Search

Synthesis of copper oxide (CuO) nanostructures via biological approach has gained attention to reduce the harmful effects of chemical synthesis. The CuO nanostructures were synthesized through a green approach using the Garcinia mangostana L. leaf extract and copper (II) nitrate trihydrate as a precursor at varying calcination temperatures (200–600 °C). The effect of calcination temperatures on the structural, morphological and optical properties of CuO nanostructures was studied. The red shifting of the green-synthesized CuO nanoparticles' absorption peak was observed in UV-visible spectrum, and the optical energy bandgap was found to decrease from 3.41 eV to 3.19 eV as the calcination temperatures increased. The PL analysis shown that synthesized CuO NPs calcinated at 500 °C has the maximum charge carriers separation. A peak located at 504–536 cm−1 was shown in FTIR spectrum that indicated the presence of a copper-oxygen vibration band and become sharper and more intense when increasing the calcination temperature. The XRD studies revealed that the CuO nanoparticles' crystalline size was found to increase from 12.78 nm to 28.17 nm, and dislocation density decreased from 61.26 × 1014 cm−1 to 12.60 × 1014 cm−1, while micro strain decreased from 3.40 × 10−4 to 1.26 × 10–4. From the XPS measurement, only CuO single phase without impurities was detected for the green-mediated NPs calcinated at 500 °C. The morphologies of CuO nanostructures were examined using FESEM and became more spherical in shape at elevated calcination temperature. More or less spherical nanostructure of green-mediated CuO calcinated at 500 °C were also observed using TEM. The purity of the green-synthesized CuO nanoparticles was evaluated by EDX analysis, and results showed that increasing calcination temperature increases the purity of CuO nanoparticles. [ABSTRACT FROM AUTHOR]

Tungsten oxide (WOx) thin films were synthesized through the RF magnetron sputtering method by varying the sputtering power from 30 W to 80 W. Different investigations have been conducted to evaluate the variation in different morphological, optical, and dielectric properties with the sputtering power and prove the possibility of using WOx in optoelectronic applications. An Energy Dispersive X-ray (EDX), stylus profilometer, and atomic force microscope (AFM) have been used to investigate the dependency of morphological properties on sputtering power. Transmittance, absorbance, and reflectance of the films, investigated by Ultraviolet-Visible (UV-Vis) spectroscopy, have allowed for further determination of some necessary parameters, such as absorption coefficient, penetration depth, optical band energy gap, refractive index, extinction coefficient, dielectric parameters, a few types of loss parameters, etc. Variations in these parameters with the incident light spectrum have been closely analyzed. Some important parameters such as transmittance (above 80%), optical band energy gap (~3.7 eV), and refractive index (~2) ensure that as-grown WOx films can be used in some optoelectronic applications, mainly in photovoltaic research. Furthermore, strong dependencies of all evaluated parameters on the sputtering power were found, which are to be of great use for developing the films with the required properties. [ABSTRACT FROM AUTHOR]

Improving the safety efficacy ratio of existing drugs is a current challenge to be addressed rather than the development of novel drugs which involve much expense and time. The efficacy of drugs is affected by a number of factors such as their low aqueous solubility, unequal absorption along the gastrointestinal (GI) tract, risk of degradation in the acidic milieu of the stomach, low permeation of the drugs in the upper GI tract, systematic side effects, etc. This review aims to enlighten readers on the role of pH sensitive hydrogels in drug delivery, their mechanism of action, swelling, and drug release as a function of pH change along the GI tract. The basis for the selection of materials, their structural features, physical and chemical properties, the presence of ionic pendant groups, and the influence of their pKa and pKb values on the ionization, consequent swelling, and targeted drug release are also highlighted. [ABSTRACT FROM AUTHOR]

A gel polymer electrolyte system based on phthaloylchitosan was prepared. The effects of process variables, such as lithium iodide, caesium iodide, and 1-butyl-3-methylimidazolium iodide were investigated using a distance-based ternary mixture experimental design. A comparative approach was made between response surface methodology (RSM) and artificial neural network (ANN) to predict the ionic conductivity. The predictive capabilities of the two methodologies were compared in terms of coefficient of determination R2 based on the validation data set. It was shown that the developed ANN model had better predictive outcome as compared to the RSM model. [ABSTRACT FROM AUTHOR]

Electrocatalytic water splitting is a promising solution to resolve the global energy crisis. Tuning the morphology and particle size is a crucial aspect in designing a highly efficient nanomaterials-based electrocatalyst for water splitting. Herein, green synthesis of nickel oxide nanoparticles using phytochemicals from three different sources was employed to synthesize nickel oxide nanoparticles (NiOx NPs). Nickel (II) acetate tetrahydrate was reacted in presence of aloe vera leaves extract, papaya peel extract and dragon fruit peel extract, respectively, and the physicochemical properties of the biosynthesized NPs were compared to sodium hydroxide (NaOH)-mediated NiOx. Based on the average particle size calculation from Scherrer's equation, using X-ray diffractograms and field-emission scanning electron microscope analysis revealed that all three biosynthesized NiOx NPs have smaller particle size than that synthesized using the base. Aloe-vera-mediated NiOx NPs exhibited the best electrocatalytic performance with an overpotential of 413 mV at 10 mA cm−2 and a Tafel slope of 95 mV dec−1. Electrochemical surface area (ECSA) measurement and electrochemical impedance spectroscopic analysis verified that the high surface area, efficient charge-transfer kinetics and higher conductivity of aloe-vera-mediated NiOx NPs contribute to its low overpotential values. [ABSTRACT FROM AUTHOR]

In this study, phytochemical assisted nanoparticle synthesis was performed using Muntingia calabura leaf extracts to produce copper oxide nanoparticles (CuO NPs) with interesting morphology. Scanning electron microscope (SEM) and transmission electron microscope (TEM) analysis of the biosynthesized CuO NPs reveal formation of distinct, homogeneous, and uniform sized CuO nanorods structure with thickness and length of around 23 nm and 79 nm, respectively. Based on Fourier-transform infrared (FTIR) analysis, the unique combinations of secondary metabolites such as flavonoid and polyphenols in the plant extract are deduced to be effective capping agents to produce nanoparticles with unique morphologies similar to conventional chemical synthesis. X-ray diffraction (XRD) analysis verified the monoclinical, crystalline structure of the CuO NPs. The phase purity and chemical identity of the product was consolidated via X-Ray photoelectron spectroscopy (XPS) and Raman spectroscopic data which indicate the formation of a single phase CuO without the presence of other impurities. The direct and indirect optical band gap energies of the CuO nanorods were recorded to be 3.65 eV and 1.42 eV. [ABSTRACT FROM AUTHOR]

This study explores the possibility of transforming lignocellulose-rich agricultural waste materials into value-added products. Cellulose was extracted from an empty fruit bunch of oil palm and further modified into carboxymethyl cellulose (CMC), a water-soluble cellulose derivative. The CMC was then employed as the polymeric content in fabrication of solid polymer electrolyte (SPE) films incorporated with lithium iodide. To enhance the ionic conductivity of the solid polymer electrolytes, the compositions were optimized with different amounts of glycerol as a plasticizing agent. The chemical and physical effects of plasticizer content on the film composition were studied by Fourier transform infrared (FTIR) and X-ray diffraction (XRD) analysis. FTIR and XRD analysis confirmed the interaction plasticizer with the polymer matrix and the amorphous nature of fabricated SPEs. The highest ionic conductivity of 6.26 × 10−2 S/cm was obtained with the addition of 25 wt % of glycerol. By fabricating solid polymer electrolytes from oil palm waste-derived cellulose, the sustainability of the materials can be retained while reducing the dependence on fossil fuel-derived materials in electrochemical devices. [ABSTRACT FROM AUTHOR]

A starch-resorcinol-formaldehyde (RF)-lithium triflate (LiTf) based biodegradable polymer electrolyte membrane was synthesized via the solution casting technique. The formation of RF crosslinks in the starch matrix was found to repress the starch's crystallinity as indicated by the XRD data. Incorporation of the RF plasticizer improved the conductivity greatly, with the highest room-temperature conductivity recorded being 4.29 × 10−4 S cm−1 achieved by the starch:LiTf:RF (20 wt.%:20 wt.%:60 wt.%) composition. The enhancement in ionic conductivity was an implication of the increase in the polymeric amorphous region concurrent with the suppression of the starch's crystallinity. Chemical complexation between the plasticizer, starch, and lithium salt components in the electrolyte was confirmed by FTIR spectra. [ABSTRACT FROM AUTHOR]

This work is a pioneer attempt to fabricate quasi-solid dye-sensitized solar cell (QSDDSC) based on organosoluble starch derivative. Rheological characterizations of the PhSt-HEC blend based gels exhibited viscoelastic properties favorable for electrolyte fabrication. From amplitude sweep and tack test analyses, it was evident that the inclusion of LiI improved the rigidity and tack property of the gels. On the other hand, the opposite was true for TPAI based gels, which resulted in less rigid and tacky electrolytes. The crystallinity of the gels was found to decline with increasing amount of salt in both systems. The highest photoconversion efficiency of 3.94% was recorded upon addition of 12.5 wt % TPAI and this value is one of the highest DSSC performance recorded for starch based electrolytes. From electrochemical impedance spectroscopy (EIS), it is deduced that the steric hindrance imposed by bulky cations aids in hindering recombination between photoanode and electrolyte. [ABSTRACT FROM AUTHOR]

Several images are presented in support of a study which examined artificial neural networks, phthaloylchitosan-based gel polymer electrolyte, and ionic conductivity.