Search

In this paper, a novel precast concrete composite wall connected by tooth groove and grouted sleeve was introduced, which is produced in factories by means of structure-insulation integrated prefabrication, and the prefabrication and assembly process were presented minutely. To verify the feasibility and reliability of this novel tooth groove and grouted sleeve connection method and explore the joint connection performance and the seismic performance of the precast concrete composite wall connected by tooth groove and grouted sleeve, low-cyclic reversed loading tests with an axial compressive ratio of 0.1 were performed on two full-scale precast concrete composite walls. Moreover, the failure mode, hysteretic curve, skeleton curve, stiffness degradation, displacement ductility, energy dissipation capacity, and reinforcement strain were comprehensively discussed. The research results showed that under the vertical axial load and low-cyclic reversed load, the distributed reinforcements in the wall panel only played a structural role, while the connecting reinforcements at horizontal joints can always effectively transfer stress without bond failure, and the tooth groove and grouted sleeve connection performance was reliable. In addition, the hysteretic curves of the precast concrete composite wall connected by tooth groove and grouted sleeve were full, showing good ductile deformation capacity and energy dissipation capacity. In general, the precast concrete composite wall connected by tooth groove and grouted sleeve not only possessed favorable seismic performance but also showed obvious advantages such as green energy saving, high assembly rate, and less on-site wet operation, which can be applied to practical engineering under reasonable design. [ABSTRACT FROM AUTHOR]

In order to explore the horizontal joint connection performance of the innovative tooth groove connection and vertical reinforcement lapping in the reserved hole, five horizontal joint specimens were designed and constructed in this paper. Through the combination of monotonic horizontal load tests and finite element simulation analysis, the effects of axial compression ratio, vertical reinforcement connection degree, reserved hole type, mortar strength, and tooth groove depth on the horizontal joint connection performance of innovative tooth groove connections and vertical reinforcement lapping in reserved holes were comprehensively analyzed and discussed. The results indicated that the specimens were subjected to penetration failure at the tooth groove joint, but the vertical reinforcements and UHPC in reserved holes can effectively transfer the stress, ensuring satisfactory connection performance. With the increase in axial compression ratio and vertical reinforcement connection degree, the joint connection performance enhanced gradually, while the reserved hole type had little effect on the joint connection performance. In addition, it was found that increasing the mortar strength and the tooth groove depth can significantly improve the peak bearing capacity through finite element analysis. Finally, the optimization design suggestions for this innovative tooth groove connection and vertical reinforcement lapping in the reserved hole were given considering factors such as joint connection performance and construction assembly. [ABSTRACT FROM AUTHOR]

Rebar corrosion is the primary cause of the durability degradation of reinforced concrete (RC) structures, where non-uniform corrosion is the typical pattern in engineering. This study experimentally and numerically investigated the tensile degradation properties of non-uniform corroded rebars. Corrosion morphology was accurately determined by three-dimensional (3D) laser scanning techniques, studying the characteristics of longitudinal non-uniform corrosion. The results showed that the non-uniformity of corrosion increased with an increase in corrosion levels. From tensile tests, the differences in nominal stress–strain curves among rebars with similar average corrosion levels indicated that corrosion non-uniformity has appreciable effects on the tensile behavior of rebars. The residual load-bearing capacity of corroded rebars was dominated by the reduced critical cross-section, while residual ductility was associated with the cross-section loss throughout the entire length of rebars. The degradation relations of nominal yield and ultimate strength, ultimate strain, and elongation after fracture were better correlated to the maximum cross-section loss than to the average volume loss. Additionally, numerical calculation based on the cross-sectional areas of corroded rebars was conducted to evaluate the tensile behavior of non-uniform corroded rebars. Equivalent distribution models simulating the longitudinal non-uniform corrosion were proposed, on the basis of probability characteristics of cross-sectional areas, for practical application of the numerical method. [ABSTRACT FROM AUTHOR]

Using high strength wire (HSW) as a longitudinal reinforcement in UHPC can make full use of the outstanding properties of UHPC. In this paper, the flexural test was carried out on normal rebar-reinforced UHPC (NRRU) and HSW reinforced UHPC (HSWRU) slabs. The cracking resistance, failure modes, bearing capacity and deformation characteristics of specimens were investigated. The test results indicated that both HSWRU and NRRU specimens exhibited excellent flexural performance under concentrated loads. Fewer inclined cracks and a slower cracking development process were observed for HSWRU specimens, and brittle failure did not occur during the whole loading process. As compared to HSWRU specimens, the cracking and ultimate load of NRRU specimens increased by 24.64% and 85.47%, respectively, due to a higher reinforcement ratio. Then the theoretical method available for flexural capacity and ductility calculation was proposed, and the feasibility was substantiated through test results. In addition, the traditional deformation ductility coefficient was found to be 30% conservative against the applied energy ductility coefficient. Finally, the extensive parametric analysis revealed that the increase of the reinforcement ratio and the strength of the steel rebar significantly enhanced the ultimate capacity, while the ductility coefficient was obviously weakened. Inversely, those two factors had little impact on the cracking capacity. Moreover, section height was found to be beneficial for both the flexural capacity and ductility of specimens. [ABSTRACT FROM AUTHOR]