Search

Silicon anodes with a high theoretical capacity possess great potential applications in power batteries for electric vehicles, while their volume expansion always leads to crystal pulverization and electrode polarization. An ideal solution to alleviate such pulverization and polarization of silicon crystals is to simultaneously use nano-sized silicon crystals and introduce high viscosity and elasticity polymer binders. This work has achieved the adjustable introduction of hydroxyl groups to silicon nanocrystals under the optimal reaction temperature (e.g., 80 °C) and appropriate piranha solution composition (e.g., H2SO4/H2O2 = 3:1 v/v), ultimately forming an amorphous coating layer of ~1.3 nm on the silicon surface. The optimized silicon anode exhibits superior electrochemical performance (with an initial Coulombic efficiency of 85.5%; 1121.4 mA h g−1 at 1 A g−1 after 200 cycles) and improved hydrophilicity. The introduced hydroxyl groups significantly enhance the hydrophilicity of silicon in the electrolyte and the electrochemical activity of the silicon anodes. The hydroxyl groups achieve stronger bonding between silicon and polymer binders, ultimately improving the mechanical strength and stability of the electrode. The introduction of hydrophily functional groups on the surface of silicon crystals can be explored as an active strategy to solve the above issues. This surface engineering method could be extended to more fields of infiltrating silicon-based functional materials. [ABSTRACT FROM AUTHOR]

Stable F-T-based catalyst development in direct CO hydrogenation to higher alcohols is still a challenge at present. In this study, CuFe/SiO2 catalysts with a SiO2 support treated with a piranha solution were prepared and evaluated in a long-term reaction. The treated catalyst showed higher total alcohols' selectivity and great stability during a reaction of more than 90 h. It was found that the treatment with the piranha solution enriched the surface hydroxyl groups on SiO2, so that the Cu–Fe active components could be firmly anchored and highly dispersed on the support, resulting in stable catalytic performance. Furthermore, the in situ DRIFTS revealed that the adsorption strength of CO on Cu+ on the treated catalyst surface was weakened, which made the C-O bond less likely to be cleaved and thus significantly inhibited the formation of hydrocarbon products. Meanwhile, the non-dissociated CO species were obviously enriched on the Cu0 surface, promoting the formation of alcohol products, and thus the selectivity of total alcohols was increased. This strategy will shed light on the design of supported catalysts with stabilized structures for a wide range of catalytic reactions. [ABSTRACT FROM AUTHOR]

This study aimed to achieve bioactivity on the PEEK surface using piranha solution through a lower functionalization time. For this purpose, the functionalization occurred with piranha solution and 98% sulfuric acid in the proportions of 1:2, 1:1, and 2:1 at periods of 30, 60, and 90 s. The samples treated for longer times at higher concentrations registered the characteristic spectroscopy band associated with sulfonation. Additionally, both chemical treatments allowed the opening of the aromatic ring, increasing the number of functional groups available and making the surface more hydrophilic. The piranha solution treatments with higher concentrations and longer times promoted greater heterogeneity in the surface pores, which affected the roughness of untreated PEEK. Furthermore, the treatments induced calcium deposition on the surface during immersion in SBF fluid. In conclusion, the proposed chemical modifications using sulfuric acid SPEEK 90 and, especially, the piranha solution PEEK-PS 2:1-90, were demonstrated to be promising in promoting the rapid bioactivation of PEEK-based implants. [ABSTRACT FROM AUTHOR]

The main aim of this research was the preparation of a polymer–ceramic composite with PA-12 as the polymer matrix and modified aluminosilicate cenospheres (CSs) as the ceramic filler. The CSs were subjected to an early purification and cleaning process, which was also taken as a second objective. The CSs were surface modified by a two-step process: (1) etching in Piranha solution and (2) silanization in 3-aminopropyltriethoxysilane. The composite was made for 3D printing by FDM. Raw and modified CSs and a composite with PA-12 were subjected to the following tests: surface development including pores (BET), real density (HP), chemical composition and morphology (SEM/EDS, FTIR), grain analysis (PSD), phase composition (XRD), hardness (HV), and static tensile tests. The composites were subjected to soaking under simulated body fluid (SBF) conditions in artificial saliva for 14, 21, and 29 days. Compared to pure PA-12, PA-12_CS had generally better mechanical properties and was more resistant to SBF at elevated temperatures and soaking times. These results showed this material has potential for use in biomedical applications. These results also showed the necessity of developing a kinetic aging model for aging in different liquids to verify the true value of this material. [ABSTRACT FROM AUTHOR]

In this paper, a low-cost yet effective method of irreversible bonding between two elastomeric polydimethylsiloxane (PDMS) interfaces using Piranha solution is investigated. Piranha solutions at a weight ratio of 3:1 using different acids and hydrogen peroxide were attempted. The average tensile strengths of the device bonded with concentrated sulfuric acid-based piranha solution and nitric acid-based piranha solution were found to be 200 ± 20 kPa and 100 ± 15 kPa respectively. A PDMS surface treated with Piranha Solution demonstrated an increase in hydrophilicity. In addition, relatively straightforward swelling studies of PDMS using a weight loss method with common organic solvents were also investigated. Experimental results show that hexane, toluene, ethyl acetate, n-propyl alcohol and acetone swell PDMS significantly over a duration of up to 1 h and above; PDMS samples reached a steady state of swelling only after 5 min of immersion in other solvents. This will enable researchers to develop devices for the future according to the interaction between the material and the solvents in contact. [ABSTRACT FROM AUTHOR]