Search

Polyhydroxyalkanoate (PHA) is a biodegradable plastic with great potential for tackling plastic waste and marine pollution issues, but its commercial applications have been limited due to its poor processability. In this study, surface-modified cellulose nanocrystals were used to improve the mechanical properties of PHA composites produced via a melt-extrusion process. Double silanization was conducted to obtain hydrophobically treated CNC-based fillers, using tetraethyl orthosilicate (TEOS) and methyltrimethoxysilane (MTMS). The morphology, particle size distributions, and surface characteristics of the silanized CNCs and their compatibility with a PHA polymer matrix differed by the organosiloxane treatment and drying method. It was confirmed that the double silanized CNCs had hydrophobic surface characteristics and narrow particle size distributions, and thereby showed excellent dispersibility in a PHA matrix. Adding hydrophobically treated CNCs to form a PHA composite, the elongation at break of the PHA composites was improved up to 301%, with little reduction of Young’s modulus, compared to pure PHA. Seemingly, the double silanized CNCs added played a similar role to a nucleation agent in the PHA composite. It is expected that such high ductility can improve the mechanical properties of PHA composites, making them more suitable for commercial applications.

This study optimizes furfural production from pentose released in the liquid hydrolysate of hardwood using an aqueous biphasic system. Dilute acid pretreatment with 4% sulfuric acid was conducted to extract pentose from liquid Quercus mongolica hydrolysate. To produce furfural from xylose, a xylose standard solution with the same acid concentration of the liquid hydrolysate and extracting solvent (tetrahydrofuran) were applied to the aqueous biphasic system. A response surface methodology was adopted to optimize furfural production in the aqueous biphasic system. A maximum furfural yield of 72.39% was achieved at optimal conditions as per the RSM, a reaction temperature of 170 &deg, C, reaction time of 120 min, and a xylose concentration of 10 g/L. Tetrahydrofuran, toluene, and dimethyl sulfoxide were evaluated to understand the effects of the solvent on furfural production. Tetrahydrofuran generated the highest furfural yield, while DMSO gave the lowest yield. A furfural yield of 68.20% from pentose was achieved in the liquid hydrolysate of Quercus mongolica under optimal conditions using tetrahydrofuran as the extracting solvent. The aqueous and tetrahydrofuran fractions were separated from the aqueous biphasic solvent by salting out using sodium chloride, and 94.63% of the furfural produced was drawn out through two extractions using tetrahydrofuran.

The effect of drying on the enzymatic hydrolysis of cellulose was determined by analysis of porosity and crystallinity. Fiber hornification induced by drying produced an irreversible reduction in pore volume due to shrinkage and pore collapse, and the decrease in porosity inhibited enzymatic hydrolysis. The drying effect index (DEI) was defined as the difference in enzymatic digestibility between oven- and never-dried pulp, and it was determined that more enzymes caused a higher DEI at the initial stage of enzymatic hydrolysis and the highest DEI was also observed at the earlier stages with higher enzyme dosage. However, there was no significant difference in the DEI with less enzymes because cellulose conversion to sugars during hydrolysis did not enhance enzymatic hydrolysis due to the decrease in enzyme activity. The water retention value (WRV) and Simons&rsquo, staining were used to measure pore volume and to investigate the cause of the decrease in enzymatic hydrolysis. A decrease in enzyme accessibility induced by the collapse of enzymes&rsquo, accessible larger pores was determined and this decreased the enzymatic hydrolysis. However, drying once did not cause any irreversible change in the crystalline structure, thus it seems there is no correlation between enzymatic digestibility and crystalline structure.

Brønsted acid-catalyzed reactions of α-pinene have been studied because of their ability to produce various types of fragrance molecules. Beyond this application, dimeric hydrocarbon products produced from coupling reactions of α-pinene have been suggested as renewable high-density fuel molecules. In this context, this paper presents the application of a sulfated tin(IV) oxide catalyst for the partial coupling reaction of α-pinene from turpentine. Brønsted acid sites inherent in this solid superacid catalyst calcined at 550 °C successfully catalyzed the reaction, giving the largest yield of dimeric products (49.6%) at 120 °C over a reaction time of 4 h. Given that the low-temperature viscosity of the mentioned dimeric products is too high for their use as a fuel in transportation engines, lowering the viscosity is an important avenue of study. Therefore, our partial coupling reaction of α-pinene provides a possible solution as a considerable amount of the isomers of α-pinene still remained after the reaction, which reduces the low-temperature viscosity. On the basis of a comparison of the reaction products, a plausible mechanism for the reaction involving coinstantaneous isomerization and coupling reaction of α-pinene was elucidated.