Search

The purpose of this study was to investigate the effect of previous phosphoric acid etching on the dentin bond strength of single-step self-etch adhesive systems. Facial surfaces of bovine teeth were wet ground with #600 SiC paper. Adhesives were applied with and without previous phosphoric acid etching, and light irradiated. Resin composite was bonded to the adherend surface, followed by light irradiation and storage in water at 37 degrees C. Four groups (n = 10) were made per adhesive system: with and without previous acid etching and with and without thermal cycling between 5 degrees C and 55 degrees C for 10,000 cycles. Specimens were tested in a shear mode at a crosshead speed of 1.0 mm/min. Two-way ANOVA and Tukey HSD test at a level of 0.05 were performed. The changes in dentin bond strengths were different among the adhesive systems tested. In all experimental conditions of this study, the dentin bond strength decreased or remained unchanged with previous acid etching. From the results of this study, previous acid etching might not be acceptable for increasing dentin bond strength of the single-step self-etch adhesive systems.

The purpose of this study was to investigate the development of shear bond strength of resin composites using self-etching primer systems. Four different types of self-etching primer systems with different combinations of their recommended resin composites were used. Bovine incisors were mounted in self-curing resin and the facial surfaces were wet ground on #600-SiC paper to expose the dentin. The shear bond strengths of ten samples per test group were measured at a crosshead speed of 1.0 mm/min after storage for 5, 10, and 60 min, and 24 h in distilled water at 37 degrees C. One-way ANOVA followed by Dunnett's test (alpha = 0.05) was used to examine the significance of differences between the mean bond strength at 24 h and each of the other storage periods. The dentin bond strengths of all the materials tested increased with prolonged storage time. Such differences in the changes in bond strength might have clinical implications if a restoration is subjected to high stress immediately after it has been placed. It is important to consider the development of dentin bond strength to allow the materials sufficient maturation time prior to functional loading or application of other forms of external stress.

Color characteristics of the shades for different filler type resin composites were compared in the reflectance and transmittance modes, and specular component included (SCI) and specular component excluded (SCE) geometries for reflectance mode. Resin composites and shades used in this study were submicron filled Estelite Sigma (Sigma: Inc, A2, A3, B3, C2, OA2, OA3) and nanofilled Filtek(TM) Supreme XT (XT: Clear, A2E, A2B, A3B, C2B, A2D, A3D). Resin disks of 2 mm in thickness and final polish with 2,400-grit silicon carbide paper were kept in 100% humidity. One week after curing, color of the resin disks were measured with a spectrophotometer. Both for Sigma and XT, reflectance of each of all shades measured with SCI were significantly higher than those with SCE. Compared to the values with SCI and SCE, the L with SCI were significantly higher for all shades of Sigma and XT, however, a and b were depended with brands and shades. Different filler type resin composites showed different color characteristics, reflectance, transmittance and L a b distribution. In some shades, color difference between the measurement with SCI and SCE was visually perceptible level. It would be concluded that the color of resin composite measured with the SCI and SCE geometries differed.

Single-step self-etch adhesive systems have been developed to simplify and shorten bonding procedures. With the gain in popularity of these simplified systems, their reliability has become a focus of interest. The purpose of this study was to determine the effect of adhesive application method on enamel bond strength. Two commercial single-step self-etch adhesive systems, Clearfil tri-S Bond, and G-Bond, were used. Bovine mandibular incisors were mounted in self-curing resin and the facial enamel surfaces were ground wet on 600-grit SiC paper. Adhesives were only applied without agitation (inactive) or were agitated by a brush (active), and resin composites were condensed into the mold on the enamel surface and light-activated. Ten specimens per test group were stored in water at 37 degrees C for 24 h, then shear-tested at a cross-head speed of 1.0 mm/min. Two-way ANOVA followed by the Tukey HSD test were used. The bond strengths for active application were higher than those for inactive application. Significant differences were found for both adhesive systems. From the results of this study, active application of single-step self-etch adhesive may help to ensure the creation of a roughened enamel surface and enhance the penetration of resin monomer into the subsurface demineralized enamel.

Milk and milk products, such as cheese, have been shown to exhibit anticariogenic properties in human and animal models. CPP-ACP shows an anti-caries effect by suppressing demineralization, enhancing remineralization, or possibly a combination of both. The purpose of this study was to evaluate the effect of CPP-ACP paste on demineralization by observing the treated tooth surface using an FE-SEM. The specimens were prepared by cutting enamel and dentin of bovine teeth into blocks. A few specimens were stored in 0.1 M lactic acid buffer solution for 10 min and then in artificial saliva (negative control). The remaining specimens were stored in a 10 times-diluted solution of CPP-ACP paste or a placebo paste containing no CPP-ACP for 10 min, followed by 10 min immersion in a demineralizing solution (pH = 4.75, Ca) twice a day before storage in artificial saliva. After treatment of the specimens for 3, 7, 21 and 28 days, they were fixed in 2.5% glutaraldehyde in cacodylate buffer solution, dehydrated in ascending grades of tert-butyl alcohol, and then transferred to a critical-point dryer. The surfaces were coated with a thin film of Au in a vacuum evaporator, and were observed under field emission-scanning electron microscopy (FE-SEM). The SEM observations revealed different morphological features brought about by the various storage conditions. Demineralization of the enamel and dentin surfaces was more pronounced with the longer test period in the control and negative control specimens. On the other hand, enamel and dentin specimens treated with CPP-ACP paste revealed slight changes in their morphological features. From the morphological observations of the enamel and dentin surfaces, it could be considered that the CPP-ACP paste might prevent demineralization of the tooth structure.

This study was conducted to clarify the influence of dentin surface moisture on bond strength of single-step self-etch adhesive systems. The adhesive systems used were Adper Prompt L-Pop (AP), Clearfil tri-S Bond (CT), Fluoro Bond Shake One (FB), G-Bond (GB), and One-Up Bond F Plus (OF). Bovine mandibular incisors were wet-ground with #600 SiC to expose the labial dentin. After rinsing with tap water, the dentin surface was dried with air for 10 sec (Dry condition) or blotted (Wet condition). Adhesives were applied according to each manufacturer's instructions, followed by resin composite polymerization. Ten samples per test group were stored in distilled water at 37 degrees C for 24 h, then shear tested at a crosshead speed of 1.0 mm/min. The data were analyzed by Student's t test and Tukey HSD test at a probability level of 0.05. The mean bond strengths for Dry condition ranged from 13.9 MPa to 18.2 MPa, and those for Wet condition ranged from 7.1 MPa to 18.4 MPa. Significantly lower bond strengths were obtained for the Wet condition for GB, FB, and OF. Failure after the test was commonly due to adhesive breakdown associated with partial cohesive failure in the dentin. These data suggest that air-drying of the dentin surface is appropriate for the adhesive systems tested.

The purpose of this study was to investigate the influence of light intensity on dentin bond strengths of four self-etch adhesive systems. The light intensities used to polymerize specimens were controlled at levels of 150, 300, 600, and 900 mW/cm2. The two-step self-etch adhesive systems Imperva Fluoro Bond and Mac Bond II, and the one-step self-etch systems Fluoro Bond Shake-One and One-Up Bond F Plus were used with their corresponding light-cured resins. Labial surfaces of lower bovine incisors were ground with #600 grit SiC paper to expose the dentin. The dentin surfaces were treated according to each manufacturer's instructions and bonded with resin composites. A shear bond strength test was performed and the data were analyzed by one-way ANOVA followed by Newman-Keuls multiple comparison at a level of 0.05. Statistical analysis of the data indicated that light intensity affected the dentin bond strengths of the adhesive systems tested. Significantly lower bond strengths were obtained by exposure to 150 mW/cm2, and there were no differences between the bond strengths obtained at 600 and 900 mW/cm2 for all the adhesive systems used. Further research will be required to clarify the irradiance-dependent properties of light-cured resin adhesive systems.

This study aimed to determine the influence of metal conditioners on the polymerization behavior of bonding agents. Bonding agents of two-step self-etching primer systems and metal conditioners for adhesion of dental metal alloys were used. Double bond conversion was determined by Fourier transform-ation infrared spectroscopy. The percentage of residual double bonds, including pendant and monomeric double bonds, was calculated by comparing the obtained ratio with that of the uncured bonding agent. The degree of conversion of the bonding agents was obtained by subtracting the remaining double bonds from 100%. ANOVA followed by a Tukey HDS test was performed. Degree of conversion of the bonding agents ranged from 86.0 to 87.8%. When the bonding agents were mixed with metal conditioners or solvents of the metal conditioners, double bond conversion of the bonding agents tended to decrease. Within the limitations of this study, which was far removed from clinical situations, the presence of metal conditioners and remaining solvents had adverse effects on the polymerization reaction of bonding agents. Clinicians should be cognizant of the various factors that can influence bond strength of restorative resins to dentin.

There is a need for effective polishing instruments for resin composite restorations with highly polished surfaces. The purpose of this study was to investigate the influence of polishing duration on surface roughness of light-cured resin composites. Four polishing systems, Compomaster (Shofu), Silicone Points C Type (Shofu), Super Snap (Shofu) and Enhance Finishing and Polishing System (Dentsply/Caulk), were used to polish two commercially available resin composites, Clearfil AP-X (Kuraray Medical) and Lite-Fil II A (Shofu). Resin pastes were condensed into molds (10 mm in diameter, 5 mm in depth) and light irradiated for 40 s. Composite surfaces were ground with # 600 SiC paper followed by polishing with an instrument for 30 s, and the surface roughness was measured every 10 s during polishing procedures. The average surface roughnesses (Ra) were determined using a profilometer. Data were analyzed by Tukey HSD test (P = 0.05). After 30 s of polishing, mean Ra values ranged from 0.07 to 0.50 for Clearfil AP-X, and from 0.11 to 0.57 for Lite-Fil II A. Although the time required for polishing was longer, the surface finish produced by multiple-step polishing systems was superior to that obtained with one-step polishing systems.