In this study, the researchers aimed to broaden the applications of unsaturated polyester resin (UPR) composites in the building field by incorporating surface-modified titanium dioxide (TiO2) nanoparticles and reinforced chopped glass fibers within the UPR matrix. Specifically, the composites containing 4 wt.% TiO2 nanoparticles and 30 wt.% chopped glass fiber exhibited remarkable properties of 46.1 kJ/m2 in impact strength, 90.1 MPa in flexural strength, 78.8 MPa in tensile strength, and 121.5 °C in heat deflection temperature, which improve 207.5%, 80.3%, 62.5%, and 73.6%, respectively, when compared with the blank sample. Furthermore, the results of the corrosion resistance test showed that the composites performed poorly against polar organic and alkaline solutions, presented good corrosion resistance against acidic media, and behaved relatively stable in the salt solution. [ABSTRACT FROM AUTHOR]

Rubber-based conductive composites are widely used in sensors, wearable electronic devices and electromagnetic fields. In this work, by using the two-roll milling and hot-pressing process, chopped glass fiber (CGF) and graphene (Gr) as additives, and acrtlinitrile-brtadiene rubber (NBR) as the matrix, a series of anisotropic flexible rubber-based composites were prepared. Using this preparation method, both CGF and Gr additives were directly arranged in the material. When the content of CGF was 1 wt.%, the tensile strength in both the T and W directions of the material reached 27 MPa and 28 MPa, respectively. When the content of CGF was fixed at 1 wt.% and Gr was 1.5 wt.% and the elongation at break in both directions reached 328% and 347%. By focusing on the comparison of the dielectric differences in the T and W directions in the X band, it was found that the directional arrangement of the additives led to differences in the dielectric properties. [ABSTRACT FROM AUTHOR]