Search

Cationic photo-initiated and polymerized epoxies are characterized by good adhesion, high modulus, zero volatiles, low shrinkage and living polymerization characteristics. Radiation—cured acrylate resins are characterized by rapid initial curing with increased initial strength. The combination of radiation-cured acrylates and epoxies may present advantageous attributes. Thus, the system investigated is a hybrid epoxy/methyl acrylate and three different initiators for cationic polymerization of epoxies, the radical reaction of acrylates and the thermal initiator. When incorporating additives like opaque WS2 nanoparticles (NPs), absorption of the photo radiation takes place, which may lead to low photo activity. Curing kinetics measurements revealed that the absorbing/masking effect of WS2 was insignificant, and surprisingly, the level of curing was enhanced when the WS2 NPs were incorporated. FTIR results demonstrated that covalent bonds were formed between the inorganic fullerenes (IF-WS2) and the crosslinked matrix. Viscosity measurements showed a surprising reduction of five to ten times in the low-shear viscosity upon NPs incorporation compared to neat resins. It was concluded that the decrease of viscosity by the inorganic NPs, in addition to the enhanced level of conversion, has profound advantages for structural adhesives and 3D printing resins. To the best of our knowledge, this investigation is the first to report on a radiation-induced curing system containing opaque WS2 NPs that leads to an enhanced degree of curing and reduced shear viscosity.

The effect of particle loading on the wetting properties of coatings was investigated by modifying a coating formulation based on hydrophilic silica nanoparticles and poly (acrylic acid) (PAA). Water contact angle (WCA) measurements were conducted for all coatings to characterize the surface wetting properties. Wettability was improved with an increase in particle loading. The resulting coatings showed superhydrophilic (SH) behavior when the particle loading was above 53 vol. %. No new peaks were detected by attenuated total reflection (ATR-FTIR). The surface topography of the coatings was studied by atomic force microscopy (AFM) and scanning electron microscopy (SEM). The presence of hydrophilic functional groups and nano-scale roughness were found to be responsible for superhydrophilic behavior. The surface chemistry was found to be a primary factor determining the wetting properties of the coatings. Adhesion of the coatings to the substrate was tested by tape test and found to be durable. The antifogging properties of the coatings were evaluated by exposing the films under different environmental conditions. The SH coatings showed anti-fogging behavior. The transparency of the coatings was significantly improved with the increase in particle loading. The coatings showed good transparency (>85% transmission) when the particle loading was above 84 vol. %.

This study focused on the effect of Multi Wall Carbon Nanotubes (MWCNT) content and its surface treatment on thermo-mechanical properties of epoxy nanocomposites. MWCNTs were surface treated and incorporated into two epoxy systems. MWCNT's surface treatments were based on: (a) Titania coating obtained by sol-gel process and (b) a nonionic surfactant. Thermo-mechanical properties improvement was obtained following incorporation of treated MWCNT. It was noticed that small amounts of titania coated MWCNT (0.05 wt %) led to an increase in the glass transition temperature and stiffness. The best performance was achieved adding 0.3 wt % titania coated MWCNT where an increase of 10 °C in the glass transition temperature and 30% in storage modulus were obtained.