We demonstrate a facile, two-step coating/calcination approach to grow a uniform MnO nanoparticle@ mesoporous carbon (MnO@C) composite on conducting substrates, by direct coating of the Mn-oleate precursor solution without any conducting/binding reagents, and subsequent thermal calcination. The monodispersed, sub-10 nmMnOnanoparticles offer high theoretical energy storage capacities and catalytic properties, and the mesoporous carbon coating allows for enhanced electrolyte transport and charge transfer towards/from MnO surface. In addition, the direct growth and attachment of the MnO@C nanocomposite in the supporting conductive substrates provide much reduced contact resistances and efficient charge transfer. These excellent features allow the use of MnO@C nanocomposites as lithium-ion battery and supercapacitor electrodes for energy storage, with high reversible capacity at large current densities, as well as excellent cycling and mechanical stabilities. Moreover, this MnO@C nanocomposite has also demonstrated a high sensitivity for H2O2 detection, and also exhibited attractive potential for the tumor cell analysis. [ABSTRACT FROM AUTHOR]

Composites of styrene butadiene rubber (SBR), hydrogenated acrylonitrile-butadiene rubber (HNBR) and silica were prepared. Sulfur (S), dicumyl peroxide (DCP) and a combination of S and DCP (M) were used as curing agents, respectively. The morphology of the composites with different blend ratio was examined to correlate with observations on mechanical properties by scanning electron microscopy. The effects of blend ratio and curing systems on the curing characteristics and mechanical properties, such as stress-strain behavior, tensile strength, elongation at break and hardness of SBR/HNBR/Silica composites, were studied. Composites prepared by M curing systems showed comparatively better mechanical properties, wet traction and rolling resistance than S and D curing systems. The tensile strength, tear strength, and elongation at break were improved by adding HNBR for M curing systems. The wet traction of the vulcanizates containing HNBR was better than that of the vulcanizates without HNBR. A relatively uniform dispersion of silica was observed for SBR/HNBR/silica compositions compared with SBR/silica composites. [ABSTRACT FROM AUTHOR]