Abstract Flexible and lightweight Cu(In,Ga)Se2 (CIGS) thin-film solar cells are promising for versatile applications, but there is limited understanding of stress-induced changes. In this study, the charge carrier generation and trapping behavior under mechanical stress was investigated using flexible CIGS thin-film solar cells with various alkali treatments. Surface current at the CIGS surface decreased by convex bending, which occurs less with the incorporation of alkali metals. The formation energy of the carrier generating defects increased in convex bending environments clarifying the degradation of the surface current. Moreover, alkali-related defects had lower formation energy than the intrinsic acceptors, mitigating current degradation in mechanical stress condition. The altered defect energy levels were attributed to the deformation of the crystal structure under bending states. This study provides insights into the mitigating of strain-induced charge degradation for enhancing the performance and robustness of flexible CIGS photovoltaic devices.

Abstract Understanding the stress-induced phenomena is essential for improving the long-term application of flexible solar cells to non-flat surfaces. Here, we investigated the electronic band structure and carrier transport mechanism of Cu2ZnSn(S,Se)4 (CZTSSe) photovoltaic devices under mechanical stress. Highly efficient flexible CZTSSe devices were fabricated controlling the Na incorporation. The electronic structure of CZTSSe was deformed with stress as the band gap, valence band edge, and work function changed. Electrical properties of the bent CZTSSe surface were probed by Kelvin probe force microscopy and the CZTSSe with Na showed less degraded carrier transport compared to the CZTSSe without Na. The local open-circuit voltage (V OC) on the bent CZTSSe surface decreased due to limited carrier excitation. The reduction of local V OC occurred larger with convex bending than in concave bending, which is consistent with the degradation of device parameters. This study paves the way for understanding the stress-induced optoelectronic changes in flexible photovoltaic devices.