Search

Intoduction: Limited research has explored the mechanical characteristics of recently introduced multilayered monolithic zirconia (MZC) crowns with feather-edge margins design. Moreover, most of the conventional techniques for evaluating the mechanical behavior of brittle dental ceramics rely on destructive tests, making it impossible to precisely evaluate real strength values due to premature crack initiation detection failure. Objectives: The main objective of the study was to assess the load capacity of translucent multilayered monolithic zirconia crowns with feather-edge margin thicknesses of 0.4 mm and 0.5 mm. Additionally, the research introduced a novel non-destructive acoustic emission testing (AET) technique in the laboratory to identify early cracks in dental ceramics. Methods: Forty multilayered zirconia crowns produced using computer-aided design and computer-aided manufacturing (CAD/CAM) technology were evenly divided into two groups, each with distinct feather-edge margin thicknesses: 0.5 mm (group 1) and 0.4 mm (group 2). These crowns were securely cemented onto customized polymethyl methacrylate (PMMA) dies using a universal restorative glass ionomer. Subsequently, the crowns underwent a compressive axial loading test, controlled by an innovative AET crack detection system rooted in the principles of non-destructive laboratory testing. Fractographic analysis was conducted to determine the location of crack or eventual fracture. Results: The proportion of MZCs with a crack was statistically higher than the proportion with a fracture in the whole sample (p<0.001). In addition, the results showed that the crowns in group 1 exhibited higher loading values than those in group 2. The mean loading capacity in group was 911.2 N ± 614.7 N. Two locations of crack and fracture were registered: occlusal and marginal. No statistical association was observed between the two groups for the location of cracks or fractures. Conclusions: The feather-edge crowns with a 0.5 mm margin thickness had a higher loading capacity than those with a 0.4 mm. However, the latter supports loads that exceed occlusal force in the oral cavity suggesting that 0.4 mm feathered edge MZCs may be a valid and less invasive alternative to thicker margins. The novel load-to-fracture AET setup proved effective in detecting early crack initiation, suggesting it as a promising method for assessing the mechanical properties of brittle materials prior to failure, potentially impacting the field of dentistry. However more advanced research is needed to enhance the accuracy of the proposed technique. Clinical implications: The examined MZC demonstrates the ability to withstand occlusal forces in a patient's mouth, offering clinical practitioners the option of embracing minimally invasive dentistry through the use of 0.4 mm feather-edge MZC in their treatment options. Furthermore, the positive results from the innovative acoustic emission testing technique, facilitating early crack detection, indicate a promising future for studying the behavior of brittle materials in dental laboratory testing. [ABSTRACT FROM AUTHOR]

Introduction: The purpose of this in vitro study was to test the influence of the margin design of implant supported monolithic zirconia crowns and test if monolithic zirconia crowns with extra fine finish line thickness cemented on zirconia implant abutments can bare the maximum masticatory forces on molars and hence be used in the posterior region. Methods: Fourteen identical monolithic zirconia crowns cemented on zirconia implant abutments mounted on titanium bases and fixed on implant replicas embedded in PMMA resin were divided into two groups: group I designed with a 0.5 mm CFL (CFL) and group II with a feather-edge finish line (FEFL) of 0.3 mm. All specimens underwent static load until fracture in order to determine the break force. Break forces in N were recorded for each group. Results: The CFL group exhibited slightly higher fracture resistance (1879.14 ± 322.28 N) compared to the feather-edge finish line group (1685.00 ± 362.18 N). However, statistical analysis revealed that the observed difference between the two groups (194.14 ± 183.24; p = 0.310) was not significant. Conclusions: Within the limitations of this study, both monolithic zirconia crowns with 0.5 mm chamfer and 0.3 mm feather edge margins cemented on zirconia implant abutments can be used in the posterior region as their resistance to fracture is similar and surpasses the maximum masticatory force applied on molars. [ABSTRACT FROM AUTHOR]

Copyright of International Arab Journal of Dentistry is the property of Saint Joseph University, Faculty of Dental Medicine and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Botulinum toxin type A (BTA) injections in masticatory muscles are used to treat numerous clinical conditions. This neurotoxin causes atrophy and transient paralysis of the concerned muscles. The aim of this review is to gather and define the effects of BTA injections in masticatory muscles on the underlying cartilage and bone structures. Electronic search of Medline and Google scholar databases covering the period between January 2007 and July 2019 was carried out. Eligible articles were selected according to the inclusion/exclusion criteria. Fourteen articles were included. BTA injections may cause short term reduction of cortical bone thickness and trabeculation. On the long term, cartilage volume reduction and bone volume loss were evident on the condyle and mandibular angle, at both injected and non-injected mandibular bone structures. Bone mineral density remained unaffected when only one masticatory muscle was injected but was reduced when several masticatory muscles were treated with BTA. Several cellular and molecular alterations were noticed in some articles. Because of evidence of irreversible negative effects of BTA on the underlying structures, possible muscle, bone and cartilage volume reduction should be communicated to the patients prior to any intervention. Further studies are needed to fully understand the cellular mechanisms and molecular responses behind this phenomenon. [ABSTRACT FROM AUTHOR]

Tissue engineering is an alternative to traditional strategies to repair and regenerate temporomandibular joints (TMJ). Nowadays, patients suffering from severe dysfunctions of the TMJ may undergo discectomy, a procedure that consists of removing the damaged disc in hopes of reducing the symptoms. However, tissue engineering presents a potential solution for patients suffering from these disorders, due to the lack of safety and effectiveness of TMJ disc implants. Since 1991, several studies have investigated the possibility of regenerating the articular disc. This literature review aims to expose the new challenges and techniques in TMJ disc tissue engineering whether it concerns cell sourcing, scaffold or bioreactors. As these challenges are overcome, the goal of future studies remains to create a functional biological replacement of the TMJ components. [ABSTRACT FROM AUTHOR]