The crystallization behavior and magnetic properties of Fe62Co10Si15−xB18−yNb(x + y)−5amorphous alloys with x = 0–5 and y = 0–5 were examined. Primary crystallization temperature of Fe62Co10Si15−xB13Nbx and Fe62Co10Si10B18−yNbyalloys increased with the addition of Nb. The primary and secondary crystallization temperatures were well separated when the Nb content is above 4 at%. The alloys with 15–18 at% B showed a distinct supercooled region. The Nb addition decreased the Curie temperature as well as room temperature saturation magnetization. The glassy-type Fe62Co10Si10B18 alloy exhibited good soft magnetic properties as well as a supercooled liquid region of 39 K. The finding of the glassy-type Fe-based alloy without Nb element exhibiting high Bs above 1.4 T is promising for future use as a soft magnetic glass material.

Crystallization and magnetic behavior of melt-spun Fe62Co10Si10B13Nb4TM1 amorphous ribbon where TM = Ni, Cr, V, Pd, Pt, Ti, Ta and Zr were examined. The alloy with Pt as transition metal showed the lowest crystallization temperature of 823 K among the studied alloys. Significant increase in crystallization temperature was observed when the atomic radius of the substituted transition metal was varied from that of Pt. High Curie temperature and high saturation magnetization were recognized for the alloys containing Pd, Pt or Ti. The amorphous alloys except the alloys containing Ti or V showed good soft magnetic properties.