Search

Statement of Problem: Natural teeth are graded in terms of translucency and strength. Graded zirconia materials are now available with a higher yttria content on the top or in the enamel zone to increase surface translucency and a lower yttria content on the bottom or in the dentin zone to increase strength. Such materials could provide multiple advantages over uniform materials and reduce the need for porcelain veneering in anterior artificial crowns; however, studies on the properties of these materials are lacking., Purpose: The purpose of this in vitro study was to measure and compare the biaxial flexural strength, percentage light transmission, elemental content, and phase content of zones within and among color graded zirconia blocks and color- and strength-graded zirconia blocks., Material and Methods: Disks of a color graded material (Katana STML) and a strength- and color-graded material (IPS e.max ZirCAD Prime) were fabricated (Zircom Furnace). Biaxial flexural strength was measured using a piston-on-3-ball test in a universal testing machine (n=10). Absolute light transmission was measured with a spectrophotometer. Elemental compositions were quantified for 3 zones in each of the 2 zirconia materials using X-ray fluorescence analysis. Zirconia phase fractions were quantified for 3 zones using X-ray diffraction analysis (XRD). Where appropriate, 2-way ANOVA, 1-way ANOVA, and Tukey multiple pairwise comparison testing were used to determine which of the 6 zones differed from one another (α=.05)., Results: The color-graded zirconia exhibited gradients in light transmission and differences in phase content in the 3 zones measured. The color- and strength-graded zirconia exhibited gradients in light transmission, biaxial flexural strength, elemental composition, and phase content in the 3 zones measured. The bottom, dentin, or intaglio layer of a strength graded zirconia material was substantially stronger than all other zones of either material (P<.05). The top, enamel, zones of both materials possessed high light transmissibility (P<.05). The 2 materials differed with respect to biaxial strength (P<.001), light transmission (P<.02), elemental composition, and phase composition overall, as well as in most zone-by zone comparisons (P<.05). The performance and composition of the color graded material was consistent with it being a 5Y material throughout. The performance and composition of the color and strength graded material was consistent with it having a 3Y bottom zone and a 5Y top zone., Conclusions: A strength-graded and color-graded zirconia material offers potential advantages in both strength and translucency., (Published by Elsevier Inc.)

Statement of Problem: Newly developed translucent zirconia materials have been used for anterior monolithic complete coverage restorations. Surface treatments can improve adhesion, as well as decrease or increase the strength of ceramics. However, information on the influence of surface treatments on the strength of translucent zirconias is sparse., Purpose: The purpose of this in vitro study was to measure and characterize the effects of different surface treatments, including airborne-particle abrasion, on the strength of different translucent 4 mol% and 5 mol% yttria-stabilized zirconia materials., Materials and Methods: Disks (N=160) made from 4 types of translucent yttria-stabilized zirconia materials were surface-treated in 4 ways: Control groups were hand-polished with 2000-grit silicon carbide abrasive paper; as-machined; glass bead airborne-particle abraded; and alumina airborne-particle abraded. The biaxial flexural strength was measured by using a piston-on-3-ball test in a universal testing machine. The simple main effects of material type and surface treatment and their interaction on biaxial flexural strength were evaluated with 2-way ANOVA (α=.05). A priori, 1-way ANOVA and the Tukey multiple comparisons tests were used within material and treatment types (α=.05). Surface morphology was assessed by using scanning electron microscopy. Translucency, absolute transmittance, was measured by using a spectrophotometer., Results: Two-way ANOVA revealed that the effects of zirconia type, surface treatment, and their interaction all significantly affected biaxial flexural strength (P<.001). One-way ANOVA revealed that the 4Y material was stronger than all 5Y materials, regardless of surface treatment; all 5Y materials were ranked from strongest to weakest as polished; as-machined, or glass bead abraded; and alumina abraded. The 4Y material was stronger when alumina abraded than when glass bead abraded. Scanning electron microscopy showed that as-polished surfaces were smoother than all others; as-machined and glass bead abraded surfaces displayed little difference; alumina abraded was the roughest; and differences among materials were not discerned. The 1-way ANOVA and multiple comparisons testing showed that the 4Y material had less absolute transmittance, approximately 5% less, than all the 5Y materials., Conclusions: Zirconia material type and surface treatment influenced the strength of translucent zirconia materials; a 4 mol% zirconia material was stronger than 5 mol% zirconia materials for all surface treatments tested; airborne-particle abrasion using alumina had a slight strengthening effect on a 4 mol% zirconia but had a weakening effect on 5 mol% materials; airborne-particle abrasion by using alumina produced the roughest surfaces on all materials; and the 4 mol% material was slightly less translucent than the 5 mol% materials., (Copyright © 2021 The Authors. Published by Elsevier Inc. All rights reserved.)

Statement of Problem: Bonded porcelain veneers are widely used esthetic restorations. High success and survival rates have been reported, but failures do occur. Fractures are the commonest failure mode. Minimally invasive or thin veneers have gained popularity. Increased enamel and porcelain thickness improve the strength of veneers bonded to enamel, but less is known about dentin or mixed substrates., Purpose: The purpose of this in vitro study was to measure the influences of tooth substrate type (all-enamel, all-dentin, or half-dentin-half-enamel) and veneer thickness on the loads needed to cause initial and catastrophic porcelain veneer failure., Material and Methods: Model discoid porcelain veneer specimens of varying thicknesses were bonded to the flattened facial surfaces of incisors with different enamel and dentin tooth substrates, artificially aged, and loaded to failure with a small sphere. Initial and catastrophic fracture events were identified and analyzed statistically and fractographically., Results: Fracture events included initial Hertzian cracks, intermediate radial cracks, and catastrophic gross failure. All specimens retained some porcelain after catastrophic failure. Cement failure occurred at the cement-porcelain interface not at the cement-tooth interface. Porcelain veneers bonded to enamel were substantially stronger and more damage-tolerant than those bonded to dentin or mixed substrates. Increased porcelain thickness substantially raised the loads to catastrophic failure on enamel substrates but only moderately raised the loads to catastrophic failure on dentin or mixed substrates. The veneers bonded to half-dentin-half-enamel behaved remarkably like those bonded wholly to dentin., Conclusions: Porcelain veneers bonded to enamel were substantially stronger and more damage-tolerant than those bonded to dentin or half-enamel-half dentin., (Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.)

Statement of Problem: Bonded porcelain veneers are widely used esthetic restorations. Although high success and survival rates have been reported, failures occur. Fracture is the most common failure mode. Fractures range from incomplete cracks to the catastrophic. Minimally invasive or thin partial veneers have gained popularity., Purpose: The aim of this study was to measure the influences of porcelain veneer thickness and enamel substrate thickness on the loads needed to cause the initial fracture and catastrophic failure of porcelain veneers., Material and Methods: Model discoid porcelain veneer specimens of varying thickness were bonded to the flattened facial surfaces of incisors, artificially aged, and loaded to failure with a small sphere. Individual fracture events were identified and analyzed statistically and fractographically., Results: Fracture events included initial Hertzian cracks, intermediate radial cracks, and catastrophic gross failure. Increased porcelain, enamel, and their combined thickness had like effects in substantially raising resistance to catastrophic failure but also slightly decreased resistance to initial Hertzian cracking. Fractographic and numerical data demonstrated that porcelain and tooth enamel behaved in a remarkably similar manner. As porcelain thickness, enamel thickness, and their combined thickness increased, the loads needed to produce initial fracture and catastrophic failure rose substantially. Porcelain veneers withstood considerable damage before catastrophic failure., Conclusions: Increased enamel thickness, increased porcelain thickness, and increased combined enamel and porcelain thickness all profoundly raised the failure loads necessary to cause catastrophic failure. Enamel and feldspathic porcelain behaved in a like manner. Surface contact damage occurred initially. Final catastrophic failure followed flexural radial cracking. Bonded porcelain veneers were highly damage tolerant., (Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.)

A 53-year-old man experienced 2 soft tissue graft failures resulting in sizable hard and soft tissue defects in the esthetic zone following implant placement. A third connective tissue graft surgery was successful in repairing the defect and significantly improving soft tissue quality. A screw-retained, interim implant prosthesis was instrumental in gradually shaping the soft tissue over the course of the 3 surgeries. The interim prosthesis was modified numerous times to achieve a balance of esthetics, surgical protection, and gingival contours. The initial form of the prosthesis was designed to protect the surgical site and allow space for postsurgical edema. In its final form, the tissue side of the interim prosthesis pontic was designed to mimic the cross-sectional profile of a natural central incisor root but modified to deliver gentle pressure until maximum papilla height was achieved. The definitive restoration was fabricated to mimic the final design of the interim restoration and gingival architecture., (Copyright © 2013 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.)

Statement of Problem: Porcelain fused to zirconia prostheses are widely used. However, porcelain chipping, spalling, fracture, and delamination are common clinical problems. Residual stresses of thermal origin have received attention, but clear data and firing guidelines remain absent., Purpose: The purpose of this study was to measure the influence of heating and cooling protocols on the strength of porcelain fused to zirconia., Material and Methods: A modified 4-point flexural testing technique was used to measure strength, and porcelain buttons were bonded to the beam between the 2 central loading points. Beams (n=54) were made of a tetragonal polycrystalline zirconium dioxide that was partially stabilized with an yttria core and a feldspathic dental porcelain. Three different heating rates and 3 different cooling regimens were used during firing. Two-way analysis of variance (ANOVA) was used to evaluate the 2 main effects of the heating and cooling regimens and their interaction with the delamination force (α=.05). The Tukey multiple comparisons test was used to identify differences among heating or cooling regimens., Results: During loading, the porcelain buttons separated from the zirconia beams because of delamination within the porcelain, which was close to the porcelain to zirconia interface. ANOVA revealed that the effects of the cooling regimen and heating rate had statistically significant effects on failure load (P<.05). The effect of the cooling regimen was greater than that of the heating regimen., Conclusions: Slow cooling and slow heating regimens should be used when firing porcelain to zirconia. Cooling regimens were found to be more influential than heating rates. Failure was localized to the porcelain adjacent to the porcelain-zirconia interface, not to the interface itself, indicating that the residual stresses of thermal origin within the porcelain dominated. The preparation of zirconia with 50 μm aluminum oxide at a pressure of 0.34 MPa was sufficient to prevent interfacial failure., (Copyright © 2012 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.)