Composites of CoO/graphene nanosheets are prepared and characterized by X-ray diffraction and scanning electron microscopy. Their electrochemical behavior as anode materials of lithium-ion rechargeable batteries is investigated by galvanostatic discharge/charge measurements and cyclic voltammetry. The composite is composed of CoO nanorods (around 20-40 nm in diameter) and nanoparticles (around 10 nm in diameter) distributed within the graphene matrix. The specific capacity of the composite is higher than both CoO and graphene nanosheets. The cycling stability of CoO is obviously enhanced by compositing with graphene. After 100 cycles, the discharge and charge capacity of the composite is 1,005 and 975 mAh g, respectively, and the irreversible capacity loss is less than 3%. [ABSTRACT FROM AUTHOR]

Highlights: A freestanding MXene-derived defect-rich TiO2@reduced graphene oxides (M-TiO2@rGO) foam electrode was fabricated. M-TiO2@rGO presents fast Na+ storage kinetics due to capacitive contribution. M-TiO2@rGO foam electrode displays a capacity retention of 90.7% after 5000 cycles. Sodium ion batteries and capacitors have demonstrated their potential applications for next-generation low-cost energy storage devices. These devices's rate ability is determined by the fast sodium ion storage behavior in electrode materials. Herein, a defective TiO2@reduced graphene oxide (M-TiO2@rGO) self-supporting foam electrode is constructed via a facile MXene decomposition and graphene oxide self-assembling process. The employment of the MXene parent phase exhibits distinctive advantages, enabling defect engineering, nanoengineering, and fluorine-doped metal oxides. As a result, the M-TiO2@rGO electrode shows a pseudocapacitance-dominated hybrid sodium storage mechanism. The pseudocapacitance-dominated process leads to high capacity, remarkable rate ability, and superior cycling performance. Significantly, an M-TiO2@rGO//Na3V2(PO4)3 sodium full cell and an M-TiO2@rGO//HPAC sodium ion capacitor are fabricated to demonstrate the promising application of M-TiO2@rGO. The sodium ion battery presents a capacity of 177.1 mAh g−1 at 500 mA g−1 and capacity retention of 74% after 200 cycles. The sodium ion capacitor delivers a maximum energy density of 101.2 Wh kg−1 and a maximum power density of 10,103.7 W kg−1. At 1.0 A g−1, it displays an energy retention of 84.7% after 10,000 cycles. [ABSTRACT FROM AUTHOR]