CuO thin films with broccoli-like structure were prepared using a facile hydrothermal method to construct photocathodes for water-splitting application. The morphological, structural, and optical properties of thin films were characterized and measured using several techniques, including X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), photoluminescence (PL), and ultraviolet-visible spectroscopy (UV-Vis). The thickness, structure, and morphology of CuO thin films can be controlled by varying the precursor concentration (Cp) and reaction temperature (Tr), which are also discussed. Moreover, the electrical properties of CuO thin films were also measured in the three-electrode system. The photocurrent density of photocathodes, when synthesized by a 0.5 M solution at 150 °C for 12 h, was 0.5 mA/cm2 at −0.6 V vs. Ag/AgCl, which is 1.8 times higher than that of photocathodes synthesized in a 0.1 M solution at 100 °C with the same reaction time. In addition, increasing the reaction temperature and precursor concentration aided in the enhancement of the IPCE and APCE values, which peaked at a wavelength range of 330–400 nm.

In previous decades, investigation of superconductors was aimed either at finding materials with higher critical temperatures or at discovering nontypical superconducting behavior. Here, we present the cupric (CuO) thin films, which were synthesized by atomic layer deposition by using a metal-organic precursor, copper (II)-bis-(-dimethylamino-2-propoxide), and ozone as an oxidizer. The deposition process was optimized by employing a quartz crystal monitoring, and the contact between the deposited films and planar and three-dimensional SiO2/Si substrates was examined by scanning electron microscopy with a focused ion beam module. Phase and elemental composition were analyzed by X-ray diffraction and X-ray fluorescence. Two-probe electrical resistivity measurements revealed a resistivity drop below the critical temperature of 4 K, which may indicate low-temperature superconductivity of the CuO thin films.