Search

A kind of paper-based composite was prepared with short carbon fibers (CFs) and para-aramid fibrids through the process of papermaking. The dielectric properties of the paper-based composites at microwave frequency were investigated. Based on the Lichtenecker Rule, the dielectric constants of CFs in composites at different CF concentrations were calculated. The absorbing performances of paper-based composites were calculated from the test results of electromagnetic parameters. It was shown that for the composites loaded with 1 mm CFs, the real part of complex permittivity rises at first then tends to be stable with the increase of the CF content, and the imaginary part rises at first then falls slightly, while for composites loaded with 3 or 6 mm CFs, both the real and imaginary part of complex permittivity grows at first and then falls rapidly with the CF content increasing. When the CF content is below 10 wt%, the composites containing longer CFs have larger permittivity at the same concentration. The Lichtenecker Rule is found to be not suitable for the system studied in this paper, especially when the content of CFs is high. The variations of reflectance and absorbance with the content of CFs generally have analogous trends . It is also found that to achieve better absorbing performance, the length and content of CFs together with the thickness of composites should be considered. In this study, the lowest reflection loss at 10 GHz reaches –27.59 dB when the paper-based composite is loaded with 1 mm CFs at the concentration of 10 wt% and the optimum thickness of 1.84 mm. [ABSTRACT FROM AUTHOR]

The influence of temperature and relative humidity on the moisture content of paper honeycomb sandwich panels was studied, and the ideal three-dimensional diagram between the moisture content of paper honeycomb sandwich panels and the temperature and relative humidity was constructed by the GAB model. The evaluation equation of critical stress and plateau stress were obtained. The results indicate that the moisture content of paper honeycomb sandwich panels rises with the increase of relative humidity and declines with the increase of temperature; as the moisture content increases, the critical stress and plateau stress of paper honeycomb sandwich panels decline linearly; with the increase of the moisture content, the energy absorption of paper honeycomb sandwich panels increased firstly and then decreased; the evaluation equation of critical stress and plateau stress can predict the mechanical properties of paper honeycomb sandwich panels in different temperatures and relative humidities. [ABSTRACT FROM AUTHOR]

Novel sandwich composites made of syntactic foam core and paper skin were developed as potential building materials. Interface bonding between core and skin was controlled by varying starch content. Two different microsphere size groups were employed for syntactic foam core manufacturing based on the pre-mold processing method. Properties of skin paper with starch adhesive on were found to be affected by drying time of starch adhesive. Mechanical behavior of manufactured sandwich composites in relation with properties of constituent materials was studied. Skin paper contributed to increase up to 40% in estimated flexural strength over syntactic foams, depending on starch content in adhesive between syntactic foam core and paper skin. Small microsphere size group for syntactic foam core was found to be advantageous in strengthening of sandwich composites for a given starch content in adhesive. This finding was in agreement with calculated values of estimated shear stress at interface between skin and core. Failure process of the sandwich composites was discussed in relation with load–deflection curves. Cracking of syntactic foam core was detected to be the first event in sandwich composite failure sequence. Hygroscopic behavior of syntactic foam panels was investigated. Moisture content in the foam was measured to be high for high starch content in the foam panels. No significant moisture effect on flexural strength of syntactic foam panels after being subjected to moisture about 2 months was found for both microsphere size groups. However, substantial decrease (28%) in flexural modulus was found for the foam panels made of large microspheres although not much moisture effect was found on that of small microspheres. [ABSTRACT FROM PUBLISHER]

The effects of partial or complete replacement of two commercial fillers, carbon black (CB) and silica on cure characteristics, tensile properties, fatigue life, morphological properties, and rubber-filler interaction of paper sludge (PS) filled natural rubber composites were elucidated. Compounding was carried out on a two-roll mill with total filler loading of 30 phr. Results indicate that maximum torque, tensile strength, elongation at break, tensile modulus, and fatigue life increased the cure time while the scorch time decrease with increasing carbon black loading ratio of PS/CB filled natural rubber composites. On the other hand, increased loading of silica in PS/silica weight ratio resulted in an increment in cure time, scorch time, maximum torque, elongation at break, and fatigue life but not significantly altering tensile strength and tensile modulus of the natural rubber composites. In addition, PS/silica filled natural rubber composites exhibit lower maximum torque, tensile properties, and fatigue life compared to the PS/CB filled natural rubber composites. Rubber-filler interaction and SEM micrograph studies proved that the higher interaction between carbon black and natural rubber occurred in PS/CB filled natural rubber composites rather than PS/silica filled natural rubber composites. [ABSTRACT FROM AUTHOR]