The paper presents the results of preliminary research on the use of silica sands with hydrated sodium silicate 1.5% wt. of binder for the performance of eco-friendly casting cores in hot-box technology. To evaluate the feasibility of high quality casting cores performed by the use of this method, the tests were made with the use of a semiautomatic core shooter using the following operating parameters: initial shooting pressure of 6 bar, shot time 4 s and 2 s, core-box temperature 200, 250 and 300 °C and core heating time 30, 60, 90 and 150 s. Matrixes of the moulding sands were two types of high-silica sand: fine and medium. Moulding sand binder was a commercial, unmodified hydrated sodium silicate having a molar module SiO2 / Na2O of 2.5. In one shot of a core-shooter were made three longitudinal samples (cores) with a total volume of about 2.8 dm3. The samples thus obtained were subjected to an assessment of the effect of shooting parameters, i.e. shooting time, temperature and heating time, using the criteria: core-box fill rate, bending strength (RgU), apparent density and surface quality after hardening. The results of the trials on the use of sodium silicate moluding sands made it possible to further refine the conditions of next research into the improvement of inorganic warm-box / hot-box technology aimed at: reduction of heating temperature and shot time. It was found that the performance of the cores depends on the efficiency of the venting system, shooting time, filling level of a shooting chamber and grains of the silica matrix used.

The paper presents results of initial research on the possibility of applying microwave radiation in an innovative process of making casting moulds from silica sand, where gypsum CaSO4∙2H2O was acting as a binding material. In the research were compared strengths and technological properties of moulding mixture subjected to: natural bonding process at ambient temperature or natural curing with additional microwave drying or heating with the use of microwaves immediately after samples were formed. Used in the research moulding sands, in which dry constituents i.e. sand matrix and gypsum were mixed in the ratio: 89/11. On the basis of the results of strength tests which were obtained by various curing methods, beneficial effect of using microwaves at 2.45 GHz for drying up was observed after 1, 2 and 5 hours since moisture sandmix was formed. Applying the microwaves for hardening just after forming the samples guarantees satisfactory results in the obtained mechanical parameters. In addition, it has been noted that, from a technological and economic point of view, drying the silica sand with gypsum binder in microwave field can be an alternative to traditional molding sand technologies.

Moulding sands containing sodium silicate (water-glass) belong to the group of porous mixture with low resistance to increased humidity. Thanks to hydrophilic properties of hardened or even overheated binder, possible is application of effective methods of hydrous reclamation consisting in its secondary hydration. For the same reason (hydrophilia of the binder), moulds and foundry cores made of high-silica moulding sands with sodium silicate are susceptible to the action of components of atmospheric air, including the contained steam. This paper presents results of a research on the effect of (relative) humidity on mechanical and technological properties of microwave-hardened moulding mixtures. Specimens of the moulding sand containing 1.5 wt% of sodium water-glass with module 2.5 were subjected, in a laboratory climatic chamber, to long-term action of steam contained in the chamber atmosphere. Concentration of water in atmospheric air was stabilized for 28 days (672 h) according to the relative humidity parameter that was ca. 40%, 60% and 80% at constant temperature 20 °C. In three cycles of the examinations, the specimens were taken out from the chamber every 7 days (168 h) and their mechanical and technological parameters were determined. It was found on the grounds of laboratory measurements that moulds and cores hardened with microwaves are susceptible to action of atmospheric air and presence of water (as steam) intensifies action of the air components on glassy film of sodium silicate. Microwave-hardened moulding sands containing sodium silicate may be stored on a long-term basis in strictly determined atmospheric conditions only, at reduced humidity. In spite of a negative effect of steam contained in the air, the examined moulding mixtures maintain a part of their mechanical and technological properties, so the moulds and foundry cores stored in specified, controlled conditions could be still used in manufacture.

In this paper, the effect of changes the parameters of heat treatment on the structure and the degree of elements segregation was determined, in the context of corrosion resistance of ductile iron Ni-Mn-Cu, containing 7.2% Ni, 2.6% Mn and 2.4% Cu. In the condition after casting, castings of austenitic matrix and 160HBW hardness were obtained. The achieved castings were soaked at 450, 550 and 650°C for 4, 8 and 12 hours, then cooled down at the ambient air. In most cases, the heat treatment resulted in a change in the castings matrix, had the consequence of increasing their hardness in comparison to raw castings. Increasing the temperature and prolonging soaking time resulted in increasing the degree of transformation of austenite, while reducing the degree of elements segregation. This led to the formation of slightly bigger number of pitting due to corrosion, but not so deep and more evenly distributed in comparison to raw castings. Wherein the results of corrosion tests show that heat treatment of castings did not significantly change their corrosion resistance in comparison to raw castings, in contrast to the significant increase in mechanical properties.

In the paper, a research on effects of baking temperature on chromite sand base of moulding sands bonded with sodium silicate is presented. Pure chromite sand and its chromite-based moulding sand prepared with use of sodium silicate were subjected to heating within 100 to 1200 °C. After cooling-down, changes of base grains under thermal action were determined. Chromite moulding sand was prepared with use of 0.5 wt% of domestic made, unmodified sodium silicate (water-glass) grade 145. After baking at elevated temperatures, creation of rough layer was observed on grain surfaces, of both pure chromite sand and that used as base of a moulding sand. Changes of sand grains were evaluated by scanning microscopy and EDS analyses. It was found that changes on grain surfaces are of laminar nature. The observed layer is composed of iron oxide (II) that is one of main structural components of chromite sand. In order to identify changes in internal structure of chromite sand grains, polished sections were prepared of moulding sand hardened with microwaves and baked at elevated temperatures. Microscopic observations revealed changes in grains structure in form of characteristically crystallised acicular particles with limited magnesium content, intersecting at various angles. EDS analysis showed that these particles are composed mostly of chromium oxide (III) and iron oxide (II). The temperature above that the a.m. changes are observed in both chromite-based moulding sand and in pure chromite sand. The observed phenomena were linked with hardness values and mass of this sand.

The paper presents a research on the relation between thermal preparation of chromite sand base of moulding sands containing sodium silicate, hardened with selected physical and chemical methods, and structure of the created bonding bridges. Test specimens were prepared of chromite sand - fresh or baked at 950°C for 10 or 24 hours - mixed with 0.5 wt.% of the selected non-modified inorganic binder and, after forming, were hardened with CO2 or liquid esters, dried traditionally or heated with microwaves at 2.45 GHz. It was shown on the grounds of SEM observations that the time of baking the base sand and the hardening method significantly affect structure of the bonding bridges and are correlated with mechanical properties of the moulding sands. It was found that hardening chromite-based moulding mixtures with physical methods is much more favourable than hardening with chemical methods, guaranteeing also more than ten times higher mechanical properties.

The paper presents a research on the effect of extreme - for the technology of the considered silumin EN AB 47100 - parameters of high-pressure die casting on occurrence of casting nonconformities. Considered was influence of the way of assembling the mould cooled-down to 140-160°C, non-standard for the selected casting, and pouring temperature in the range of 705 to 720°C (higher than the recommended) of non-refined alloy. The castings were prepared with use of a high-pressure casting machine made by Kirov with mould closing force of 2500 kN. Occurrence of nonconformities was evaluated on properly prepared specimens taken from the castings manufactured with various parameters of the injection piston and various multiplication pressures. The results were subjected to quantitative and qualitative analyses of casting nonconformities and distribution of major alloying elements. It was found that proper selection of working parameters of the casting machine, in spite of disadvantageous pouring conditions, makes it possible to reduce occurrence of some casting defects, like shrinkage cavities and porosity, to improve tightness of castings even when the alloy refining process is omitted.

In the paper, a research on effects of baking temperature on chromite sand base of moulding sands bonded with sodium silicate is presented. Pure chromite sand and its chromite-based moulding sand prepared with use of sodium silicate were subjected to heating within 100 to 1200 °C. After cooling-down, changes of base grains under thermal action were determined. Chromite moulding sand was prepared with use of 0.5 wt% of domestic made, unmodified sodium silicate (water-glass) grade 145. After baking at elevated temperatures, creation of rough layer was observed on grain surfaces, of both pure chromite sand and that used as base of a moulding sand. Changes of sand grains were evaluated by scanning microscopy and EDS analyses. It was found that changes on grain surfaces are of laminar nature. The observed layer is composed of iron oxide (II) that is one of main structural components of chromite sand. In order to identify changes in internal structure of chromite sand grains, polished sections were prepared of moulding sand hardened with microwaves and baked at elevated temperatures. Microscopic observations revealed changes in grains structure in form of characteristically crystallised acicular particles with limited magnesium content, intersecting at various angles. EDS analysis showed that these particles are composed mostly of chromium oxide (III) and iron oxide (II). The temperature above that the a.m. changes are observed in both chromite-based moulding sand and in pure chromite sand. The observed phenomena were linked with hardness values and mass of this sand.

In the paper, presented is a research on effectiveness of absorbing electromagnetic waves at frequency 2.45 GHz by unhardened moulding sands prepared of three kinds of high-silica base and a selected grade of sodium silicate. Measurements of power loss of microwave radiation (Pin) expressed by a total of absorbed power (Pabs), output power (Pout) and reflected power (Pref) were carried-out on a stand of semiautomatic microwave slot line. Values of microwave power loss in the rectangular waveguide filled with unhardened moulding sands served for determining effectiveness of microwave heating. Balance of microwave power loss is of technological and economical importance for manufacture of high-quality casting moulds and cores of various shapes and sizes. It was found that relative density influences parameters of power output and power reflected from samples of moulding sand placed in a waveguide. Absorption expressed by the parameter Pabs is not related to granularity of high-silica base: fine, medium and coarse. It was found that the semiautomatic microwave slot line supports evaluation of effectiveness of microwave absorption on the grounds of power loss measurements and enables statistic description of influence of relative density of the sandmix on penetration of electromagnetic waves in unhardened moulding sands.

In the paper, an attempt was made to evaluate the effect of preliminary wetting of high-silica base during preparation of moulding sands containing a selected grade of sodium water-glass, designed for hardening by traditional drying or by electromagnetic microwaves at 2.45 GHz. In the research, some water was dosed during stirring the sandmix before adding 1.5 wt% of the binder that was unmodified sodium water-glass grade 137, characterised by high molar module within 3.2 to 3.4. Scope of the examinations included determining the effect of wetting the base on mechanical parameters like compression, bending and tensile strength, as well as on technological parameters like permeability, abrasion resistance and apparent density. The research revealed a significant positive effect of adding water to wet surfaces of high-silica base grains on mechanical properties and quality of moulding sands hardened by physical methods, in particular by microwave heating.

In the paper, an attempt is made to explain the previously observed increased effectiveness of utilising hydrated sodium water-glass grade 137 after hardening moulding sands with selected physical methods. In the modified process of preparing sandmixes, during stirring components, water as a wetting additive was introduced to the sand-binder system. Presented are examination results of influence of faster microwave heating and slower traditional drying of the so-prepared moulding sands on their tensile and bending strength, calculated per weight fraction of the binder. The measurement results were confronted with SEM observations of linking bridges and with chemical analyses of grain surfaces of high-silica base. On the grounds of comprehensive evaluation of hardened moulding sands, positive effects were found of the applied physical process of binder dehydration and presence of the wetting additive. It was observed that introduction of this additive during stirring, before adding the binder, improves flowing the binder to the places where durable linking bridges are created. It was also found that the applied methods of hardening by dehydration enable creation of very durable linking bridges, strongly connected with the sand base, which results in damages of high-silica grain surfaces, when the bridges are destroyed.

This paper presents the results on the effects of die-casting process on the strength parameters of castings of the aluminium AlSi9Cu3 alloy belonging to the group of EN AB-46000, made on renovated high pressure die-casting machine. Specimens for quality testing were taken from the places of the casting most loaded during the service. The aim of a research was to prove how the new die-casting process control capabilities influence on the tensile strength of the cast material defined as a value of the breaking force of the specimens. It has been found that it is possible to specify a set of recommended settings valves of second (II) and third (III) phase, which are responsible for filling the metal mould on die-casting pressure machine. From the point of view of the finished cast element, it was noticed that exceeding the prescribed values of valve settings does not bring further benefits and even causes unnecessary overload and reduce the durability of the mold. Moreover, it was noticed that reduction of the predetermined setting of the second phase (II) valve leads to the formation of casting defects again.

Presented are results of a research on the possibility of using artificial neural networks for forecasting mechanical and technological parameters of moulding sands containing water-glass, hardened in the innovative microwave heating process. Trial predictions were confronted with experimental results of examining sandmixes prepared on the base of high-silica sand, containing various grades of sodium water-glass and additions of a wetting agent. It was found on the grounds of obtained values of tensile strength and permeability that, with use of artificial neural networks, it is possible complex forecasting mechanical and technological properties of these materials after microwave heating and the obtained data will be used in further research works on application of modern analytic methods for designing production technology of high-quality casting cores and moulds.

The paper presents a research on abrasion resistance of selected construction materials designed for foundry tooling applied in the innovative microwave heating process of moulding and core sands. One of the main selection criteria of the materials for foundry tooling, in particular for models, moulding boards, moulding boxes and core boxes, is their good abrasive wear resistance. Usability of the selected polymeric materials, designed for foundry tooling used in electromagnetic field, is decided also by other evaluation criteria determined in the examinations, like thermal resistance and electrical properties. Abrasion resistance of the selected materials was determined for three grades of the moulding sand matrixes. Combined analysis of the determined abrasion resistance, considering also electrical properties and thermal resistance of the foundry tooling materials, characterising their usability for microwave heating of moulding and core sands, will make possible their systemising with respect to effectiveness and efficiency of the heating process, taking under consideration durability of such foundry tooling to be used in industrial conditions.

W pracy przedstawiono wyniki badań nad określeniem możliwości prowadzenia skutecznej regeneracji zużytych mas formierskich ze szkłem wodnym utwardzanych w procesie nagrzewania mikrofalowego. Przeznaczoną do badań masę, sporządzoną z wybranym szkłem wodnym sodowym gatunku 145, poddawano kolejno procesom: utwardzania mikrofalowego, studzenia, obciążaniu termicznemu do temperatury 800°C. studzenia do temperatury otoczenia, rozkruszania i regeneracji mechanicznej. Opisane procesy tworzyły jeden zamknięty cykl przerobu zużytej masy. Po każdym kolejnym cyklu przerobu masy określano zmianę wytrzymałości na rozciąganie i zginanie. Analizując wyniki przeprowadzonych badań stwierdzono, że istnieje możliwość aktywacji regeneratu zużytej masy formierskiej ze szkłem wodnym, utwardzanej w procesie nagrzewania mikrofalowego, pod warunkiem zastosowania odpowiednich parametrów jej przygotowania, odbywającego się w kolejnych cyklach eksploatacji.

In the paper presented are results of a research on influence of electrical and physico-chemical properties of materials being parts of multicomponent and multimaterial systems used in foundry practice on efficiency and effectiveness of microwave heating. Effectiveness of the process was evaluated on the grounds of analysis of interaction between selected parameters of permittivity and loss factor, as well as collective index of energy absorbed, reflected and transmitted by these materials. In the examinations used was a stand of waveguide resonance cavity for determining electrical properties and a stand of microwave slot line for determining balance of microwave power emitted into selected materials. The examinations have brought closer the possibility of forecasting the behaviour of multimaterial systems like e.g. model, moulding sand or moulding box in microwave field on the grounds of various electrical and physico-chemical properties. On the grounds of analysis of the results, possible was selecting a group of materials designed for building foundry instrumentation to be effectively used in electromagnetic field.

Presented are results of a research on usability of an innovative reclamation process of microwave-hardened moulding sands containing water-glass, combined with activation of binder. After each subsequent stage of reclamation, quality of the reclaimed material was determined on the grounds of measurements of permeability and results of screen analysis. The reclaimed material was next used again to prepare new moulding sand. The sandmix based on high-silica sand prepared with water-glass grade 145, was subject to the following cyclical treatment operations: mixing components, consolidation, microwave hardening, cooling, heating the mould up to 800 °C, cooling to ambient temperature, mechanical reclamation dry and wet. It was found that the used-up and reclaimed sandmix containing water-glass is susceptible to the applied activation process of thermally reacted film of binder and, in addition, it maintains good quality and technological properties of high-silica base. Observations of surfaces of reclaimed high-silica grains with activated film of reacted inorganic binder were carried-out using a scanning microscope. Thanks to properly selected reclamation parameters, the high-silica base can be reused even five times, thus reducing demand for fresh aggregate and inorganic binder.

In the paper presented are results of a research on effectiveness of absorbing electromagnetic waves at frequency 2.45 GHz by unhardened sodium silicate base sands (SSBS) prepared of high-silica base sand and a PLA (Polylactide) 3D-prited (3DP) mould walls. Measurements of power loss of microwave radiation (Pin) expressed by a total of absorbed power (Pabs), output power (Pout) and reflected power (Pref) were carried-out on a stand of semiautomatic microwave slot line for determining balance of microwave power emitted into selected multimaterial systems. Values of microwave power loss in the rectangular waveguide filled with unhardened moulding sands and prepared by fused deposition modelling (FDM) 5 mm polylactide (PLA) walls with grid infill density from 25% to c.a. 100% served for determining effectiveness of microwave heating. Balance of microwave power loss is of technological importance for microwave manufacture of highquality casting sand moulds and cores in possibility of use 3D-printed mould tools and core boxes. It was found that apparent density of SSBS placed in a waveguide with PLA walls influences parameters of power output (Pout) and power reflected (Pref). The PLA wall position and grid infill density were identified to have a limited effect on effectiveness of absorbing microwaves (Pabs). [ABSTRACT FROM AUTHOR]

The study discusses the issues of low durability of dies used in the first operation of producing a valve type forging from high nickel steel assigned for the application in motor truck engines. The analyzed process of manufacturing the exhaust valve forgings is realized in the coextrusion technology, followed by forging in closed dies. This process is difficult to master, mainly due to elevated adhesion of the charge material (high nickel steel - NCF3015) to the tool substrate as well as very high abrasive wear of the tool, most probably caused by the dissolution of hard carbide precipitates during the charge heating. A big temperature scatter of the charge during the heating and its short presence in the inductor prevents microstructure homogenization of the bearing roller and dissolution of hard precipitates. In effect, this causes an increase of the forging force and the pressures in the contact, which, in extreme cases, is the cause of the blocking of the forging already at the beginning of the process. In order to analyze this issue, complex investigations were conducted, which included: numerical modelling, dilatometric tests and hardness measurements. The microstructure examinations after the heating process pointed to lack of structure repeatability; the dilatometric tests determined the phase transformations, and the FEM results enabled an analysis of the process for different charge hardness values. On the basis of the conducted analyzes, it was found that the batch material heating process was not repeatable, because the collected samples showed a different amount of dissolved carbides in the microstructure, which translated into different hardnesses (from over 300 HV to 192 HV). Also, the results of numerical modeling showed that lower charge temperature translates into greater forces (by about 100 kN) and normal stresses (1000 MPa for the nominal process and 1500 MPa for a harder charge) and equivalent stresses in the tools (respectively: 1300 MPa and over 1800 MPa), as well as abrasive wear (3000 MPa mm; 4500 MPa mm). The obtained results determined the directions of further studies aiming at improvement of the production process and thus increase of tool durability. [ABSTRACT FROM AUTHOR]

The aim of the research was to determine the effect of the primary quality of reclaim from dry mechanical reclamation on the strength properties and service life of moulding sands based on this reclaim. Another aim was to establish the effect of the quality of reclaim, sulphur content - in particular, on the surface quality and thickness of the deformed surface layer in ductile iron castings. The research has revealed differences in the strength parameters and service life (mouldability) of sands based on the tested reclaims, depending on the type of the furfuryl resin used, including resins whose synthesis was done as part of the Żywfur project. Examinations of the structure of the surface layer of test castings poured in moulds made of loose self-hardening sands containing the addition of reclaim have confirmed the occurrence of degenerated spheroidal graphite in this part of the casting. It should be noted here that when massive castings with a long solidification time are made, the graphite degeneration effect can be more visible and the layer with the changed structure can increase in thickness. The research has clearly shown that it is necessary to control the parameters of the reclaim, including sulphur content which is transferred from the hardener and accumulates on the grains. This phenomenon has a negative impact not only on the sand strength and technological properties but also on the surface layer of castings. [ABSTRACT FROM AUTHOR]

For research purposes and to demonstrate the differences between materials obtained from the carbonaceous additives to classic green moulding sands, five lustrous carbon carriers available on the market were selected. The following carbonaceous additives were tested: two coal dusts (CD1 and CD2), two hydrocarbon resins (HR1 and HR2) and amorphous graphite (AG1). The studies of products and material effects resulting from the high-temperature pyrolysis of lustrous carbon carriers were focused on determining the tendency to gas evolution, including harmful compounds from the BTEX group (benzene, toluene, ethylbenzene and xylene). Moreover, the content of lustrous carbon (LC), the content of volatile matter and loss on ignition (LOI) of the carbonaceous additives were tested. The solid products formed during high-temperature pyrolysis were used for the quantitative and qualitative evaluation of elemental composition after the exposure to temperatures of 875oC in a protective atmosphere and 950oC in an oxidizing atmosphere. The conducted studies have indicated the necessity to examine the additives to classic green moulding sands, which is of particular importance for the processing, rebonding and storage of waste sand. The studies have also revealed some differences in the quantitative and qualitative composition of elements introduced to classic moulding sands together with the carbonaceous additives that are lustrous carbon carriers. It was also considered necessary to conduct a research on lustrous carbon carriers for their proper and environmentally friendly use in the widely propagated technology of classic green sand system. [ABSTRACT FROM AUTHOR]

The paper presents the preliminary results of research on determining the possibilities of using available on the market commercial gypsum kinds as a binder for foundry moulding and core sandmixes. Construction gypsum and plaster gypsum, finishing coat and jewelry casting gypsum were tested. Elemental composition of gypsum kinds were carried out using a scanning electron microscope (SEM) with EDS/EDX probe, their crystal structure and phase composition was determined by analyzing the results of X-ray diffraction measurements (XRD) and thermogravimetric studies (TG-DTA). Evaluation of the mechanical properties of selected materials was carried out at the tensile strength test of the dog-bone samples after initial hardening of gypsum mortar at 25 °C for 5 h and drying at 110 °C for 24 hours. The impact of the properties of the used commercial gypsum kinds on the possibility of their use as a valuable binders in the manufacture of the foundry sandmixes for moulds and cores was evaluated. Construction gypsum and finishing coat have the highest tensile strength. Plaster gypsum and finishing coat have the longest setting time. In all tested types of gypsum, the initial water loss during heating occurs at a temperature of about 200 °C. The lowest valuable properties as a binder for sand moulding mixtures has jewelry casting gypsum mass. [ABSTRACT FROM AUTHOR]

The paper presents the results of preliminary research on the application of olivine moulding sands with hydrated sodium silicate containing 1.5 % wt. of binder to perform ecological casting cores in hot-box technology using a semi-automatic core shooter. The following parameters were used in the process of core shooting: initial shot pressure of 6 bar, shot time 3 s, the temperature of the corebox: 200, 250 and 300 °C and the core curing time: 30, 60, 90, 120 and 150 s. The matrix of the moulding mixture was olivine sand, and the binder of the sandmix was commercial, unmodified hydrated sodium silicate with molar module SiO2/Na2O of 2.5. In one shot of the automatic core-shooter were formed three longitudinal specimens (cores) with a dimensions 22.2×22.2×180 mm. The samples obtained in this way were subjected to the assessment of the influence of the shooting parameters, i.e. shooting time, temperature and curing time in core-box, using the following criteria: core box fill rate, mechanical strength to bending RgU, apparent density, compaction degree and susceptibility to friability of sand grains after hardening. The results of trials on the use of olivine moulding sands with hydrated sodium silicate (olivine SSBS) in the process of core shooting made it possible to determine the conditions for further research on the improvement of inorganic hot-box process technology aimed at: reduction of the heating temperature and the curing time. It was found that correlation between the parameters of the shooting process and the bending strength of olivine moulding sands with sodium silicate is observed. [ABSTRACT FROM AUTHOR]

This paper outlines issues associated with gas-shielded braze welding of CU-ETP copper with austenitic steel X5CrNi18-10 (1.4301) using a consumable electrode. The possibilities for producing joints of this type using innovative low-energy welding methods are discussed. The paper provides an overview of the results of metallographic and mechanical (static shear test, microhardness) tests for braze welded joints made on an automated station using the Cold Metal Transfer (CMT) method. Significant differences in the structure and mechanical properties are indicated, resulting from the joint configuration and the type of shielding gas (argon, helium). [ABSTRACT FROM AUTHOR]

This study is an attempt to determine by Hot Distortion Test (HDT) the impact of physical methods of hardening inorganic binders in the moulding sands on phenomena caused by influence of thermal energy from heating elements with a temperature of 900°C +/- 10°C. Medium silica sand-based moulding mixtures were densified and then hardened using two physical methods: microwave heating at a frequency of 2.45 GHz or classical drying at a temperature of 110oC. Sodium silicate bonded sand (SSBS) with five unmodified kinds of hydrated sodium silicates subjected to two different types of hardening method were assessed in terms of their behaviour in high temperature. Thermal behaviour by means of deformation measurement was carried out with a modified Hot Distortion Test (mHDT). Due to this advanced, but unstable by appropriate standards Hot Distortion Test gives an opportunity to measure thermoplastic deformations (L) in moulding sands in many aspects, such as time of annealing. Research carried out in this way exposed differences between inorganic binders with molar module ranging from 3.4 to 2.0. It was established that deformations under the influence of high temperature last the longest in SSBS containing binders with molar module ranging from 3.4 to 2.9. Similarly, for these types of moulding sands the method of hardening the binder is found to be essential for increasing/decreasing the rate of thermoplastic deformations during the annealing of samples. The samples of SSBS made with binders with molar module from 2.5 to 2.0 are found to be excessively susceptible to thermoplastic deformation as a result of heating them in high environmental temperature presence. [ABSTRACT FROM AUTHOR]

This paper presents initial findings from research into the possibility of using gypsum binders in quartz moulding sand that could be used in the production of casting moulds and cores. For the purposes of the research two commercial types of gypsum were used as binders: building gypsum and gypsum putty. Dry components of moulding sand i.e. medium quartz sand and gypsum were mixed in proportion of 89/11 parts by weight. In order to achieve bonding properties for the binders, 5 parts by weight of water was added to the mixture of dry components. After 24 hours of adding water and mixing all the components, the moulding sand, naturally hardened, was subjected to high temperature. The moulding sand thus produced, i.e. with cheap and environmentally-friendly gypsum binders, was eventually analysed after heating (at temperatures of 300oC, 650oC and 950oC) and cooling in order to determine changes in the following parameters: LOI - loss on ignition, chemical composition and pH. Moreover, investigated were bonding bridges, before and after the moulding sand was roasted. The research results revealed differences in the structure of bonding bridges and the occurrence of automatic adhesive destruction for both types of gypsum binders. For two types of moulding sands under the investigation of the LOI exceeded 2.59wt.% (with building gypsum) or 2.84wt.% (with putty gypsum) and pH increased to ca. 12 as a result of increasing roasting temperature from 300oC to 650oC. Next, roasting at 950oC decrease value of LOI in both types of moulding sands. Moulding sand with building gypsum roasted at 950oC revealed a return to the value of pH parameter measured prior to annealing. [ABSTRACT FROM AUTHOR]