Search

The anaerobic biodegradation rates of four different sizes of poly (lactic acid) (PLA) films (thickness 25 μm) in anaerobic sludge at 55 °C were examined. The anaerobic biodegradation rates of small pieces of PLA film were slower than for large pieces of PLA film. We also examined whether PLA film could also be used as a reference material in the anaerobic biodegradation test in addition to PLA powder. The anaerobic biodegradation rate of PLA film became slower with lower activity sludge, but the rate of decrease was gradual, and the anaerobic biodegradation rate of PLA film was faster than the PLA powder (125-250 μm). The anaerobic biodegradation rate of the PLA powder (125-250 μm) reflected the plastic anaerobic biodegradation activity of the sludge more accurately than the thin PLA film (thickness 25 μm). Consequently, PLA powder (125-250 μm) is more suitable than thin PLA film (thickness < 25 μm) for use as a reference material to assess the plastic anaerobic biodegradation activity of the sludge in an anaerobic biodegradation test at 55 °C. [ABSTRACT FROM AUTHOR]

The evaluation method of biomass carbon ratio of polymer composite samples including organic and inorganic carbons individually was investigated. Biodegradable plastics and biobased plastics can have their mechanical properties improved by combining with inorganic fillers. Polymer composites consisting of biodegradable plastics and carbonate were prepared by two different methods. Poly(lactic acid) (PLA) composite was prepared by synthesis from l-lactide with catalyst and calcium carbonate (CaCO3) powders from lime. Poly(butylene succinate) (PBS) composite was prepared by hot-pressing the mixture of PBS powder and CaCO3 powders from oyster shells. The mechanical properties of composite samples were investigated by a tensile test and a compression test using an Instron type mechanical tester. Tensile test with a dumbbell shape specimen was performed for PBS composite samples and compression test with a column shape specimen for PLA composite samples. Strength, elastic modulus and fracture strain were obtained from the above tests. Biomass carbon ratio is regulated in the American Standards for Testing and Materials (ASTM). In ASTM standards on biomass carbon ratio, it is required that carbon atoms from carbonates, such as CaCO3, are omitted. Biomass carbon ratio was evaluated by ratio of 14C to 12C in the samples using Accelerator Mass Spectrometry (AMS). The effect of pretreatment, such as oxidation temperature and reaction by acid, on results of biomass carbon ratio was investigated. Mechanical properties decrease with increasing CaCO3 content. The possibility of an evaluation method of biomass carbon ratio of materials including organic and inorganic carbons was shown. [ABSTRACT FROM AUTHOR]

The biobased contents of raw materials such as starches, sugar, chitin, or wood powders for biomass plastics were measured using Accelerator Mass Spectrometry (AMS) based on ASTM D6866. AMS measures the isotope carbon ratio of 14C to 12C and 13C in graphite derived from sample powders. The biobased contents of starches, sugar or chitin were almost 100% which means that they are fully biobased. The biobased contents of the wood powders were over 140% due to the effect of the post 1950s 14C injection due to nuclear testing. Poly(ε-caprolactone) (PCL) composite samples were prepared using the polymerization and direct molding method. The starting compound was the ε-caprolactone monomer liquid combined with cellulose and inorganic fillers using aluminum triflate as a catalyst at 80 °C for 6 or 24 h. PCL cylinder-shaped composite samples with a homogeneously dispersed cellulose filler were prepared with Mn = 4,600 (Mw/Mn = 2.9). The biobased content of the PCL composite with 50 wt% cellulose filler (51.67%) measured using AMS was slightly higher than the carbon ratio of cellulose in the starting powder samples (41.3 mol%). This is due to the higher biobased content (112.70%) of the cellulose filler used in this study. The biobased content of the polymer composite powders by AMS was found not to be affected by the presence of inorganic fillers, such as talc. [ABSTRACT FROM AUTHOR]

Returnable cups made of poly(lactic acid) (PLA) are employed as an example of products made of biodegradable plastics. Two kinds of PLA samples plates and powders with different shapes were prepared from PLA cups. The plates were cut from a cup using nippers. Powders were prepared using a rotation mechanical mixer for 45 min. PLA powders were separated by sieves with 60 meshes (250 μm) into a size ranging from 0 to 250 μm. An average diameter of powders separated by a sieve is 169 μm. Biodegradation tests of PLA plates, PLA powders and cellulose powders in controlled compost at 58 °C were performed using a Microbial Oxidative Degradation Analyzer (MODA) instrument according to ISO 14855-2. PLA powders showed almost the same biodegradation curve as that of cellulose powders. PLA plates biodegraded at a slower rate than PLA powders. [ABSTRACT FROM AUTHOR]

Polycaprolactone (PCL) powders were prepared from PCL pellets using a rotation mechanical mixer. PCL powders were separated by sieves with 60 and 120 meshes into four classes; 0–125 μm, 125–250 μm, 0–250 μm and 250–500 μm. Biodegradation tests of PCL powders and cellulose powders in an aqueous solution at 25°C were performed using the coulometer according to ISO 14851. Biodegradation tests of PCL powders and cellulose powders in controlled compost at 58°C were performed by the Mitsui Chemical Analysis and Consulting Service, Inc. according to ISO 14855-1 and by using the Microbial Oxidative Degradation Analyzer (MODA) instrument according to ISO/DIS 14855-2. PCL powders were faster biodegraded than cellulose powders. The reproducibility of biodegradation of PCL powders is excellent. Differences in the biodegradation of PCL powders with different class were not observed by the ISO 14851 and ISO/DIS 14855-2. An enzymatic degradation test of PCL powders with different class was studied using an enzyme of Amano Lipase PS. PCL with smaller particle size was faster degraded by the enzyme. PCL powders with regulated sizes from 125 μm to 250 μm are proposed as a reference material for the biodegradation test. [ABSTRACT FROM AUTHOR]