A composite of 70/30 poly(lactic acid)/hydroxyapatite was systematically prepared using various amounts of glycidyl methacrylate as reactive compatibilizer or Joncryl ADR®-4368 containing nine glycidyl methacrylate functions as a chain extension/branching agent to improve the mechanical and biological properties for suitable usage as internal bone fixation devices. The effect of glycidyl methacrylate/Joncryl on mechanical properties of poly(lactic acid)/hydroxyapatite was investigated through flexural strength. Cell proliferation and differentiation of osteoblast-like MC3T3-E1 cells cultured on the composite samples were determined by Alamar Blue assay and alkaline phosphatase expression, respectively. Result shows that flexural strength tends to decrease, as glycidyl methacrylate content increases except for 1 wt.% glycidyl methacrylate. With an addition of dicumyl peroxide, the flexural strength shows an improvement than that of without dicumyl peroxide probably due to the chemical bonding of the hydroxyapatite and poly(lactic acid) as revealed by FTIR and NMR, whereas the composite with 5 wt.% Joncryl shows the best result, as the flexural strength increases getting close to pure poly(lactic acid). The significant morphology change could be seen in composite with Joncryl where the uniform agglomeration of hydroxyapatite particles oriented in poly(lactic acid) matrix. Addition of the epoxy functional compatibilizers at suitable percentages could also have benefits to cellular attachment, proliferation, differentiation and mineralization. So that, this poly(lactic acid)/hydroxyapatite composite could be a promising material to be used as internal bone fixation devices such as screws, pins and plates.

Hydroxyl-capped polylactic acid (PLA) oligomers are prepared by glycolysis reaction of PLA with ethylene glycol (EG) and used as a macromolecular cross-linker for epoxidized natural rubber (ENR). The glycolyzed PLA (GPLA) with three different molecular weights (2000, 10,000, and 44,000 g mol−1) are prepared by varying the glycolysis conditions. Effects of GPLA chain lengths and GPLA/ENR feed ratios on cross-linking efficiency, chemical structures, and physical properties of the cured products are investigated. The cross-linking efficiency is examined using a moving die rheometer, solvent fractionation, thermogravimetric analysis, and Fourier transform infrared spectroscopy. Optimum GPLA/ENR compositions for the curing reaction range from 20 wt% to 33 wt%, depending on the GPLA chain length. Because of their biodegradability, biocompatibility, and the ability to tune up their structures and properties, the cured rubber materials have high potential for use in various biomedical applications.