Search

This research presents the microstructural and mechanical evolution throughout the welded seam of an austenitic stainless steel (ASS) tube. It was found that the main hardness decrement occurred in the fusion zone (FZ), followed by the heat-affected zone (HAZ) and the base material (BM). Optical microscopy indicated a dendritic structure in FZ and heterogeneous austenitic grain size from the HAZ towards the BM, ranging from 100 µm to 10 µm. The welding process generated an intense texture around the FZ and the HAZ, while the BM still showed an extrusion-like texture. In terms of mechanical behavior, the largest austenite grain size in the FZ led to the lowest strength and ductility of all zones due to the earliest strain localization manifested by heterogeneous strain distribution. However, the strain localization in all zones appeared after 0.4 true strain, indicating an overall good ductility of the seam. These high values were related to two microstructure characteristics: (1) the 10% d-ferrite after solidification in the FZ favored by the Creq/Nieq=1.67 relationship that delayed the crack propagation along the austenite grains and (2) the heterogeneous microstructure made up of soft austenite and hard martensite in the HAZ and BM producing multiple strain concentrations. Kernel Average Misorientation (KAM) maps obtained by Electron Back-Scattering Diffraction (EBSD) allowed observing higher internal misorientations in the FZ than in the HAZ due to interconnected walls between the d-ferrite grains. However, the largest KAM values were observed in the BM between ¿-austenite and the deformation-induced a’-martensite phases. X-ray diffraction revealed that the residual stresses in the cross-section of the welded seam were compression-type and then switched to tension-type in the outer surface., Peer Reviewed, Postprint (published version)

Metastable austenitic stainless steels (MASS) are widely used in various industrial applications due to their exceptional compromise between mechanical properties and corrosion resistance. However, the mechanical properties of these materials can be further enhanced by surface treatments. This paper reviews various surface treatment methodologies used to improve the mechanical properties of MASS, with particular attention to laser treatments. The effects of these surface treatments on the microstructure and chemical composition in the thermal affected zone of the MASS are discussed, and their impact on the material’s mechanical properties, such as hardness, tensile strength, and fatigue life, are investigated in detail. Additionally, the paper highlights the limitations of these surface treatments and points out some areas where further research is needed. The findings presented can be used to guide the selection of appropriate surface treatment techniques for specific applications, ultimately improving the performance and lifespan of MASS in various industrial settings., Peer Reviewed, Postprint (published version)

This study explores pulsed Nd:YLF laser surface modification (LSM) effects on AISI 301LN stainless steel. Laser-treated surfaces underwent SEM characterization, revealing patterns and irregularities. Higher heat input surfaces showed significant microstructural changes, while lower heat input surfaces experienced less alteration. Increased laser spot overlap led to larger exposed areas and higher heat input, influencing groove width, depth, and surface roughness. Three-dimensional reconstructions illustrated the correlation between laser parameters and surface characteristics. XRD (X-ray diffraction analysis) and EBSD (Electron backscatter diffraction) analyses revealed a transformation from austenite to martensite, with an increase in the a’-martensite phase, particularly in patterns with high laser power, attributed to rapid cooling during laser modification. Grain size analysis indicated a 42% reduction post-treatment, enhancing the surface fraction of fine grains. Hardness measurements demonstrated an overall increase in laser-treated samples, linked to fine-grained microstructure formation, induced residual stresses, and the a’-martensitic phase., The authors would like to express their special gratitude to the Outokumpu for supplying the stainless steel and the Agència de Gestió d’Ajuts Universitaris i de Recerca (AGAUR) del Departament de Recerca i Universitats de la Generalitat de Catalunya for recognizing the Microstructural Design and Advanced Manufacturing of Materials Group as a consolidated research group (number 2021SGR01053). M. Rezayat acknowledges the AGAUR (FI-SDUR-2020) of the Generalitat de Catalunya for its financial support. H. Besharatloo acknowledges Ministerio de Universidades for the Margarita Salas grant., Peer Reviewed, Postprint (published version)