Search

Bisphenol A (BPA) is an endocrine-disrupting chemical (EDC) that can cause adverse effects on human health. The incorporation of materials as visible light photocatalysts and its energy storage capability allow for the photodegradation of BPA, especially in the absence of a light source. To date, there have been no significant studies regarding energy storage in membrane technology, with only a focus on the suspension form. Hence, this study was conducted to degrade the pollutant through a co-extrusion process using a mixture of copper (II) oxide and tungsten oxide as the photocatalyst and energy storage materials, respectively. Both materials were embedded into polyvinylidene (PVDF) membranes to produce a Cu2O/WO3/PVDF dual-layer hollow fiber (DLHF) membrane. The outer dope extrusion flow rate was set at 3 mL/min, 6 mL/min, and 9 mL/min with photocatalyst:polymer ratios of 0.3, 0.50, and 0.7 Cu2O/WO3/PVDF, respectively. The performance of the membranes for each ratio was evaluated using 2 ppm of BPA with visible light irradiation. The results showed that each membrane's outer and inner layers featured finger-like void structures, while the intermediate part had a sponge-like structure. The membrane with the photocatalyst:polymer ratio of 0.5 was hydrophilic and had a high porosity of 54.97%, resulting in a high flow of 510 L/m2h. Under visible light irradiation, a 0.5 Cu2O/PVDF DLHF membrane with a 6-mL/min outer dope flow rate was able to remove 97.82% of 2-ppm BPA without copper leaching into the water sample. Under dark conditions, the DLHF sample showed the capability of energy storage performance and could drive certain degradation after lighting off up to 70.73% of 2-ppm BPA. The photocatalytic DLHF membrane with the ratio of 0.5 was the most optimal due to its potential morphology and ability to degrade a large amount of BPA. It is important to emphasize that usage of materials with the capability for energy storage can provide a significant contribution toward more practical membranes, so photodegradation can occur even in dark conditions. [ABSTRACT FROM AUTHOR]

Since the major route of BPA exposure is via the oral route, BPA may have effects on the gastrointestinal tract, especially on the intestinal barrier, where most digestion and absorption processes occur. In this study, the effects of BPA-treated water on the small intestine (SI) and SI tight junction proteins (TJPs) of both pregnant Sprague–Dawley rats and their fetuses were investigated. Previously, hybrid photocatalytic filtration treatment by a visible light driven N-doped TiO2 membrane has successfully removed up to 81.6% of BPA in water. The effect of BPA-untreated (5.00 ± ppm) and BPA-treated water (0.9 ± ppm) after 21 days of exposure on the jejunum and ileum, as well as the expressions of claudin proteins, were investigated by Western blotting (WB) and hematoxylin and eosin (H&E) in order to investigate the potential of the photocatalytic membrane in removing the detrimental effect of BPA. The results suggest that BPA exposure altered the morphology of villi, and affected the expression level of claudin-2, -3, and -4 proteins in the jejunum and ileum of both pregnant rats and their fetuses. Interestingly, villi and claudins expressions were undisrupted in a treated-BPA water group, which indicated that the degradation of BPA via membranes effectively mitigates the effect on BPA on gastrointestinal tract. [ABSTRACT FROM AUTHOR]

Existing toxic solvents in the manufacturing of polymeric membranes have been raising concerns due to the risks of exposure to health and the environment. Furthermore, the lower tensile strength of the membrane renders these membranes unable to endure greater pressure during water treatment. To sustain a healthier ecosystem, fabrication of polyvinylidene fluoride (PVDF) hollow fiber membrane using a less toxic solvent, triethyl phosphate (TEP), with a lower molecular weight polyethylene glycol (PEG 400) (0–3 wt.%) additive were experimentally demonstrated via a phase inversion-based spinning technique at various air gap (10, 20 and 30 cm). Membrane with 2 wt.% of PEG 400 exhibited the desired ultrafiltration asymmetric morphology, while 3 wt.% PEG 400 resulting microfiltration. The surface roughness, porosity, and water flux performance increased as the loading of PEG 400 increased. The mechanical properties and contact angle of the fabricated membrane were influenced by the air gap where 20 cm indicate 2.91 MPa and 84.72°, respectively, leading to a stronger tensile and hydrophilicity surface. Lower toxicity TEP as a solvent helped in increasing the tensile properties of the membrane as well as producing an eco-friendly membrane towards creating a sustainable environment. The comprehensive investigation in this study may present a novel composition for the robust structure of polymeric hollow fiber membrane that is suitable in membrane technology. [ABSTRACT FROM AUTHOR]

The presence of bisphenol A (BPA) in various water sources has potentially led to numerous adverse effects in human such as increased in blood pressure and derangement in liver function. Thus, a reliable treatment for the removing BPA is highly required. This present work aimed to study the efficiency of visible light driven photocatalytic dual-layer hollow fiber (DLHF) membrane for the removal of BPA from water and further investigated its detrimental effects by using an in-vivo model. The prepared membranes were characterized for their morphology, particles distribution, surface roughness, crystallinity and light absorption spectra. The removal of 81.6% and 86.7% in BPA concentration was achieved for N-doped TiO2 DLHF after 360 min of visible and UV light irradiation, respectively. No significant changes for all three groups were observed in liver function test meanwhile the rats-exposed to untreated BPA water shows significance blood pressure increment contrary to rats-exposed to treated BPA water. Similarly, the normal morphology in both jejunum and ileum were altered in rats-exposed to untreated BPA water group. Altogether, the presence of N-doped TiO2 in DLHF are shown to significantly enhance the photocatalytic degradation activity under visible irradiation, which effectively mitigates the effect of BPA in an in-vivo model. [ABSTRACT FROM AUTHOR]