Search

The new, quaternary diamond-like semiconductor (DLS) Cu4MnGe2S7 was prepared at high-temperature from a stoichiometric reaction of the elements under vacuum. Single crystal X-ray diffraction data were used to solve and refine the structure in the polar space group Cc. Cu4MnGe2S7 features [Ge2S7]6- units and adopts the Cu5Si2S7 structure type that can be considered a derivative of the hexagonal diamond structure. The DLS Cu2MnGeS4 with the wurtz-stannite structure was similarly prepared at a lower temperature. The achievement of relatively phase-pure samples, confirmed by X-ray powder diffraction data, was nontrival as differential thermal analysis shows an incongruent melting behaviour for both compounds at relatively high temperature. The dark red Cu2MnGeS4 and Cu4MnGe2S7 compounds exhibit direct optical bandgaps of 2.21 and 1.98 eV, respectively. The infrared (IR) spectra indicate potentially wide windows of optical transparency up to 25 μm for both materials. Using the Kurtz-Perry powder method, the second-order nonlinear optical susceptibility, χ(2), values for Cu2MnGeS4 and Cu4MnGe2S7 were estimated to be 16.9 ± 2.0 pm V-1 and 2.33 ± 0.86 pm V-1, respectively, by comparing with an optical-quality standard reference material, AgGaSe2 (AGSe). Cu2MnGeS4 was found to be phase matchable at λ = 3100 nm, whereas Cu4MnGe2S7 was determined to be non-phase matchable at λ = 1600 nm. The weak SHG response of Cu4MnGe2S7 precluded phase-matching studies at longer wavelengths. The laser-induced damage threshold (LIDT) for Cu2MnGeS4 was estimated to be ∼0.1 GW cm-2 at λ = 1064 nm (pulse width: τ = 30 ps), while the LIDT for Cu4MnGe2S7 could not be ascertained due to its weak response. The significant variance in NLO properties can be reasoned using the results from electronic structure calculations.

Two new biaxial, diamond-like semiconductors, Li2CdGeSe4 and Li2CdSnSe4, were prepared via high-temperature, solid-state synthesis. Single crystal X-ray diffraction and X-ray powder diffraction coupled with Rietveld refinement were used to refine the crystal structures and assess the phase purity, respectively. Both compounds adopt the lithium cobalt(II) silicate structure type. Strong second-order nonlinear optical (NLO) susceptibility, phase matchability, relatively high thermal stability, and excellent transparency deem both materials potential infrared (IR) NLO candidates. Li2CdGeSe4 and Li2CdSnSe4 display optical bandgaps of approximately 2.5 and 2.2 eV, respectively. Li2CdSnSe4 exhibits a strong, red-light emission under 1064 nm excitation, allowing the compound to release energy that accumulates by two-photon absorption under Nd:YAG laser radiation. Therefore, Li2CdSnSe4 shows a high laser-induced damage threshold (LIDT) of 0.7 GW cm−2. This special phenomenon is remarkable and may open a new avenue in searching for promising IR NLO materials with large LIDTs.

Several compositions of the Cu3NbS4−xSex (x = 0, 0.1, 0.2, 0.4, 0.6, 0.8, and 4) series were synthesized through combination of the elements using conventional solid-state reactions. X-ray powder diffraction patterns suggest that the synthesized polycrystalline powder samples are isostructural to sulvanite (Cu3VS4). However, plotting the refined lattice parameters as well as the measured “true” density as a function of Se content (x) showed deviations from linearity, suggesting that the Cu3NbS4−xSex series is not a “true” solid solution. Differential scanning calorimetry data showed that all compounds incongruently melt at ∼1100 K and recrystallize with a minor impurity phase. Optical diffuse reflectance UV/Vis/NIR spectroscopy revealed a nearly linear contraction of the optical band gap with increasing Se content. The direct band gap decreases from 2.53 eV for x = 0.1 to 2.43 eV for x = 0.8. Electronic transport data indicate p-type semiconducting behavior for all samples. Thermal conductivity data showed a rather surprising trend, with the substituted compositions exhibiting higher thermal conductivity than the two end members.