The purpose of this study was to investigate the antibacterial effect of silver nanoparticles in chitosan-poly(ethylene glycol) suspension. The silver nanoparticles (AgNPs) were prepared by use of an environmentally benign method from chitosan (Cts) and poly(ethylene glycol) (PEG) at moderate temperature and with stirring for different times. Silver nitrate (AgNO) was used as the metal precursor and Cts and PEG were used as solid support and polymeric stabilizer, respectively. The antibacterial activity of silver-chitosan-poly(ethylene glycol) nanocomposites (Ag-Cts-PEG NCs) against Staphylococcus aureus, Micrococcus luteum, Pseudomonas aeruginosa, and Escherichia coli was tested by use of the Mueller-Hinton agar disk-diffusion method. Formation of AgNPs was determined by UV-visible spectroscopy; surface plasmon absorption maxima were observed at 415-430 nm in the UV-visible spectrum. The peaks in the XRD pattern confirmed that the AgNPs had a face-centered cubic structure; peaks of contaminated crystalline phases were not observed. Transmission electron microscopy (TEM) revealed that the AgNPs synthesized were spherical. The optimum stirring time for synthesis of the smallest particle size (mean diameter 5.50 nm) was 12 h. The AgNPs in Cts-PEG were effective against all the bacteria tested. Higher antibacterial activity was observed for AgNPs with smaller size. These results suggest that AgNPs can be used as an effective inhibitor of bacteria and can be used in medical applications. These results also suggest that AgNPs were successfully synthesized in Cts-PEG suspension at moderate temperature with different stirring times. [ABSTRACT FROM AUTHOR]

The purpose of this study was to investigate the effect of OH concentration on the size of Fe3O4 nanoparticles (Fe3O4-NPs). Fe3O4-NPs with different cubic nanocrystal structure and percentage Fe3O4 content were successfully prepared, by use of the chemical co-precipitation method, on the exterior surface of talc, as solid substrate, by an environmentally friendly process. Ferric chloride, ferrous chloride, and sodium hydroxide were used as iron oxide precursors and reducing agent. The results showed that the morphology of the Fe3O4-NPs can be adjusted by changing the reaction conditions, for example volume of reducing agent and concentration of iron salts. Different size, dispersal, and the magnetic properties were obtained by changing the concentration of iron salts and NaOH. The products were characterized by powder X-ray diffraction, scanning electron microscopy, transmission electron microscopy, energy-dispersive X-ray spectroscopy, and Fourier-transform infrared spectroscopy. The reaction was conducted in a non-oxidizing, oxygen-free environment. Because the interlamellar spacing of the talc was almost unchanged (ds = 0.94-0.87 nm), the Fe3O4-NPs were formed on the exterior surface of the talc. The average diameter of the Fe3O4-NCs could be varied from 6.62-8.13 nm in adjusting the concentration of NaOH. The size of the nanoparticles decreased as the amount of reducing agent was increased. These talc-Fe3O4nanocomposites (talc-Fe3O4-NCs) may have potential applications in the chemical and biological industries. [ABSTRACT FROM AUTHOR]