Search

All-inorganic lead perovskite quantum dots (QDs), due to their distinctive optical properties, have become one of the “hottest” topics in materials science; therefore, the development of new QD synthesis methods or their emission color adjustment is of great interest. Within this study, we present the simple preparation of QDs employing a novel ultrasound-induced hot-injection method, which significantly reduces the QD synthesis time from several hours to merely 15-20 minutes. Moreover, the post-synthesis treatment of perovskite QDs in solutions using zinc halogenide complexes could increase the QD emission intensity and, at the same time, boost their quantum efficiency. This behavior is due to the zinc halogenide complex's ability to remove or significantly reduce the number of surface electron traps in perovskite QDs. Finally, the experiment that shows the ability to instantly adjust the desired emission color of perovskite QDs by variation of the amount of added zinc halogenide complex is presented. The instantly obtained perovskite QD colors cover virtually the full range of the visible spectrum. The zinc halogenide modified perovskite QDs exhibit up to 10-15% higher QEs than those prepared by an individual synthesis.

Fabrication of a true-3D inorganic ceramic with resolution down to the nanoscale (∼100 nm) using a sol–gel resist precursor is demonstrated. This method has an unrestricted free-form capability, control of the fill-factor, and high fabrication throughput. A systematic study of the proposed approach based on ultrafast laser 3D lithography of organic–inorganic hybrid sol–gel resin followed by a heat treatment enabled the formation of inorganic amorphous and crystalline composites guided by the composition of the initial resin. The achieved resolution of 100 nm was obtained for 3D patterns of complex free-form architectures. Fabrication throughput of 50 × 103 voxels per second is achieved; voxel – a single volume element recorded by a single pulse exposure. A post-exposure thermal treatment was used to form a ceramic phase, the composition and structure of which were dependent on the temperature and duration of the heat treatment as revealed by Raman micro-spectroscopy. The X-ray diffraction (XRD) showed a gradual emergence of the crystalline phases at higher temperatures with a signature of cristobalite SiO2, a high-temperature polymorph. Also, a tetragonal ZrO2 phase known for its high fracture strength was observed. This 3D nano-sintering technique is scalable from nanoscale to millimeter dimensions and opens a conceptually novel route for optical 3D nano-printing of various crystalline inorganic materials defined by an initial composition for diverse applications for microdevices designed to function in harsh physical and chemical environments and at high temperatures.

A novel and simple method for CeO2 nanoscale particle synthesis in aqueous solutions via a photochemical route is reported in this paper. To this end, CeCl3·7H2O or Ce(NO3)3·6H2O was used as a Ce precursor, while NaN3 was chosen as the photoactive compound. Synthesis was carried out without any surfactants or by using polyvinylpyrrolidone (PVP). The synthesized samples were subsequently thermally treated at different temperatures between 100 and 900 °C. XRD patterns and Raman spectra indicated that CeO2 samples possess the fluorite structure. TEM analysis revealed that synthesis without surfactants leads to formation of highly agglomerated particles, while adding PVP to the primary solution resulted in decreased agglomeration and reduced particle size. The particle size was calculated from XRD and Raman line broadening and confirmed by TEM analysis. The average crystallite size for the unheated samples prepared without surfactant was hardly radiation exposure dependent and varied from 6.5 to 8.9 nm. Even smaller particles (3.3–7.0 nm) were formed by using PVP. It turned out that an increase of the calcination temperature causes significant crystallite growth. A strong interaction between CeO2 nanoparticles and PVP was revealed by TG analysis. The UV/VIS absorption spectra showed a strong absorption below 400 nm (3.10 eV) with a well-defined absorption peak at around 295–320 nm. The estimated band gap (Eg) of the obtained nanoscale particles was in the range of 2.90–3.57 eV, i.e. the values are higher than that of a bulk CeO2 powder (Eg = 3.19 eV), except for the sample calcined at 900 °C.

A series of polycrystalline Li3Ba2La3−xEux(MoO4)8 samples were prepared by the conventional solid-state reaction. The phase formation of the samples was investigated by X-ray diffraction measurements. The luminescence spectra and decay curves were studied as a function of Eu3+ concentration and temperature. It turned out that the optical band gap of the undoped molybdates is at 3.65 eV. The quantum efficiency (QE) of the Eu3+ doped luminescent materials increases with increasing Eu3+ concentration and almost 100% QE was obtained for those samples doped with 70, 80, or 90% Eu3+. A sample containing 100% Eu3+ showed solely a slight decrease in quantum efficiency. The luminous efficacy (LE) was 330 and 312 lm Wopt−1 for the 10 and 100% Eu3+ doped samples, respectively. The decrease of LE values is caused by a slight shift of the colour point to the red spectral range with increasing Eu3+ content. Temperature dependent measurements revealed that Li3Ba2Eu3(MoO4)8 loses only 15% of efficiency up to 400 K, which demonstrates that the investigated phosphors are attractive for application in pcLEDs.