Search

This paper presents the results of an analysis of the changes in the stiffness of asphalt binders modified with a bio-flux additive and subjected to the processes of foaming and short-term ageing. The purpose of the analyses was to determine changes in the rheological properties of asphalt binder as a result of technological processes characteristic of hot and warm mix asphalt technology. Three asphalt binders with similar penetration but varying degrees of polymer modification were tested: 50/70, 45/80–55 polymer-modified bitumen, and 45/80–80 highly modified bitumen. Tests were carried out on four groups of binders: original binders, foamed binders after 14 days of storage, non-foamed binders after Rolling Thin Film Oven Test (RTFOT) ageing, and foamed binders after 14 days of storage subjected to RTFOT ageing. The master curves of the complex shear modulus G* were analysed, and three indexes of binder stiffening were determined, characterising the investigated effects. The tests showed that some of the stiffening indices significantly depended on the degree of polymer modification and the content of the bio-flux additive. Moreover, it was found that the foaming process in the case of paving-grade bitumen and polymer-modified bitumen did not contribute to the additional stiffening of the binders.

The study investigated the effects of laboratory ageing on the fluxed and water-foamed asphalt binders in scope of Fourier transform infrared spectroscopic measurements of ageing indicators and changes in their chemical composition. The investigated binders included two paving grades, two polymer modified asphalt binders, and a highly modified asphalt binder. The bio-flux additive was produced from rapeseed methyl esters in an oxidation reaction in the presence of a metal catalyst and organic peroxide. The use of the bio-origin additive, in particular oil derivatives, was aimed at softening and better foaming of asphalt binders. This modification is possible due to the good mixability of vegetable oils with an asphalt binder, which gives a homogeneous product with reduced stiffness. The study involved the rolling thin film oven, short-term, and the pressure ageing vessel, long term, and ageing to induce oxidation on the evaluated asphalt binders. The addition of the bio-flux additive has significantly decreased the measured content of ketone compounds related to oxidation in both non-aged and aged asphalt binders, although this effect after ageing were far smaller in magnitude. Additionally, both ageing processes decreased significantly the absorbances in the ester spectral bands specific to the bio-flux additive. All mentioned effects were similar in magnitude in all tested asphalt binders.

The research was aimed at assessing the effect of the redispersible polymer powder on the fracture resistance of a subbase made of a mineral–cement mixture with a bitumen emulsion. The test was performed at two temperatures, i.e., 0 °C and 20 °C. The prepared mixtures differed in the content of cement, asphalt emulsion, and polymer modifier. Cement and redispersible polymer powder were dosed in 1.5% steps from 0.5% to 3.5% while the amount of bitumen emulsion ranged from 0.0% to 5.0%. The SCB (semi-circular bending) tests carried out in the laboratory showed the dependence of the influence of the amount of binder and polymer modifier on the fracture resistance of the recycled subbase. Mixes containing a polymer modifier in their composition are characterized by a much higher resistance to cracking than traditional mineral–cement–emulsion mixtures. An example is the doubling of the framework’s fracture toughness (KIC) when the amount of the polymer modifier is increased from 0.5% to 2.0% with a constant cement content of 0.5%. The obtained results (KIC) in this case were 2.90 and 5.81. The key is the right ratio of polymer powder and cement in the base composition.

The paper investigates the influence of redispersible polymer powder (RPP) on the physical and mechanical properties of a cold-recycled mixture with foamed bitumen (CRM-FB). Four types of RPP with a varied chemical base were used: VA-VeoVA, VA-VeoVa-Ac, EVA and VA/VV/E/Ac. The polymer powder-modified cold recycled mixture with foamed bitumen, (P)CRM-FB, was composed of 45.8% reclaimed asphalt pavement (RAP), 45.8% natural aggregate (VA), 3.0% Portland cement CEM I 42,5R, 3.0% foamed bitumen 50/70 and 3.0% RPP, all dosed by weight. The reference mixture, (R)CRM-FB, served as a reference point for comparison. It was found that RPP improved the workability of the CRM-FB mixture. This results in a reduced number of compaction cycles and lower energy needed to obtain the air void content as in the reference mixture. In addition, the RPP modifier markedly increased the CRM-FB mixture cohesion (ITSDRY) and strength, by approximately 40&ndash, 70%, depending on the RPP used. These findings are particularly important for CRM-FB mixtures designed for road bases. The present investigations confirmed the improvement of the CRM-FB mixture parameters after the modification with RPP, regardless of the powder type used.