Search

This article explores wood-fiber-based fabrics containing Lyocell yarn in the warp and Spinnova–Lyocell (60%/40%) yarn in the weft, which are used to form unidirectional all-cellulose composites (ACC) through partial dilution in a NaOH–urea solution. The aim is to investigate the role of the yarn orientation in composites, which was conducted by measuring the tensile properties in both the 0° and 90° directions. As a reference, thermoplastic biocomposites were prepared from the same fabrics, with biobased polypropylene (PP) as the matrix. We also compared the mechanical and thermal properties of the ACC and PP biocomposites. The following experiments were carried out: tensile test, TGA, DSC, DMA, water absorption test and SEM. The study found no significant difference in tensile strength regarding the Spinnova–Lyocell orientation between ACC and PP biocomposites, while the composite tensile strength was clearly higher in the warp (Lyocell) direction for both composite variants. Elongation at break doubled in ACC in the Lyocell direction compared with the other samples. Thermal analysis showed that mass reduction started at a lower temperature for ACC, but the thermal stability was higher compared with the PP biocomposites. Maximum thermal degradation temperature was measured as being 352 °C for ACC and 466 °C for neat PP, and the PP biocomposites had two peaks in the same temperature range (340–474 °C) as ACC and neat PP combined. ACCs absorbed 93% of their own dry weight in water in just one hour, whereas the PP biocomposites BC2 and BC4 absorbed only 10% and 6%, respectively. The study highlights the different properties of ACC and PP reference biocomposites that could lead to further development and research of commercial applications for ACC.

All-cellulose composites (ACCs) are manufactured using only cellulose as a raw material. Biobased materials are more sustainable alternatives to the petroleum-based composites that are used in many technical and life-science applications. In this study, an aquatic NaOH-urea solvent system was used to produce sustainable ACCs from wood-based woven textiles with and without the addition of TEMPO-oxidized nanocellulose (at 1 wt.-%). This study investigated the effects of dissolution time, temperature during hot press, and the addition of TEMPO-oxidized nanocellulose on the mechanical and thermal properties of the composites. The results showed a significant change in the tensile properties of the layered textile composite at dissolution times of 30 s and 1 min, while ACC elongation was the highest after 2 and 5 min. Changes in hot press temperature from 70 °C to 150 °C had a significant effect: with an increase in hot press temperature, the tensile strength increased and the elongation at break decreased. Incorporating TEMPO-oxidized nanocellulose into the interface of textile layers before partial dissolution improved tensile strength and, even more markedly, the elongation at break. According to thermal analyses, textile-based ACCs have a higher storage modulus (0.6 GPa) and thermal stabilization than ACCs with nanocellulose additives. This study highlights the important roles of process conditions and raw material characteristics on the structure and properties of ACCs.

The physical, mechanical, and chemical properties of both stem wood and knot wood were investigated from two subfossil Scots pine (Pinus sylvestris L.) trunks retrieved from a lake in Finnish Lapland, dated to 404–486 CE and to 1318–1444 CE. Both the stem wood and the knot wood of the younger trunk had higher moisture content, lower density, and lower strength properties in comparison to the older trunk. The ash content of the stem wood of the younger trunk was lower, but the ash content of the knot wood was higher than that of the older trunk. Due to the degradation that occurred over time, all the values of physical and mechanical properties were lower compared to typical values of recently grown Scots pine wood. The chemical composition of both stem wood samples was close to the composition of the recently grown wood, and the only exception was the small decrease of the cellulose and hemicellulose in the subfossil samples. The bulk extractives were well-preserved, but terpenes and fatty acids underwent transformation, resulting in more stable compounds. The SWOT analysis (strengths, weaknesses, opportunities, and threats) showed pros and cons for the productization of subfossil wood, with the branding value of an ancient material being the potential enabler in developing commercial niche uses.