Search

Titanium alloys have high specific strength and corrosion resistance, which have promising applications in industry. However, the machinability of titanium alloys is limited due to their crystal lattice and physical properties. Thus, in recent years, the superplastic forming of titanium alloys has been intensively developing, in particular, forming at low temperatures and/or high strain rates. In this work, a tensile test of low-cost Ti-2Fe-0.1B alloys was carried out at a temperature of 550~750 °C and a strain rate of 1 × 10−3 s−1~1 × 10−2 s−1. The results showed that the alloy exhibited good superplasticity even at a high strain rate (1 × 10−2 s−1) and a low deformation temperature of 550 °C; the elongation of the alloy in this state reached 137.5%. The high strain rate sensitivity coefficient m (0.3) and the maximum elongation (452%) were obtained at a strain rate of 1 × 10−3 s−1 and a temperature of 750 °C. Characteristics of the microstructure showed that during superplastic deformation, the recrystallization and grain boundary sliding of the alloy phases were accelerated, which could be ascribed to the effect of the element Fe. At the same time, the TiB phase located around the primary elongated α grains could also induce dynamic recrystallization and dynamic globularization during deformation. [ABSTRACT FROM AUTHOR]

The present paper is concerned with the dynamic recrystallization of the Ti-6Al-4V alloy. Electron Backscatter Diffraction (EBSD) observations are performed after high-temperatures tensile tests, with the temperature ranging from 700 to ~950 °C, and the strain rates varying between 10−4 and 10−2/s. Based on the analysis of flow behavior, the dominant mechanism is identified, and a mechanism map is proposed. In particular, the conditions of 890 °C and strain rates ranging from 10−3 to ~10−2/s serve as the delineating boundary of dynamic recovery (DRV) and dynamic recrystallization (DRX). For superplastic deformation, the dominant softening mechanism is DRV. Consequently, the occurrence of continuous dynamic recrystallization (CDRX) can naturally be ascribed to the process of grain refinement. Then, a multi-scales physical-based constitutive model of CDRX is developed, demonstrating a good agreement is obtained between the experimental and calculated grain sizes, so the above model could be used to describe the grain growth for superplastic deformation. In conclusion, DRV and DRX in the superplastic forming of Ti-6Al-4V are studied in this study, the condition boundaries of their occurrence are distinguished, and a constitutive equation-based CDRX recrystallization mechanism is given, which might be employed in the fracture mechanism research. [ABSTRACT FROM AUTHOR]

This article presents the results of investigation of the influence of holding temperature during the quenching process on the microstructure and superplasticity of the Co-Ni-Nb alloy. Temperature-strain rate intervals of the deformation of the superplasticity effects are stated. The optimal regimes of the preliminary treatment by quenching and rolling as well as the routine of the superplastic deformation of the Co-Ni-Nb alloy are defined. The interval of the temperatures of the precipitation, morphology, composition, type and parameters of the lattice of the secondary phase, which appears after the annealing + rolling (to 90%) Co-Ni-Nb alloy, are determined. [ABSTRACT FROM AUTHOR]

In this paper, the equiaxed superfine/nanocrystalline duplex PM-TiAl-based alloy with (γ + α2) microstructure, Ti-45Al-5Nb (at %), has been synthesized by high-energy ball milling and vacuum hot pressing sintering. Superplastic deformation behavior has been investigated at 1000 °C and 1050 °C with strain rates from 5 x 10-5 s-1 to 1 x 10-3 s-1. The effects of deformation on the microstructure and mechanical behaviors of high Nb containing TiAl alloy have been characterized and analyzed. The results showed that, the ultimate tensile strength of the alloy was 58.7 MPa at 1000 °C and 10.5 MPa at 1050 °C with a strain rate of 5 x 10-5 s-1, while the elongation was 121% and 233%, respectively. The alloy exhibited superplastic elongation at 1000 and 1050 °C with an exponent (m) of 0.48 and 0.45. The main softening mechanism was dynamic recrystallization of y grains; the dislocation slip and γ/γ interface twinning were responsible for superplastic deformation. The orientation relationship of γ/γ interface twinning obeyed the classical one: (001)γ//(110)γ. [ABSTRACT FROM AUTHOR]

The superplastic deformation of a hot-extruded GH4151 billet was investigated by means of tensile tests with the strain rates of 10−4 s−1, 5 × 10−4 s−1 and 10−3 s−1 and at temperatures at 1060 °C, 1080 °C and 1100 °C. The superplastic deformation of the GH4151 alloy was reported here for the first time. The results reveal that the uniform fine-grained GH4151 alloy exhibited an excellent superplasticity and high strain rate sensitivity (exceeded 0.5) under all experimental conditions. It was found that the increase of strain rate resulted in an increased average activation energy for superplastic deformation. A maximum elongation of 760.4% was determined at a temperature of 1080 °C and strain rate of 10−3 s−1. The average activation energy under different conditions suggested that the superplastic deformation with 1 × 10−4 s−1 in this experiment is mainly deemed as the grain boundary sliding controlled by grain boundary diffusion. However, with a higher stain rate of 5 × 10−4 s−1 and 1 × 10−3 s−1, the superplastic deformation is considered to be grain boundary sliding controlled by lattice diffusion. Based on the systematically microstructural examination using optical microscope (OM), SEM, electron backscatter diffraction (EBSD) and TEM techniques, the failure and dynamic recrystallization (DRX) nucleation mechanisms were proposed. The dominant nucleation mechanism of dynamic recrystallization (DRX) is the bulging of original grain boundaries, which is the typical feature of discontinuous dynamic recrystallization (DDRX), and continuous dynamic recrystallization (CDRX) is merely an assistant mechanism of DRX. The main contributions of DRX on superplasticity elongation were derived from its grain refinement process. [ABSTRACT FROM AUTHOR]

In this study, the compressive deformation of zirconia toughened alumina (ZTA) ceramics doped with different amounts of TiO2 dopants were investigated in the temperature range of 1300–1400 °C to evaluate the stress exponent (n value) and apparent deformation activation energy (Q value). With 0–8 wt.% TiO2 dopants, the n values and Q values of the TiO2-doped ZTA ceramics were calculated as 2–3 and 605–749 kJ/mol, respectively. Moreover, three grain boundary features were observed in these deformed materials, named the clean grain boundary, thin liquid phase grain boundary, and thick liquid phase grain boundary. Based on the deformation behavior and microstructure evolution, it was found that the lower apparent activation energy and higher strain rate of TiO2-doped ZTA ceramics are intensively related to the grain boundary feature. [ABSTRACT FROM AUTHOR]

Determining a desirable strain rate-temperature range for superplasticity and elongation-to-failure are critical concerns during the prediction of superplastic forming processes in α + β titanium-based alloys. This paper studies the superplastic deformation behaviour and related microstructural evolution of conventionally processed sheets of Ti-6Al-4V alloy in a strain rate range of 10–5–10–2 s–1 and a temperature range of 750–900 °C. Thermo-Calc calculation and microstructural analysis of the as-annealed samples were done in order to determine the α/β ratio and the grain size of the phases prior to the superplastic deformation. The strain rate ranges, which corresponds to the superplastic behaviour with strain rate sensitivity index m ˃ 0.3, are identified by step-by-step decreasing strain rate tests for various temperatures. Results of the uniaxial isothermal tensile tests at a constant strain rate range of 3 × 10−4–3 × 10−3 s−1 and a temperature range of 800–900 °C are presented and discussed. The experimental stress-strain data are utilized to construct constitutive models, with the purpose of predicting the flow stress behaviour of this alloy. The cross-validation approach is used to examine the predictability of the constructed models. The models exhibit excellent approximation and predictability of the flow behaviour of the studied alloy. Strain-induced changes in the grain structure are investigated by scanning electron microscopy and electron backscattered diffraction. Particular attention is paid to the comparison between the deformation behaviour and the microstructural evolution at 825 °C and 875 °C. Maximum elongation-to-failure of 635% and low residual cavitation were observed after a strain of 1.8 at 1 × 10−3 s−1 and 825 °C. This temperature provides 23 ± 4% β phase and a highly stable grain structure of both phases. The optimum deformation temperature obtained for the studied alloy is 825 °C, which is considered a comparatively low deformation temperature for the studied Ti-6Al-4V alloy. [ABSTRACT FROM AUTHOR]

In this paper, the equiaxed superfine/nanocrystalline duplex PM-TiAl-based alloy with (γ + α₂) microstructure, Ti-45Al-5Nb (at %), has been synthesized by high-energy ball milling and vacuum hot pressing sintering. Superplastic deformation behavior has been investigated at 1000 °C and 1050 °C with strain rates from 5 × 10 -5 s -1 to 1 × 10 -3 s -1 . The effects of deformation on the microstructure and mechanical behaviors of high Nb containing TiAl alloy have been characterized and analyzed. The results showed that, the ultimate tensile strength of the alloy was 58.7 MPa at 1000 °C and 10.5 MPa at 1050 °C with a strain rate of 5 × 10 -5 s -1 , while the elongation was 121% and 233%, respectively. The alloy exhibited superplastic elongation at 1000 and 1050 °C with an exponent (m) of 0.48 and 0.45. The main softening mechanism was dynamic recrystallization of γ grains; the dislocation slip and γ/γ interface twinning were responsible for superplastic deformation. The orientation relationship of γ/γ interface twinning obeyed the classical one: (001) γ //(110) γ ., Competing Interests: The authors declare no conflict of interest.