Search

In this study, a dental membrane scaffold was fabricated using a 3D printing technique, and the antimicrobial effect of pomegranate seed and peel extract were investigated. For the production of the dental membrane scaffold, a combination of polyvinyl alcohol, starch, and pomegranate seed and peel extracts was used. The aim of the scaffold was to cover the damaged area and aid in the healing process. This can be achieved due to the high antimicrobial and antioxidant content of pomegranate seed and peel extracts (PPE: PSE). Moreover, the addition of starch and PPE: PSE improved the biocompatibility of the scaffold, and their biocompatibility was tested using human gingival fibroblast (HGF) cells. The addition of PPE: PSE into the scaffolds resulted in a significant antimicrobial effect on S. aureusand E. faecalis bacteria. Moreover, different concentrations of starch (1%, 2%, 3% w/v) and pomegranate peel and seed extract (3%, 5%, 7%, 9%, and 11% PE v/v) were analyzed to obtain the ideal dental membrane structure. The optimum starch concentration was chosen as 2% w/v due to it giving the scaffold the highest mechanical tensile strength (23.8607 ± 4.0796 MPa). The pore sizes of each scaffold were studied by SEM analysis, and pore sizes were arranged between 155.86 and 280.96 μm without any plugging problems. Pomegranate seed and peel extracts were obtained by applying the standard extraction method. High-performance liquid chromatography was performed using the diode-array detection (HPLC-DAD) technique to analyze the phenolic content of the pomegranate seed and peel extracts. Two phenolic components of the pomegranate seed and peel extracts were investigated in the following amounts: fumaric acid (17.56 μg analyte/mg extract) and quinic acid (18.79 μg analyte/mg extract) in pomegranate seed extract and fumaric acid (26.95 μg analyte/mg extract) and quinic acid (33.79 μg analyte/mg extract) in pomegranate peel extract.

Juglone (5-hydroxy-1,4-naphthoquinone) (J) is a naphthoquinone structured allelochemical that is mostly found in the roots, leaves, nut-hulls, bark, and wood of walnut (Juglans regia). In this study, the biocompatibility, mechanical, thermal, chemical, morphological, and antimicrobial properties of the poly(lactic acid) (PLA) (w/v)/J (10, 20, 30 mg) electrospun scaffolds were investigated. Based on the results of the study, it was shown that juglone addition increased the antimicrobial properties of the scaffolds against the Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli), compared to the neat PLA film after 24 h of contact time. According to the tensile test results, the addition of J made the scaffolds more flexible but decreased the mechanical strength. The cytotoxicity properties of the J-added scaffolds demonstrated a toxic behavior on the first day of incubation. However, with an increase in the J ratio, the fibroblast cell metabolic activity increased for all incubation periods.

FEN-C-YLP-130319-0065 BAPKO Project. UID/CTM/50025/2019 In this study, the main aim was to fabricate propolis (Ps)-containing wound dressing patches using 3D printing technology. Different combinations and structures of propolis (Ps)-incorporated sodium alginate (SA) scaffolds were developed. The morphological studies showed that the porosity of developed scaffolds was optimized when 20% (v/v) of Ps was added to the solution. The pore sizes decreased by increasing Ps concentration up to a certain level due to its adhesive properties. The mechanical, swelling-degradation (weight loss) behaviors, and Ps release kinetics were highlighted for the scaffold stability. An antimicrobial assay was employed to test and screen antimicrobial behavior of Ps against Escherichia coli and Staphylococcus aureus strains. The results show that the Ps-added scaffolds have an excellent antibacterial activity because of Ps compounds. An in vitro cytotoxicity test was also applied on the scaffold by using the extract method on the human dermal fibroblasts (HFFF2) cell line. The 3D-printed SA-Ps scaffolds are very useful structures for wound dressing applications. publishersversion published