Double-clad optical fiber with a multi-ring core profile doped with thulium and holmium fabricated by Modified Chemical Vapor Deposition Chelate Doping Technology (MCVD-CDT) is presented. The measured Tm2O3 and Ho2O3 complexes' weight concentrations were 0.5% and 0.2% respectively. Numerical analyses show weakly guiding conditions and 42.2 µm of MFD LP01 at 2000 nm. The low NA numerical aperture (NA = 0.054) was obtained for the 20/250 µm core/cladding ratio optical fiber construction. The emission spectra in the range of 1.6–2.1 µm vs. the fiber length are presented. The full width at half maximum (FWHM) decreases from 318 to 270 nm for fiber lengths from 2 to 10 m. The presented fiber design is of interest for the development of new construction of optical fibers operating in the eye-safe spectral range. [ABSTRACT FROM AUTHOR]

Fluoroindate glasses co-doped with Pr3+/Er3+ ions were synthesized and their near-infrared luminescence properties have been examined under selective excitation wavelengths. For the Pr3+/Er3+ co-doped glass samples several radiative and nonradiative relaxation channels and their mechanisms are proposed under direct excitation of Pr3+ and/or Er3+. The energy transfer processes between Pr3+ and Er3+ ions in fluoroindate glasses were identified. In particular, broadband near-infrared luminescence (FWHM = 278 nm) associated to the 1G4 → 3H5 (Pr3+), 1D2 → 1G4 (Pr3+) and 4I13/2 → 4I15/2 (Er3+) transitions of rare earth ions in fluoroindate glass is successfully observed under direct excitation at 483 nm. Near-infrared luminescence spectra and their decays for glass samples co-doped with Pr3+/Er3+ are compared to the experimental results obtained for fluoroindate glasses singly doped with rare earth ions. [ABSTRACT FROM AUTHOR]

Influence of titanium dioxide concentration on thermal properties of germanate-based glasses has been studied. Germanate glasses varying with TiO2 content were examined using DSC methods. The DSC curves exhibit two exothermic peaks, when GeO2 is substituted by TiO2. Based on DSC measurements, characteristic temperatures were determined. The studies demonstrate that glass transition temperature increases, whereas thermal stability parameters are reduced with increasing TiO2 concentration. The DSC curves were also acquired with different heating rates, and the Kissinger method was used to calculate the activation energy. X-ray diffraction analysis for germanate-based glass with TiO2 indicates that crystallization processes are more complex and several phases are formed during annealing. The absorption and emission spectra of glass samples doped with Er3+ ions were also examined before and after annealing process. [ABSTRACT FROM AUTHOR]