Uniform arrays of the InSb quantum dots with a surface density of nQD = 2 × 109 cm–2 were obtained by liquid phase epitaxy on a matrix layer based on a multicomponent InGaAsSb solid solution lattice-matched with the GaSb substrate. The change in the composition of the cationic part of the matrix by using the epitaxial matrix layer allowed to lower the temperature of the epitaxy to T = 430°C and determined the shape of a typical InSb quantum dot in the form of a truncated cone with average values of height h = 3 nm and diameter d = 30 nm, which corresponded to the aspect ratio L = h/d = 0.1. [ABSTRACT FROM AUTHOR]

Arrays of coherent InSb quantum dots (QDs) have been fabricated by liquid-phase epitaxy on InAs substrates in the temperature range T = 420–450°C. The QDs with a density of (0.9−2) × 1010 cm−2 were 3 nm high and 13 nm in diameter. A bimodal QD size distribution was observed, which was accounted for by a combined growth mechanism of these nanoobjects. Structural characteristics of a separate InSb QD formed on the InAs surface were studied for the first time by atomic-force and transmission electron microscopies. Moire fringes were observed for the first time for QDs in the InSb/InAs system, with the moire period of 3.5 nm corresponding to InSb QDs without an admixture of arsenic. [ABSTRACT FROM AUTHOR]

The first original results on the growth of quantum dots (QDs) in the InSb/InAs system by liquid phase epitaxy (LPE) are reported. The density and dimensions of QDs were studied by methods of scanning probe microscopy and atomic force microscopy. The surface density, shapes, and dimensions of LPE-grown nanoislands depend on the growth conditions (temperature, cooling rate, and solution melt-substrate contact time). In the interval of temperatures T = 420–445°C, homogeneous arrays of InSb quantum dots on InAs(100) substrates were obtained with an average height of H = 3.4 ± 1nm, a radius of R = 27.2 ± 7.5 nm, and a density of up to 1.9 × 1010 cm−2. [ABSTRACT FROM AUTHOR]