The immediate bonding effectiveness of contemporary adhesives is quite favorable, regardless of the approach used. In the long term, the bonding effectiveness of some adhesives drops dramatically, whereas the bond strengths of other adhesives are more stable. This review examines the fundamental processes that cause the adhesion of biomaterials to enamel and dentin to degrade with time. Non-carious class V clinical trials remain the ultimate test method for the assessment of bonding effectiveness, but in addition to being high-cost, they are time- and labor-consuming, and they provide little information on the true cause of clinical failure. Therefore, several laboratory protocols were developed to predict bond durability. This paper critically appraises methodologies that focus on chemical degradation patterns of hydrolysis and elution of interface components, as well as mechanically oriented test set-ups, such as fatigue and fracture toughness measurements. A correlation of in vitro and in vivo data revealed that, currently, the most validated method to assess adhesion durability involves aging of micro-specimens of biomaterials bonded to either enamel or dentin. After about 3 months, all classes of adhesives exhibited mechanical and morphological evidence of degradation that resembles in vivo aging effects. A comparison of contemporary adhesives revealed that the three-step etch-and-rinse adhesives remain the 'gold standard' in terms of durability. Any kind of simplification in the clinical application procedure results in loss of bonding effectiveness. Only the two-step self-etch adhesives approach the gold standard and do have some additional clinical benefits. [ABSTRACT FROM AUTHOR]

The recently developed hybrid restorative materials contain the essential components of conventional glass ionomers and light-cured resins. The objective of this study was to determine several physical and mechanical properties of eight such materials in comparison with two conventional glass ionomers, one micro-filled, and one ultrafine compact-filled resin composite. The two resin composites and two of the three polyacid-modified resin composites could be polished to a higher gloss than the conventional as well as the resin-modified glass ionomers. After abrasion, surface roughness increased for all materials, but not at the same extent, being the least for the conventional resin composites and one polyacid-modified resin composite, Dyract. In contrast to the latter resin composites, of which the surface roughness is principally determined by the presence of protruding filler particles above the resin matrix, roughness of conventional and resin-modified glass ionomers results from both protruding filler particles and intruding porosities. The mean particle size of the hybrid restorative materials fell between the smaller mean particle size of the resin composites and the larger one of the conventional glass ionomers. The micro-hardness and Young's modulus values varied substantially among all eight hybrid restorative materials. For all the resin-modified glass-ionomer restorative materials, the Young's modulus reached a maximum value one month after mixing and remained relatively stable thereafter. The Young's modulus of the conventional and the polyacid-modified resin composites decreased slightly after one month. The conventional glass-ionomer materials undoubtedly set the slowest, since their Young's modulus took six months to reach its maximum. The flexural fatigue limit of the hybrid restorative materials is comparable with that of the micro-filled composite. From this investigation, it can be concluded that the physico-mechanical properties vary widely among the eight hybrid restorative materials, indicating that these materials probably have yet to achieve their optimum properties. Their mechanical strength is inadequate for use in stress-bearing areas, and their appearance keeps them from use where esthetics is a primary concern. [ABSTRACT FROM AUTHOR]

Laboratory testing of dentin adhesive systems still requires corroboration by long-term clinical trials for their ultimate clinical effectiveness to be validated. The objective of this clinical investigation was to evaluate, retrospectively, the clinical effectiveness of earlier-investigated dentin adhesive systems (Scotchbond, Gluma, Clearfil New Bond, Scotchbond 2, Tenure, and Tripton), and to compare their clinical results with those obtained with four modern total-etch adhesive systems (Bayer exp. 1 and 2, Clearfil Liner Bond System, and Scotchbond Multi-Purpose). In total, 1177 Class V cervical lesions in the teeth of 346 patients were restored following two cavity designs: In Group A, enamel was neither beveled nor intentionally etched, as per ADA guidelines; in Group B, adjacent enamel was beveled and conditioned. Clinical retention rates definitely indicated the improved clinical efficacy of the newest dentin adhesives over the earlier systems. With regard to adhesion strategy, adhesive systems that removed the smear layer and concurrently demineralized the dentin surface layer performed clinically better than systems that modified the disorderly layer of smear debris without complete removal. Hybridization by resin interdiffusion into the exposed dentinal collagen layer, combined with attachment of resin tags into the opened dentin tubules, appeared to be essential for reliable dentin bonding but might be insufficient by itself. The additional formation of an elastic bonding area as a polymerization shrinkage absorber and the use of a microfine restorative composite apparently guaranteed an efficient clinical result. The perfect one-year retention recorded for Clearfil Liner Bond System and Scotchbond Multi-Purpose must be confirmed at later recalls. [ABSTRACT FROM AUTHOR]

The hardness and Young's modulus of the successive layers across a resin-dentin bonding area were determined by nano-indentation for four commercially-available dentin adhesive systems, of which two were also applied with a different conditioning agent. With a computer-controlled nano-indentation technique, minute triangular indentations were made within a small area of a few micrometers' diameter at a load of a few milli-Newtons. The load and displacement of the indenter were continuously monitored during the loading-unloading sequence, so hardness and Young's modulus could be computed as a function of the indenter geometry and the applied load. The hardness of the resin-dentin interdiffusion zone was significantly lower than that of unaltered dentin. A gradient of moduli of elasticity was observed from the rather stiff dentin over a more elastic resin-dentin inter-diffusion zone and adhesive resin layer to the restorative composite. That gradient was more substantial in those systems that produced relatively thick adhesive resin layers or supplementally provided a filled low-viscosity resin as an intermediate layer between the adhesive resin and the bulk restorative composite. Such an elastic bonding area might have a strain capacity sufficient to relieve stresses between the shrinking composite restoration and the rigid dentin substrate, thereby improving the conservation of the dentin bond and, as a consequence, the marginal integrity and retention of the restoration. [ABSTRACT FROM AUTHOR]

The chemical nature of the interface between dentin and adhesive resin materials was characterized by micro-Raman spectroscopy. The resulting chemical profiles were correlated with photomicrographs obtained by SEM after an argon-ion-beam etching treatment of the sample surface. Two commercially available dentin adhesive systems, of which one was also applied with a different conditioning agent, were investigated. Raman spectra, which were recorded along line scans across the interface with a step increment of 1 µm, revealed that resin effectively penetrated 4 to 6 µm deep into the superficially decalcified dentin zone. Across the interface, a gradual transition from resin to dentin over the interdiffusion zone with a mixed contribution of both substances was noticed. Finally, resin appeared to penetrate to the entire decalcification depth of dentin regardless of the aggressiveness of the conditioning procedure. [ABSTRACT FROM AUTHOR]

The resin-dentin interdiffusion zone produced by a den-tin-adhesive system that removes the smear layer and concurrently decalcifies superficial dentin was morphologically examined by both scanning and transmission electron microscopy. Cross-sectioned resin-bonded dentin discs were etched with an argon-ion beam to make the resin-dentin interface observable by SEM. For the TEM examination, the sections were partly decalcified by an aqueous EDTA solution to facilitate ultramicrotomy and to disclose the ultrastructure of the interdiffusion zone. Both SEM and TEM confirmed the presence of the resin-dentin interdiffusion zone as the junction between the deep unaltered dentin structure and the restorative resin. Within the interdiffusion zone, three sublayers with characteristic ultrastructure and staining were identified by TEM. An upper diffuse black layer contained few structural features. Underneath, partially-altered collagen flbrils were closely packed, mostly running parallel with the interface and perpendicular to the dentinal tubules. Their outline was electron-dense, forming tunnel-like structures. At the base of the upper layer, several stained projections were found to bulge out into the underlying collagen network and appeared to be confined by obstructive, parallel-running collagen flbrils. Finally, the third dense layer, containing hydroxyapatite crystals, demarcated the superficially demineralized dentin layer from the deeper unaltered dentin. Resin diffusion into the decalcified dentin surface layer was evident, but diminished with depth, presumably reducing deeper resin impregnation into the interfibrillar spaces. The citric acid dentin-pretreatment probably caused denaturation of the superficial collagen fibrils. Its decalcifying effect gradually weakened with depth, leaving behind hydroxyapatite crystals at the base of the interdiffusion zone. These crystals appeared to have been resistant to the EDTA TEM-sample decalcification procedure, which suggests that they were protected by resin encapsulation. [ABSTRACT FROM AUTHOR]

Cross-sections of resin-dentin interfaces were etched with an argon-ion beam to make their substructure detectable by scanning electron microscopy. The dentin adhesive systems were categorized morphologically into three groups, and an attempt was made to clarify their adhesive mechanism. The first group of products removed the smear layer. The argon-ion bombardment clearly disclosed a hybrid or resin-impregnated dentin layer. It is hypothesized that conditioning with acidic or chelating agents demineralized the dentin surface-layer to a certain depth, leaving behind a collagen-rich mesh-work. Hydrophilic monomers are then believed to alter this collagen-fiber arrangement in a way that facilitates penetration of the adhesive resin, resulting in a mechanical, intermingled link between collagen and the adhesive resin. The second group preserved the smear layer. In this case, the dentinal tubules were obliterated with globular particles at their orifices and remained patent underneath these smear plugs. This type of adhesive system aims at the incorporation of the smear layer into the hydrophilic monomers, which have an affinity for the organic and/or inorganic components of the underlying dentin. Finally, a third, small group only partly dissolved the smear layer, creating a thin resin-impregnated dentin layer and a resin-impregnated smear plug. This study clearly showed that the application of recent adhesive systems induced structural changes in the dentin surface morphology, creating a retentive interface, called the inter-diffusion zone, between the deep, untouched dentin layers and the composite filling material. This resin-dentin inter-diffusion zone offers bonding sites for copolymerization with the resin composite and, concurrently, might have protective potential for the pulp tissues. [ABSTRACT FROM AUTHOR]

The purpose of this study was to determine the surface roughness of enamel-to-enamel contact areas in order to provide a standard for comparison with surface characteristics of commercially available composite restorative materials. In addition, the inherent surface roughness of resin composites was evaluated profilometrically after a toothbrush abrasion procedure. A one-sided t-test analysis was performed to outline significant differences between the surface roughness value of enamel facets and that of the respective composite samples. A surface roughness of 0.64 ± 0.25 µm (mean ± S.D.) was found for the enamel-to-enamel contact areas. [ABSTRACT FROM AUTHOR]

Changes in the dynamic Young's modulus under flexure of self-cured and light-cured composite resins during setting were demonstrated to reflect accurately the condition of the curing composite resins. The rate of stiffness increase during setting varied considerably with the product, and the light-cured composite resins generally showed a faster rate of increase of stiffness. In the initial stage, the Young's moduli were very low, especially for the self-cured composite resins. This accounts for the damage (adhesion disruption and cross-linking interruption) that can be inflicted on a freshly placed composite resin filling that is not yet mechanically stabilized. Therefore, such fillings are vulnerable to aggressive distortion for at least 10 to 15 minutes after placement. [ABSTRACT FROM AUTHOR]

Comparisons were made of the Young's moduli obtained with tests that impose static, low-frequency, or high-frequency elastic deformations on dental composite systems. The frequency of the imposed stress was reflected in the absolute value of Young's modulus. However, the values obtained at different test frequencies could be compared and understood by taking into account this frequency dependence. It was thus found that the composite structure largely determined the type of reaction to the imposed stress. The fundamental period test permitted the greatest differentiation in the elastic behavior of the investigated composites. [ABSTRACT FROM AUTHOR]

The non-destructive determination of Young's modulus of dental composites by means of the fundamental period was found to be reliable and accurate. Post-polymerization effects could clearly be detected. Exponential regression analysis showed a correlation coefficient of 0.92, after logarithmic transformation, with volumetric filler content. The high accuracy and reliability of the measurements themselves are reflected in low standard deviations. The results are in excellent agreement with those of other investigations. Furthermore, the ease and speed of operation make this new procedure a powerful laboratory tool for material-testing and practical large-scale investigations. [ABSTRACT FROM AUTHOR]

In this study, the attrition wear, also called occlusal-contact-area wear, of human enamel was measured quantitatively with a computerized three-dimensional measuring technique over a period of four years. Tooth replicas from a clinical trial were used. A running-in wear period after restorative treatment, followed by steady-state wear, was suggested. The average steady-wear rate on occlusal contact areas was about 29 pm per year for molars and about 15 pm per year for premolars. [ABSTRACT FROM AUTHOR]