power of 30 mW. The integrated PL intensity of the QDs was significantly stronger than that of the WLL, which indicated well-grown GaSb QDs on GaAs and the generation of an interlayer exciton, as shown in the power- and temperature-dependent PL spectra, respectively. In addition, time-resolved PL data showed that the GaSb QD and GaAs layers formed a self-aligned type-II band alignment; the temperature-dependent PL data exhibited a high equivalent internal quantum efficiency of 15 ± 0.2%.