The high temperature corrosion behavior of N07263, N06600, and N06625 in LiCl-LiO molten salt was investigated at temperatures ranging from 650 to 850 °C in a glove box. The high temperature corrosion behavior was observed using measurements of the oxide morphology and thickness, the extent of internal corrosion, and the compositional changes in the scale and in the substrate. Corrosion tests were performed, and these demonstrated that the main corrosion products were Fe(Ni,Co), FeNi, and LiCrO. The internal corrosion of N07263 was localized, while that of N06600 maintained intergranular corrosion throughout the test temperature range. N06625 exhibited uniform intergranular corrosion behaviors at low and high temperatures. N07263 exhibited superior corrosion resistance, as evidenced by its corrosion layer which was more continuous, dense, and adherent when compared with those of N06600 and N06625. [ABSTRACT FROM AUTHOR]

In this study, the cyclic corrosion behavior of N06230, N07263, and N06625 in a LiCl-LiO molten salt was investigated at 650 °C in argon atmosphere. The cyclic corrosion behavior was observed through measurements of the oxide morphology and thickness, the extent of internal corrosion, and compositional changes in the oxide scale and the substrate. The corrosion products in the surface corrosion layers of N07263 were (Ni,Co)O, (Ni,Co)CrO, CrO, and TiO and those in the surface corrosion layers of N06230 were NiO, NiCrO, and CrO, while NiO, NiCrO, CrNbO, and CrO were identified as the corrosion products of N06625. The internal corrosion behavior of N07263 was localized, while N06230 and N06625 showed uniform corrosion. N07263 exhibited superior corrosion resistance as its corrosion layer was more continuous, dense, and adherent as compared to those of N06230 and N06625. [ABSTRACT FROM AUTHOR]