We report the electrical properties of Al0.3Ga0.7N/GaN heterojunction field effect transistor (HFET) structures with a Ga2O3 passivation layer grown by metal–organic chemical vapor deposition (MOCVD). In this study, three different thicknesses of β-Ga2O3 dielectric layers were grown on Al0.3Ga0.7N/GaN structures leading to metal-oxide-semiconductor-HFET or MOSHFET structures. X-ray diffraction (XRD) showed the (2¯01) orientation peaks of β-Ga2O3 in the device structure. The van der Pauw and Hall measurements yield the electron density of ~ 4 × 1018 cm−3 and mobility of ~770 cm2V−1s−1 in the 2-dimensional electron gas (2DEG) channel at room temperature. Capacitance–voltage (C-V) measurement for the on-state 2DEG density for the MOSHFET structure was found to be of the order of ~1.5 × 1013 cm−2. The thickness of the Ga2O3 layer was inversely related to the threshold voltage and the on-state capacitance. The interface charge density between the oxide and Al0.3Ga0.7N barrier layer was found to be of the order of ~1012 cm2eV−1. A significant reduction in leakage current from ~10−4 A/cm2 for HFET to ~10−6 A/cm2 for MOSHFET was observed well beyond pinch-off in the off-stage at -20 V applied gate voltage. The annealing at 900° C of the MOSHFET structures revealed that the Ga2O3 layer was thermally stable at high temperatures resulting in insignificant threshold voltage shifts for annealed samples with respect to as-deposited (unannealed) structures. Our results show that the MOCVD-gown Ga2O3 dielectric layers can be a strong candidate for stable high-power devices.

This work reports yarn pull-out studies of commercially available Kevlar® KM2+ individual yarns coated with metallic layers (copper, aluminum, aluminum nitride and silver) via a directed vapor deposition process. The uncoated control and metal-coated Kevlar® yarns are hand-woven into fabric swatches for quasi-static pull-out experiments. To perform these experiments, a yarn pull-out fixture is custom-designed and fabricated to apply transverse pre-tension to the fabric. Three levels of transverse pre-tensions are studied at 100 N, 200 N, and 400 N. The results showed that both peak pull-out force and energy absorption during the pull-out process increase with increase in transverse pre-tension. All the metal-coated groups showed an approximately 200% increase in peak pull-out force and a 20% reduction in tenacity compared to uncoated control. Furthermore, all the metal-coated groups showed an increase in energy absorption, with aluminum-coated yarns showing the highest increase of 230% compared to control. These results suggest enhanced frictional interactions during yarn pull-out in metal-coated yarns compared to uncoated control as evidenced by the surface roughness profile of individual fibers and inter-yarn frictional calculations.